Effect of pretreatment on electrochemical etching behavior of Al foil in HCl-H_2SO_4

Transactions of Nonferrous Metals Society of China 2013年第4期23卷 1039-1045页

作者：班朝磊何业东邵鑫杜鹃聊城大学材料科学与工程学院聊城252059 北京科技大学北京市腐蚀磨蚀与表面技术重点实验室北京100083

The aluminum foil for high voltage aluminum electrolytic capacitor was immersed in 0.5 mol/L H3PO4 or 0.125 mol/L NaOH solution at 40 ℃ for different time and then DC electro-etched in 1 mol/L HC1＋2.5 mol/L H2SO4 electrolyte at 80 ℃. The pitting potential and self corrosion potential of a1 foil were measured with polarization curves （PC）. The potentiostatic current--time curve was recorded and the surface and cross section images of etched a1 foil were observed with SEM. The electrochemical impedance spectroscopy （EIS） of etched a1 foil and potential transient curves （PTC） during initial etching stage were measured. The results show the chemical pretreatments can activate a1 foil surface, facilitate the absorption, diffusion and migration of C1- onto the a1 foil during etching, and improve the initiation rate of meta-stable pits and density of stable pits and tunnels, leading to much increase in the real surface area and special capacitance of etched a1 foil.

关键词： a1 foil polarization pitting corrosion electrochemical etching AI electrolytic capacitor

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：