Effects of al_2O_3 nanoparticles on properties of self compacting concrete with ground granulated blast furnace slag (GGBFS) as binder

引用

Science China(Technological Sciences) 2011年第9期54卷 2327-2338页

作者： ali NAZARI Shadi RIAHI Department of Materials Science and Engineering Saveh BranchIslamic Azad University

In this work, strength assessments and percentage of water absorption of self compacting concrete containing ground granulated blast furnace slag （GGBFS） and A1203 nanoparticles as binder have been investigated. Portland cement was replaced by different amounts of GGBFS and the properties of concrete specimens were investigated. although it negatively impacts the physical and mechanical properties of concrete at early ages of curing, GGBFS was found to improve the physical and mechanical properties of concrete up to 45 wt% at later ages. A1203 nanoparticles with the average particle size of 15 nm were added partially to concrete with the optimum content of GGBFS and physical and mechanical properties of the specimens were measured. A1203 nanoparticle as a partial replacement of cement up to 3.0 wt% could accelerate C-S-H gel formation as a result of increased crystalline Ca（OH）2 amount at the early ages and hence increase strength and improve the resistance to water permeability of concrete specimens. The increase of the A1203 nanoparticles＇ content by more than 3.0 wt% would cause the reduction of the strength because of the decreased crystalline Ca（OH）2 content required for C-S-H gel formation. Several empirical relationships have been presented to predict flexural and split tensile strength of the specimens by means of the corresponding compressive strength at a certain age of curing. Accelerated peak appearance in conduction calorimetry tests, more weight loss in thermogravimetric analysis and more rapid appearance of the peaks related to hydrated products in X-ray diffraction results, all indicate that A1203 nanoparticles could improve mechanical and physical properties of the concrete specimens.

关键词： concrete ground granulated blast furnace slag (GGBFS) al203 nanoparticles compressive strength, flexural and splittensile strength pore structure thermogravimetric analysis conduction calorimetry

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：