Effect of homogenization treatment on microstructure and mechanical properties of DC cast 7x50 aluminum alloy

Transactions of Nonferrous Metals Society of China 2015年第4期25卷 1027-1034页

作者：丛福官赵刚姜锋田昵李瑞峰东北大学材料各向异性与织构教育部重点实验室沈阳110004 东北轻合金有限责任公司哈尔滨150060 中南大学材料科学与工程学院长沙410083

The evolution of the eutectic structures in the as-cast and homogenized 7x50 aluminum alloys was studied by scanning electron microscopy(SEM), transmission electron microscopy(TEM), energy dispersive spectrometer(EDS), differential scanning calorimetry(DSC), x-ray diffraction(xRD) and tensile test. The results show that the main phases are S(Al2CuMg), T(Al2Mg3Zn3) and Mg Zn2, with a small amount of Al7Cu2 Fe and Al3 Zr in the as-cast 7x50 alloy. The volume fraction of the dendritic-network structure and residual phase decreases gradually during the homogenization. After homogenization at 470 °C for 24 h and then 482 °C for 12 h, the T(Al2Mg3Zn3) phase disappears and minimal S(Al2CuMg) phase remains, while almost no change has happened for Al7Cu2 Fe. There is a strong endothermic peak at 477.8 °C in the DSC curve of as-cast alloy. A new endothermic peak appears at 487.5 °C for the sample homogenized at 470 °C for 1 h. However, this endothermic peak disappears after being homogenized at 482 °C for 24 h. The T(Al2Mg3Zn3) phase cannot be observed by xRD, which is consistent with that T phase is the associated one of S(Al2CuMg) phase and Mg Zn2 phase. The volume fraction of recrystallized grains is substantially less in the plate with pre-homogenization treatment. The strength and fracture toughness of the plate with pre-homogenization treatment are about 15 MPa and 3.3 MPa·m1/2 higher than those of the material with conventional homogenization treatment.

关键词： 7x50 aluminum alloy microstructural evolution homogenization residual phase recrystallization

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：