Effect of alloying on the properties of 9cr low activation martensitic steels

Acta Metallurgica Sinica(English Letters) 2010年第6期23卷 451-460页

作者： Rong MA Yafeng YANG Qingzhi YAN Ying YANG Xinggang LI Changchun GE Institute of Nuclear Materials University of Science and Technology Beijing Beijing 100083 China

Two types of 9cr low activation martensitic steels （named 9cr-1 and 9cr-2） were developed in University of Science and Technology Beijing. 9cr-1 and 9cr-2 were produced by vacuum induction melting method, and examinations of the microstruc- tures were carried out with X-ray diffraction analysis, optical microscopy, scanning electron microscopy and transmission electron microscopy. The ultimate tensile strength and yield tensile strength were evaluated with tensile tests. The impact properties were characterized with Charpy impact experiments. The results indi- cated that 9cr-1 and 9cr-2 on as-received condition （95 ~C/30 min/water quenching plus 780 ~C/90 min/air cooling） were flflly martensitic steels free of ^-ferrite. The ul- timate tensile strength of 9cr-1 and 9cr-2 were 695 MPa and 680 MPa, respectively. However, 9cr-2 showed a fine grain size of 4.8 pm, and its value of ductile-brittle transition temperature （DBTT） was -90 ~C under as-received condition. The additions of vanadium, titanium and boron accelerated the formation of MX precipitates and resulted in fine grains and precipitates. The fine grains effectively reduced the value of DBTT from -60 ℃ to -90 ℃ with identical upper shelf energy （USE）. The decrease in silicon concentration of 9cr-2 induced a slight reduction in ultimate tensile strength from 695 MPa to 680 MPa.

关键词： 9cr low activation martensitie steel Grain size Mechanical properties

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：