Formation mechanism of shrinkage and large inclusions of a 70t 12cr2mo1 heavy steel ingot

China Foundry 2014年第1期11卷 46-51页

作者： Liu Hongwei Fu Paixian Kang Xiuhong Ma Xiaoping Shenyang National Laboratory for Materials Science Institute of Metal Research Chinese Academy of Sciences

Shrinkage cavities and large inclusions are serious internal defects of heavy steel ingot and influence the quality of subsequent forgings. In order to remove these two types of defects, a 70 t 12cr2mo1 heavy ingot fabricated by vacuum carbon de-oxidation process was sectioned and investigated by means of structure observation and EDS analysis. To further study the forming mechanism of shrinkage and inclusion defects and find possible solutions, simulation on pouring and solidification processes was also carried out using Fluent and ProCAST software, respectively. Results show that the shrinkage defects do not appear in the middle-upper part of the ingot. The critical value of shrinkage cavity criterion is ascertained as 0.013 on the basis of sectioning investigation and simulation results, which can be used in computer simulation to predict and avoid shrinkage defects in production of 12cr2mo1 ingots with different weights. However, large inclusions are found at the bottom of the ingot body. The bad thermal conditions of the ingot surface and large amount of entrained slag are the main origin of the large inclusions. The simulation result of the pouring process shows that large inclusions may be eliminated by combined measures of improving the top thermal condition and controlling the height of rudimental molten steel in the ladle to above 300 mm.

关键词： 12cr2mo1 heavy ingot segregation shrinkage defect large inclusions

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：