Electrospinning of Nylon-6,6 Solutions into Nanofibers: Rheology and Morphology Relationships

Chinese Journal of Polymer Science 2014年第6期32卷 793-804页

作者： Ali Abbasi Mohamed Mahmoud Nasef Matsuura Takeshi reza faridi-majidi Faculty of Chemical Engineering Universiti Teknologi Malaysia Institute of Hydrogen Economy International Campus Universiti Teknologi Malaysia Malaysia-Japan International Institute of Technology International Campus Universiti Teknologi Malaysia Department of Chemical & Biological Engineering University Ottawa Department of Medical Nanotechnology School of Advanced Medical Technologies Tehran University of Medical Sciences

The relationship between the rheological properties of nylon-6,6 solutions and the morphology of their electrospun nanofibers was established. The viscosity of nylon-6,6 in formic acid （90%） was measured in the concentration range of 5 wt%-25 wt% using a programmable viscometer. Electrospinning of nylon-6,6 solutions was carried out under controlled parameters. The chemical structure, morphology and thermal properties of the obtained nanofibers were investigated using Fourier transform infrared spectroscopy （FTIR）, scanning electron microscopy （SEM） and differential scanning calorimetry （DSC）, respectively, Entanglement concentration （ce） was found to be 15 wt% and a power law relationship between specific viscosity and solution concentration was observed with exponents of 2.0 and 3.3 for semi-dilute unentangled （c 〈 ce） and semi-dilute entangled （c 〉 ce） regimes, respectively. The diameter and uniformity of the nanofibers were found to be dependent on the viscosity. Moreover, the average diameter of electrospun nanofibers was found to be dependent on zero shear rate viscosity and normalized concentration （c/ce） in a power law relationship with exponents of 0.298 and 0.816, respectively. For nylon-6,6 solutions, the entanglement concentration （ce = 15 wt%） provides the threshold viscosity required for the formation of a stable polymeric jet during electrospinning and producing uniform beadless fibers. For concentrations less than ce, beaded fibers with some irregularities are formed. DSC analysis showed an increase in crystallinity of all electrospun samples compared to original polymer. Furthermore; Based on FTIR spectroscopy, α phase is dominant in electrospun nanofibers and minor amount offland ）,phases is also available.

关键词： Nylon-6,6 electrospinning Viscosity Nanofibers Entanglement concentration Crystallinity.

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：