Superplastic forming characteristics of az41 magnesium alloy

Transactions of Nonferrous Metals Society of China 2021年第3期31卷 648-654页

作者： S.TAYLOR G.D.WEST E.MOGIRE F.TANG H.R.KOTADIA WMG the University of WarwickCoventry CV47ALUK Buehler WMG Materials Engineering Centrethe University of WarwickCoventry CV47ALUK

An az41 magnesium alloy in the hot-rolled condition without further thermomechanical processing to modify its microstructure was investigated to establish its suitability for use within a superplastic forming process and to establish optimum forming *** was assessed using elevated temperature tensile testing and hot gas bulging,across a range of strain rates(1×10^(−1)−1×10^(−3)s^(−1))and temperatures(350−450℃).Circle grid analysis with GOM Aramis cameras was used to understand peak strains and material thinning in relation to industrial forming *** forming EBSD and STEM analysis was conducted to understand the mechanisms responsible for the materials formability,with dynamic recrystallization being clearly *** elongation of 520%was achieved at 450℃ and 1×10^(−3)s^(−1);industrially relevant elongation was achieved at 1×10^(−2) s^(−1) at both 450℃(195%)and 400℃(170%).

关键词： magnesium superplastic forming superplasticity electron back-scattered diffraction(EBSD) az41 magnesium alloy

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：