Structural Characterization of AlMgB_(14) Prepared by Field-activated, Pressure-assisted Synthesis

Journal of Materials Science & Technology 2013年第1期29卷 77-81页

作者： Wen Liu Yang Miao Qingsen Meng Shaoping Chen College of Materials Science and Engineering Taiyuan University of Technology School of Chemical and Biological Engineering Taiyuan University of Science and Technology

Mechanical alloying （MA） and field-activated, pressure-assisted synthesis （FAPAS） were used for the in situ synthesis and densification of ultra-hard, super-abrasive aimgb14 metallic ceramic, performed at 1500 ℃ under a pressure of 60 MPa with the elemental constituents of aluminum, magnesium, and boron. The microstructure and components of synthesized metallic ceramic were observed and determined by scanning electron microscopy （SEM）, energy dispersive X-ray analysis （EDX）, X-ray diffraction （XRD）, and transmission electron microscopy （TEM）. The results showed that the main components of the samples were aimgb14 with a few ***204 was derived from the contamination of the preliminary powders and the milling process. The average hardness of the samples that provided the results was 26.1 GPa. The average density of the samples was 2.62 g/cm^3, which is 98% of its theoretical density. The sample of aimgb14-TiB2 composite with 30 wt% TiB2 had a hardness of 29.5 GPa, which is consistent with that of aimgb14-TiB2 composite with 30 wt% TiB2 prepared by mechanical alloying/hot uniaxial pressing. Thus, a new approach was developed using the mechanical alloying and FAPAS process to synthesize aimgb14 with fast heating, high efficiency, energy saving, and high yield.

关键词： Field-activated and Pressure-assisted synthesis (FAPAS) aimgb14 Borides Microstructure

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：