Preparation of layered oxide li(Co_(1/3)Ni_(1/3)Mn_(1/3))O_2 via the sol-gel process

Rare Metals 2008年第2期27卷 158-164页

作者： zhang wen liu hanxing hu chen zhu xianjun li yanxi State Key Laboratory of Advanced Technology for Material Synthesis and Processing Wuhan University of Technology Wuhan 430070 China

To obtain homogenous layered oxide li（Co1/3Ni1/3Mn1/3）O2 as a lithium insertion positive electrode material, the sol-gel process using citric acid as a chelating agent was applied. The material li（Co1/3Ni1/3Mn1/3）O2 was synthesized at different calcination temperatures. XRD experiment indicated that the layered li（Co1/3Ni1/3Mn1/3）O2 material could be synthesized at a lower temperature of 800℃, and the oxidation state of Co, Ni, and Mn in the cathode confirmed by XPS were ＋3, ＋2, and ＋4, respectively. SEM observations showed that the synthesized material could form homogenous particle morphology with the particle size of about 200 nm. In spite of different calcination temperatures, the charge-discharge curves of all the samples for the initial cycle were similar, and the cathode synthesized at 900℃ showed a small irreversible capacity loss of 11.24% and a high discharge capacity of 212.2 mAh·g^-1 in the voltage range of 2.9-4.6 V.

关键词： lithium-ion battery layered transition metal oxide sol-gel process high capacity

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：