Mechanisms of cast structure and stressed state formation in Hadfield steel

China Foundry 2016年第6期13卷 433-442页

作者： Dmitri Gorlenko konstantin vdovin Nikolay Feoktistov Nosov Magnitogorsk State Technical University Magnitogorsk Russia

The paper describes the investigation of mechanisms of cast structure formation in Hadfield steel depending on the changes in the cooling rate of a casting in the following two temperature ranges: crystallization temperature(1,200-1,390 °С) and the temperature of excessive phase separation(560-790 °С). Changes in the cooling rate of the crystallization temperature range from 1.1 to 25.0 °С·s^(-1) result in the reduction of the average size of austenite grains from 266 to 131 μm. At the same time, the magnitude of developing shrinkage stresses changes from +195 to 0 MPa. When the cooling rate is higher than 16 °С·s^(-1), no shrinkage stresses are formed in the casting. Changes in the cooling rate of the casting in the temperature range of the excessive phase separation influence the number of phases, their morphology and chemical composition, the values of phase stresses, and the possibility of martensitic transformation. Changing in the cooling rate from 0.24 to 5.46 °С·s^(-1) results in the decrease of the amount of the excessive phase from 14.8% to 2.1%, which is composed of eutectic and carbides depending on the cooling rate, their quantitative ratio and morphology change. Such changes in the microstructure are reflected on the changes of value of developing phase stresses. When the cooling rate is 0.24 °С·s^(-1), it is +100 MPa, while the increase of the cooling rate to 1.4 °С·s^(-1) results in the decrease of tensile stresses to 0 MPa and their qualitative stresses change to compressive ones. Further increase of the cooling rate results in the increase of the value of compressive stresses. When the cooling rate is 5.5 °С·s^(-1), their value reaches-92 MPa. Martensite forming in the structure of Hadfield steel is possible if the cooling rate of the casting in the range of excessive phase separation is less than 0.25 °С·s^(-1).

关键词： Hadfield steel crystallization austenite excessive phase stress

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：