A sandwich-like structure hybrid coating of cold galvanizing coating/polydopamine on hot-dip galvanized steel with enhanced adhesion and corrosion resistance

引用

Science China(Technological Sciences) 2023年第8期66卷 2381-2395页

作者： LI JiWen GAO NingJie ZHANG WanYu XU Long nwokolo kenneth izuchukwu WU Hao LIU FuChun HAN En-Hou Key Laboratory of Nuclear Materials and Safety Assessment Institute of Metal ResearchChinese Academy of SciencesShenyang 110016China School of Materials Science and Engineering University of Science and Technology of ChinaShenyang 110016China Institute of Corrosion Science and Technology Guangzhou 510530China Jihua Laboratory Foshan Guangdong ProvinceFoshan 528000China

This study aims to enhance the adhesion strength and anti-corrosion performance of the cold galvanizing coating(CGC)applied on the hot-dip galvanized steel(HDG).Polydopamine(PDA)is deposited on the HDG surface with different time ranges and as an interlayer between CGC and HDG through covalent *** surface morphology and the covalent interaction between PDA/HDG are exhibited by scanning electron microscope(SEM),atomic force microscopy(AFM)and X-ray photoelectron spectroscopy(XPS).The pull-off adhesion tests before and after neutral slat spry tests show an enhanced dry adhesion strength and less adhesion loss of the hybrid CGC/PDA coated HDG compared with the direct CGC coated *** addition,open circuit potential(OCP)reveals that the corrosion protection performance of the hybrid CGC/PDA coated HDG increases by 200%(up to 201 d)and the corrosion density icorrattaining about 4.45×10^(-7)A/cm^(2).Electrochemical impedance spectroscopy(EIS)measurements and X-ray diffraction(XRD)analysis confirm that the precipitate of the stable chelation formed by PDA and Zn^(2+)between CGC and HDG substrate can also improve the corrosion protection *** a strategy of strengthening adhesion and forming the chelate compound at the HDG surface promises a new route to corrosion protection of CGC on HDG.

关键词： dopamine zinc-rich coatings hot-dip galvanized steel corrosion protection chelate compound

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：