Size Effect of Impact Abrasive Particles on Wear and Surface Hardening Behavior of High‑Manganese steel

Acta Metallurgica Sinica(English Letters) 2023年第6期36卷 906-916页

作者： Yongjin Wang Chuansongxin Song Renbo Song Zetian Ma Tom Taylor School of Materials Science and Engineering University of Science and Technology BeijingBeijing 100083China Swansea University Swansea SA18EPUK

The size effect of impact abrasive particles on wear and surface hardening behavior of high-manganese steel was studied.Impact wear tests were carried out on MLD-10 tester with abrasive particle sizes of 6.0–0.75 mm,respectively.The results showed that the impact wear behavior and surface hardening mechanism of high-manganese steel were affected by the size of abrasive particles.A critical size of abrasive particle might exhibit to distinguish the impact wear behavior.When the abrasive particle size was larger than 0.75 mm,the wear mass loss generally showed a decreasing trend with the decrease of the abrasive particle size.Dislocation strengthening and mechanical twinning contributed to the good work hardening behavior.However,effective surface hardening layer could not be formed for sample tested with particle size of 0.75 mm and the wear mass loss was the highest among all the conditions.The weak hardening effect led to the sharp increase of the wear mass loss.Press-in abrasives could be observed on the wear surface when the abrasive particle size was larger than 0.75 mm.The press-in abrasives were peeled off from the wear surface and broken,leaving deep grooves and peeling pits.Material exchange with the sample would occur with the flow of abrasives.A large area of furrow was formed on the wear surface.For particle size of 0.75 mm,aggregated abrasives formed a dynamic buffer layer on the surface and the stress distribution was more even.The formation of buffer layer would lower the effect of the impact load and the work hardening effect could not be fully activated.The mutual extrusion among the abrasives,friction wheel and sample caused plastic deformation of the worn surface during impact test.The present study would help guiding to select the application field of high-manganese steel more precisely.

关键词： Abrasive particles Three-body impact wear High-manganese steel Wear mechanism Surface hardening behavior

来源：

维普期刊数据库评论

在线全文

维普期刊数据库

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：