Complex Boronized Layer on the Hot-dip Aluminized Steels and Its Surface Performances

材料热处理学报 2004年第05B期25卷 653-656页

作者： LUOXin-min LIDian-kai WANGLan CHENKang-min JiangsuUniversity ZhenjiangJiangsuP.R.China

Plain carbon steels were dipped in molten aluminum bath at 720°C ±5°C and diffused for 1, 2.5 and 6 hours respectively and then boronized at 950°C for 6 hours. The oxidation, hot-corrosion and abrasion resistance behavior were examined. The experimental results showed the compounds of the aluminized layer, from the surface to the matrix, were composed of Fe2Al5 ( n -phase ) .. Fe3Al ( -phase ) and a phase. The microstructure of aluminized plus complex boronized were similar to that simplex boronized. The XRD analysis results indicated that there existed Fe2B> Fe2AlB2and Fe2Als in this kind of layer. The simplex aluminized layers still remained bright gray appearance when oxidized at 950°C, but complex boronized layer was not able to resist oxidization at the temperature. Both the layers of complex boronized and aluminized had the same anti-oxidization level in the circulative oxidization tests, and also good anti-corrosion ability in molten salt medium. Under dry abrasive conditions, wear resistance of complex boronized layer was superior to the aluminized layer.

关键词：热镀喷铝钢硼化热腐蚀磨损

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：