Journal of Materials Science & Technology 2017年第7期33卷 682-689页

作者： Y.Wang x.q.cai Z.W.Yang D.P.Wang x.G.Liu Y.C.Liu Key Lab of Aclvanced Joining Technology School of Materials Science and Engineering Tianjin University Tiandin 300072 China

Vacuum brazing was successfully used to join Ti-22Al-25Nb alloy using Ti-Ni-Nb brazing alloys prepared by arc-melting. The influence of Nb content in the Ti-Ni-Nb brazing alloys on the interfacial microstructure and mechanical properties of the brazed joints was investigated. The results showed that the interfacial microstructure of brazed joint consisted of B2, O, ？3, and Ti2 Ni phase, while the width of brazing seams varied at different Nb contents. The room temperature shear strength reached359 MPa when the joints were brazed with eutectic Ti40Ni40Nb20 alloy at 1180？C for 20 min, and it was321, 308 and 256 MPa at 500, 650 and 800？C, respectively. Cracks primarily initiated and propagated in ？3compounds, and partially traversed B2＋O region. Moreover, the fracture surface displayed typical ductile dimples when cracks propagated through B2＋O region, which was favorable for the mechanical properties of the brazed joint.

关键词： Ti-22Al-25Nb alloy Ti-Ni-Nb brazing alloy Nb content Microstructure Mechanical properties

THEORETICAL STUDY OF GIANT MAGNETO-IMPEDANCE IN AMORPHOUS FILMS WITH LONGITUDINAL MAGNETIC ANISOTROPY

在线全文

学校读者我要写书评

暂无评论

Acta Metallurgica Sinica(English Letters) 2000年第4期13卷 995-1000页

作者： Yu, J.q. Zhou, Y. cai, B.C. Zhao, x.L. Shanghai Jiaotong Univ Shanghai China

Giant magneto-impedance (MI) effect in thin films with longitudinal magnetic anisotropy was studied theoretically. The effective permeability of films as a function of external magnetic field Ha, anisotropy field and other parameters of films was presented by Landau-Lifshitz-Gilbert theory. The theoretical results agree well with the experimental data, which shows a strong dependence of the impedance on the applied magnetic field.

关键词： Electric currents Magnetic anisotropy Magnetic fields Skin effect

A PROBABILISTIC ASSESSMENT OF TEMPERATURE EFFECTSON THE LOW CYCLE FATIGUE BEHAVIOUR OF 1Cr_(18)Ni_9Ti STEEL WELD METAL

在线全文

学校读者我要写书评

暂无评论

Acta Metallurgica Sinica(English Letters) 1998年第6期11卷 477-484页

作者： q.Gao Y.x.Zhao L.x.cai

Based on the test results obtained from the single-step test and the incremental-step test at room temperature and 240℃, a probabilistic assessment of temperature effects on the cyclic stress-strum response and the fatigue life of 1Cr18Ni9Ti steel weld metal is performed. In orber to assess the temperature effect on cyclic stress amplitude where there is a scatter of the material cyclic constitution, a probabilistic assessment approach on the basis of probabilistic modified Ramberg-Osgood relations is *** investigation shows that the cyclic stress amplitude and the scatter of cyclic stress amplitude data are decreased at 240℃. Similarly, from the consideration of the fatigue life scatter a probabilistic assessment of temperature effect on the fatigue life is suggested on the basis of probabilistic Langer S-N relations. The investigation shows that the crack initiation life is increased and the scatter of crack initiation life data is decreased at 240℃.

关键词： 1Cr_(18)Ni_9Ti stainless steel weld metal low cycle fatigue temperature effect probabilistic assessment

THE REINFORCING MECHANISM OF TiB2 IN TiB2/A357 COMPOSITE

在线全文

学校读者我要写书评

暂无评论

Acta Metallurgica Sinica(English Letters) 2003年第5期16卷 375-378页

作者： B.Yu Y.J.Zhang Z.x.Zhao~ F.x.Zhao: q.K.cai C.S.Liu ShenyangResearchInstituteofFoundry TheChineseAcademyofMachinerySciencesShenyang110022China EastChinaUniversityofScienceandTechnology Shanghai200237China SchoolofMaterials&Metallurgy NortheasternUniversityShenyang110004China

Mechanical properties were tested for in situ TiB2/A357 composite fabricated by LSM (mixed salts reaction) method. Micro structures of as cast and plastic deformed TiB2/A357 were investigated. The results show that there is a low misfit between (200) Al and (101)TiB2 with [011]//Al [101]TiB2. There is a change from fully dendritic structure of the α-Al of A357 to a rosette-type structure of TiB2/A357. Significant increases in proof stress and Young's modulus can be obtained at low TiB2 additions. There exist dislocation loops around neighboring TiB2 particles with about 0.1μm in diameter and dislocation multiplication near TiB2 particles.

关键词： TiB2/Al in situ composite reinforcing mechanism

Stability and optoelectronic property of low-dimensional organic tin bromide perovskites

在线全文

学校读者我要写书评

暂无评论

Chinese Physics B 2021年第3期30卷 483-487页

作者： J H Lei q Tang J He M q cai School of Science Hunan University of TechnologyZhuzhou 412007China School of Physics and Electronics Science Hunan UniversityChangsha 410082China

The toxicity and degradation of hybrid lead-halide perovskites hinder their extensive *** is thus of great importance to explore non-toxic alternative materials with excellent stability and optoelectronic *** investigate the atomic structures and optoelectronic properties of non-toxic organic tin bromide perovskites(OTBP)with one/zerodimensional(1D/0D)structures by first-principles *** calculated atomic structures show that the 1D/0D OTBPs are stable and the structure of inorganic octahedra in 0D is higher order than that in ***,the origination of exceptional purity emitting light in experiments is explained based on the calculated electronic structure.

关键词： one/zero dimensional non-toxic organic tin bromide perovskites first principle calculation stability Optoelectronic property

Solid solution strengthening of high-entropy alloys from first-principles study

在线全文

学校读者我要写书评

暂无评论

Journal of Materials Science & Technology 2022年第26期121卷 105-116页

作者： H.L.Zhang D.D.cai x.Sun H.Huang S.Lu Y.Z.Wang q.M.Hu L.Vitos x.D.Ding State Key Laboratory for Mechanical Behavior of Materials Frontier Institute of Science and TechnologyXi’an Jiaotong UniversityXi’an 710049China Key Laboratory of Shaanxi Province for Craniofacial Precision Medicine Research College of StomatologyXi’an Jiaotong UniversityXi’an 710049China Department of Materials Science and Engineering The Ohio State University2041 College RoadColumbusOH 43210United States Institute of Metal Research Chinese Academy of SciencesShenyang 110016China Science and Technology on Surface Physics and Chemistry Laboratory Jiangyou 621908China Applied Materials Physics Department of Materials Science and EngineeringRoyal Institute of TechnologyStockholm SE-10044Sweden

Solid solution strengthening(SSS)is one kind of strengthening mechanisms and plays an important role in alloy design,in particular for single-phase alloys including high-entropy alloys(HEAs).The classical Labusch–Nabarro model and its expansions are most widely applicable to treating SSS of solid solution alloys including both conventional alloys(CAs)and *** this study,the SSS effects in a series of Febased CAs and HEAs are investigated by using the classical Labusch–Nabarro model and its *** size misfit and shear modulus misfit parameters are derived from first-principles *** on available experimental data in combination with empirical SSS model,we propose fitting constants(i.e.,the ratio between experimental hardness and predicted SSS effect)for these two families of *** predicted host/alloy family-dependent fitting constants can be used to estimate the hardness of these SSS *** agreement between predicted and measured hardness values is satisfactory for both CAs and HEAs,implying that the proposed approach is reliable and successful.

关键词： Alloys Solid solution strengthening Hardness Size misfit parameter Shear modulus misfit parameter First-principles calculations

Closed-Loop Control of MEMS Variable Optical Attenuator (VOA)

在线全文

学校读者我要写书评

暂无评论

光学学报 2003年第S1期23卷 235-236页

作者： H.cai x. M. Zhang A. q. Liu Y. x. Wang C. Lu School of Electrical & Electronic Engineering Nanyang Technological University Nanyang Avenue Singapore 639798 Institute for Infocomm Research Unit 230 Innovation Center Block 2 18 Nanyang Drive Singapore 639798

This paper reports the development of an optical power regulator based on surface-micromachined variable optical attenuators (VOAs). By use of closed-loop control circuits, each VOA module implements the functions of ... 详细信息

关键词： control circuits

Experimental analysis on strength and failure modes of wood beam-column connections

在线全文

学校读者我要写书评

暂无评论

Frontiers of Structural and Civil Engineering 2014年第3期8卷 260-269页

作者： Zhenhua HUANG Sheldon q SHI Liping cai Deportment of Engineering Technology University of North Texas Denton TX 76210 USA

This research experimentally examined the strength, failure modes, and behaviors of dowel-bearing and fiber-bearing wood beam-column connections and explored the effects of cyclic loading on the strength, failure modes, and behaviors of those connections. Base on limited numbers of exploratory laboratory tests （6 preliminary tests in total）, the authors observed that the typical bolted connection （dowel-bearing type wood beam-column connection with fiber- bearing surfaces） showed good behavior （large peak moment） under the monotonic loads, and the tenon joint connection （fiber-bearing wood beam-column connection） showed good behavior under cyclic loads. The cyclic property of loading reduced the strength of the dowel-bearing type wood beam-column connections, but increased the strength of fiber- bearing type wood beam-column connections. More importantly, the authors identified a possible location of safety concern in current national design specifications （NDS） standards for the typical bolted connection （dowel-bearing connection with fiber bearing surface） under cyclic loading because the tested value was smaller than the NDS calculated value. But, because of the small amount of tests conducted, no final conclusion can be drawn based on those preliminary observations yet. A large number of repetitive laboratory tests should be conducted.

关键词： wood connection dowel-beating fiber-bearing

FATIGUE PROPERTIES OF AUSTEMPERED DUCTILE IRON(ADI)IN WATER ENVIRONMENT

维普期刊数据库评论

在线全文

维普期刊数据库

学校读者我要写书评

暂无评论

Acta Metallurgica Sinica(English Letters) 2004年第2期17卷 122-130页

作者： q.Z.cai B.K.Wei Y.Tanaka StateKeyLabofPlasticFormingSimulation＆Dies／MouldTechnology FacultyofMaterialsScienceandEngineeringHuazhongUniversityofScienceandTechnologyWuhan430074China DepartmentofMechanicalSystemsEngineering MuroranInstituteofTechnologyMuroran050-8585Japan

The acicular ferrite in austempered ductile iron (ADI) matrix around graphite wascorroded preferentially in wet condition, promoting crack origination and propagationand resulting in the disappearance of ADI fatigue limit. ADI fatigue strength wasgradually reduced with increasing the time of test and was reduced by 50% in wetcondition at 10~7 cycles compared with the fatigue limit in dry condition. The fatiguestrength variation of ferritic ductile iron in wet condition was similar to that of ADI.The ferritic ductile iron, however, has better corrosion resistance so that the fatiguestrength was lowered only by 10% in wet condition at 10~7 cycles compared with thefatigue limit in dry condition. On the other hand, the fatigue limits of ADI and ferriticductile iron were dropped by 32% and 25% in tap water dipping 480h/dry conditionrespectively compared with those in dry condition. The reduction of fatigue limit wasattributed to corrosion pits formation correlated with stress concentration, resultingin origination and propagation of fatigue crack.

关键词： anstempered ductile iron water environment corrosion fatigue crack fatigue strength

Formation of intermetallic phases in unrefined and refined AA6082 Al alloys investigated by using SEM-based ultramicrotomy tomography

在线全文

学校读者我要写书评

暂无评论

Journal of Materials Science & Technology 2022年第25期120卷 118-128页

作者： J.M.Yu T.Hashimoto H.T.Li N.Wanderka Z.Zhang C.cai x.L.Zhong J.qin q.P.Dong H.Nagaumi x.N.Wang Shagang School of Iron and Steel and High-Performance Metal Structural Materials Research Institute Soochow UniversitySuzhou 215137China School of Materials The University of ManchesterSackville StreetManchester M139PLUK Chinalco Materials Application Research Institute Co.Ltd. Beijing 102200China Helmholtz-Zentrum Berlin Für Materialien und Energie Hahn-Meitner-Platz 1Berlin 14109Germany Key Laboratory of Electromagnetic Processing of Materials Ministry of EducationNortheastern UniversityShenyang 110819China

The spatial arrangement,distribution and morphology of Fe-bearing intermetallics in AA6082 alloys depends on the manufacturing process of the alloy and thus influences the macroscopic ***,the microstructure of a near industrial scale casting AA6082 Al alloy fabricated by:(a)direct chill casting,(b)Al-5 Ti-1 B grain refiner addition and(c)intensive melt shearing has been investigated by threedimensional visualization using SEM-based serial ultra microtomy *** formation sequence of phases in AA6082 alloys is generally categorized into four stages:formation ofα-Al grains,Fe-bearing intermetallics,Mg_(2)Si phase,and eutectic *** of three-dimensional visualization of the microstructure indicated that TiBparticles not only could nucleate Fe-bearingβ-intermetallics,but also could provide substrate for the formation of Fe-bearingα-intermetallics and Mg_(2)Si.A further deep analysis reveals that the essential condition for the formation of secondary phases such as Fe-bearing intermetallics and Mg_(2)Si phase is the build-up of a supersaturated solute front at theα-Al solid-liquid interface irrespective of the specific nucleation *** addition,the results indicate that grain refinement processing causes the severe interconnectivity of Fe-bearingα-***,the intensive melt shearing is a better manufacturing process because the intermetallics are more evenly distributed and refined than with the addition of the grain refiner,thereby improving the properties of the alloy.

关键词： Al-Si-Mg alloy Grain refinement Al-Fe-Si intermetallic phase Tomography Ultramicrotomy Mg2Si