Effects of Temperature and Pressure on stress Corrosion Cracking Behavior of 310s stainless steel in Chloride solution

引用

Chinese Journal of Mechanical Engineering 2017年第1期30卷 200-206页

作者： ZHONG Yunpan ZHOU Cheng CHEN songying WANG Ruiyan Key Laboratory of High-efficiency and Clean Mechanical Manufacture Shandong UniversityJinan 250061China Qingdao Boiler and Pressure Vessel supervisory Institute Qingdao 266071China

310s is an austenitic stainless steel for high temperature applications, having strong resistance of oxidation, hydrogen embrittlement and corrosion. stress corrosion cracking（sCC） is the main corrosion failure mode for 310s stainless steel. Past researched about sCC of 310s primarily focus on the corrosion mechanism and influence of temperature and corrosive media, but few studies concern the combined influence of temperature, pressure and chloride. on sCC of 310s stainless steel, prepared samples are investigated via For a better understanding of temperature and pressure＇s effects slow strain rate tensile test（ssRT） in different temperature and pressure in NACE A solution. The result shows that the sCC sensibility indexes of 310s stainless steel increase with the rise of temperature and reach maximum at 10MPa and 160~C, increasing by 22.3% compared with that at 10 MPa and 80 ℃. Instead, the sensibility decreases with the pressure up. Besides, the fractures begin to transform from the ductile fracture to the brittle fracture with the increase of temperature. 310s stainless steel has an obvious tendency of stress corrosion at 10MPa and 160℃ and the fracture surface exists cleavage steps, river patterns and some local secondary cracks, having obvious brittle fracture characteristics. The sCC cracks initiate from inclusions and tiny pits in the matrix and propagate into the matrix along the cross section gradually until rupture. In particular, the oxygen and chloride play an important role on the sCC of 310s stainless steel in NACE A solution. The chloride damages passivating film, causing pitting corrosion, concentrating in the cracks and accelerated ssC ultimately. The research reveals the combined influence of temperature, pressure and chloride on the sCC of 310s, which can be a guide to the application of 310s stainless steel in super-heater tube.

关键词： 310s stainless steel ssRT stress corrosion chloride temperature

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

Oxidation Behavior of Micro-Crystalline Coatings of 310s stainless steel

引用

International Journal of Minerals,Metallurgy and Materials 1998年第1期12卷 51-56页

作者： Zhenyu Liu Wei Gao Karl Dahm Yedong He (Department of Chemical and Materials Engineering, The University of Auckland, New Zealand)(Materials science and Engineering school, University of science and Technology Beijing, Beijing 100083, China) Department of Chemical and Materials Engineering University of Auckland Beijing New Zealand Materials science and Engineering school University of Science and Technology Beijing Beijing 100083 China

Micro-crystalline coatings of 310s stainless steels were produced by unbalanced magnetron sputter deposition. Isothermal oxidation behavior of the coated and uncoated specimens has been studied using a thermogravimetric analysis (TGA) station. The oxidation time was 50h and the temperature was 1 000℃. The oxidation rates of thecoated specimens was found to be much lower than the uncoated specimens after 50 h of oxidation. The oxidationkinetic curves of the coated specimens consisted of three stages : approximately parabolic at the first stage, speedingup at the second stage, and slow down at the third stage. The increase of the oxidation rate at the second stage nasattributed to the fast diffuison of Fe though the fine grained Cr2O3 layer formed on the micro-crystalline *** top view and cross-section microstructures of the oxides formed on the coated and the uncoated specimens werestudied with sEM and EDs. It was observed that the nucleation of oxide on the coated specimens was muchenhanced at the initial oxidation stage. This was explained as the result of reduction in the critical free energychange and increase in the supply of chromium ions.

关键词： oxidation 310s stainless steel magnetron sputter deposition oxide nucleation

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：