中国科技信息 2015年第17期 31-32+15页

作者：郭燕宿迁学院

本文通过机械合金化(MA)技术于304不锈钢基体表面制备al-al2o3涂层,应用扫描电子显微镜(SEM)观察不同球磨参数条件下制备的涂层表面及截面微观形貌,应用高温氧化实验技术分析其抗高温氧化性能,并对抗高温氧化性能机理及al元素的影响进... 详细信息

本文通过机械合金化(MA)技术于304不锈钢基体表面制备al-al2o3涂层,应用扫描电子显微镜(SEM)观察不同球磨参数条件下制备的涂层表面及截面微观形貌,应用高温氧化实验技术分析其抗高温氧化性能,并对抗高温氧化性能机理及al元素的影响进行相关探讨。

关键词：抗高温氧化性不锈钢基体表面制备高温氧化性能涂层保护 al-al2o3 复合涂层机械合金化粉末冶金

来源：

同方期刊数据库评论

在线全文

同方期刊数据库

学校读者我要写书评

暂无评论

Nanoindentation Study of al356-al2o3 Nanocomposite Prepared by Ball Milling

引用

Materials Sciences and Applications 2010年第4期1卷 217-222页

作者： Y. Mazaheri F. Karimzadeh M. H. Enayati 不详

In this study ball milling of al356 and al2o3 powder mixture was carried out in order to produce al356-al2o3 nano-composite containing 20 vol.% al2o3. The structural evolution and morphological changes of powder particles during ball milling were studied by X-ray diffractometery and scanning electron microscopy analysis. As a result of ball milling al2o3 particles were uniformly dispersed in al356 matrix. Furthermore the crystallite size of the al356 decreased to 25 nm after ball milling for 10 h. Morphological studies of powder particles indicated that the powder particle size continuously decreases with increasing milling time. Hardness and elastic modulus values of powder particles were measured by nanoindentation method. It was found that the hardness and elastic modulus of al356-20 vol.% al2o3 nanocomposite were about 216 Hv and 86 GPa, respectively which is higher than 75 Hv and 74 GPa for as-received al356.

关键词： al-al2o3 Nanocomposite Nanocrystalline Structure Ball Milling Nanoindentation

来源：

维普期刊数据库评论

在线全文

维普期刊数据库

学校读者我要写书评

暂无评论

Effect of al2o3Content and Process Variables on Structure and Properties of al-al2o3Compacts

引用

Journal of Minerals and Materials Characterization and Engineering 2014年第2期2卷 121-128页

作者： Arindam Ghosh Subrata Chatterjee Department of Metallurgy and Materials Engineering Bengal Engineering and Science University Howrah India Department of Metallurgy and Materials Engineering Bengal Engineering and Science University Howrah India Presently at National Engineering Industries Ltd. Jaipur India

aluminium-alumina compacts with varying wt% of alumina were compacted in the pressure range of 115 - 290 MPa. Compacts prepared at 290 MPa pressure, were sintered in an argon atmosphere at 573, 673, 773 and 873 K for 1 hour. The green density, % porosity, % spring back and hardness of the green compacts were determined. Scanning Electron Microscopy was carried out to observe the morphology of pores and alumina particles in green and sintered compacts. The present study indicates that, densification of the compact increases with increasing compacting pressure and decreases with increasing alumina content. Maximum density achieved is 93% for pure aluminium compacts and decreases to 85% for al-20 wt% alumina compacts. Grain growth of aluminium particles is noticed in the compacts after sintering at 773 and 873 K. Dispersion of fine alumina particle in the aluminium matrix occurs predominantly in the compact when sintered at 773 K which results in increase in hardness value.

关键词： al-al2o3 Compacts Porosity Spring Back Residual Stress Sintering

来源：

维普期刊数据库评论

在线全文

维普期刊数据库

学校读者我要写书评

暂无评论

alCl_3-EMIC室温离子液体制备al-al_2o_3复合涂层

引用

材料科学与工程学报 2012年第2期30卷 236-240,213页

作者：史晓娟吴进明凌国平浙江大学材料科学与工程学系浙江杭州310027

首次在室温下用含10g/L al2o3颗粒的alCl3-EMIC室温离子液体电沉积制备出al-al2o3复合镀层。沉降试验表明,al2o3颗粒在酸性alCl3-EMIC室温离子液体中能形成稳定的悬浮液。通过SEM观察镀层表面和断面形貌,发现al2o3颗粒均匀地分布在镀层... 详细信息

首次在室温下用含10g/L al2o3颗粒的alCl3-EMIC室温离子液体电沉积制备出al-al2o3复合镀层。沉降试验表明,al2o3颗粒在酸性alCl3-EMIC室温离子液体中能形成稳定的悬浮液。通过SEM观察镀层表面和断面形貌,发现al2o3颗粒均匀地分布在镀层中。显微努氏硬度检测结果表明,al-al2o3复合镀层的硬度高于纯al镀层,其中al镀层的硬度随着电流密度的增大而增高,而al-al2o3复合镀层的硬度却随着电流密度的增大而呈降低的趋势。本文还讨论了al2o3颗粒在离子液体中的分散机制,以及和颗粒共沉积的过程。

关键词：室温离子液体复合镀层 al-al2o3 电沉积

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

PECVD制备al-al_2o_3复合阻氢涂层的研究

引用

表面技术 2008年第3期37卷 41-43,48页

作者：银陈陈长安张鹏程表面物理与化学国家重点实验室四川绵阳621700

为了提高不锈钢的阻氢性能,利用PECVD(等离子体增强化学气相沉积)技术在不锈钢表面上制备了al薄膜,经真空热氧化处理(480℃)获得了al-al2o3复合薄膜。用表面分析手段SEM、XRD、EDS和XPS对所制备涂层的表面形貌、相结构、表面成分、表面... 详细信息

为了提高不锈钢的阻氢性能,利用PECVD(等离子体增强化学气相沉积)技术在不锈钢表面上制备了al薄膜,经真空热氧化处理(480℃)获得了al-al2o3复合薄膜。用表面分析手段SEM、XRD、EDS和XPS对所制备涂层的表面形貌、相结构、表面成分、表面元素的化学态进行了分析,并对其进行了阻氘性能研究。结果表明:该技术能够获得均匀、致密复合薄膜;在低于350℃时,阻氘效果非常好,几乎没有渗透,在350℃到450℃之间,阻氘因子能够达到250左右,但在高于450℃后,渗透非常明显。

关键词： PECVD 复合薄膜阻氘因子 al-al2o3

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

在线全文

在线全文

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

在线全文

在线全文

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：