Acta Metallurgica Sinica(English Letters) 2021年第11期34卷 1591-1600页

作者： Yong Xie Zhixin Xia jixin hou Jiachao Xu Peng Chen Le Wan Shagang School of Iron and Steel Soochow UniversitySuzhou 215131China School of Mechanical and Electric Engineering Soochow UniversitySuzhou 215131China

CoCrNiCux(x=0.16,0.33,0.75,and 1)without macro-segregation medium-entropy alloys(MEAs)was prepared using laser directed energy deposition(LDED).The microstructure and mechanical properties of CoCrNiCux alloys with increasing Cu content were *** results indicate that a single matrix phase changes into a dual-phase structure and the tensile fracture behaviors convert from brittle to plastic pattern with increasing Cu content in CoCrNiCux *** addition,the tensile strength of CoCrNiCux alloys increased from 148 to 820 MPa,and the ductility increased from 1 to 11%with increasing Cu *** nano-precipitated particles had a mean size of approximately 20 nm in the Cu-rich phase area,and a large number of neatly arranged misfit dislocations were observed at the interface between the two phases due to Cu-rich phase precipitation in the CoCrNiCu *** misfit dislocations hinder the movement of dislocations during tensile deformation,as observed through transmission electron *** allows the CoCrNiCu alloy to reach the largest tensile strength and plasticity,and a new strengthening mechanism was achieved for the CoCrNiCu ***,twins were observed in the matrix phase after tensile ***,the dual-phase structure with different elastic moduli coordinated with each other during the deformation process,significantly improving the plasticity and strength of the CoCrNiCu alloy.

关键词： Medium-entropy alloys Mechanical properties Laser directed energy deposition Misfit dislocations Cu-rich phase

The structural change of Cu-Sn melt

在线全文

学校读者我要写书评

暂无评论

Science China(Physics,Mechanics & Astronomy) 2007年第4期50卷 414-420页

作者： hou jixin SUN JianJun ZHAN ChengWei TIAN XueLei CHEN XiChen Key Laboratory of Liquid Structure and Heredity of Materials of Ministry of Education Shandong UniversityJinan 250061China

With the high-temperature viscometer and magnetic susceptibility measurement device designed by our group,the viscosity and the magnetic susceptibility of the Cu65Sn35 melt were measured during the cooling *** anomalous change can be found in the curves of viscosity and magnetic susceptibility at a certain *** structure of the melt was studied by the high-temperature X-ray *** anomalous change also can be found in the pair distribution function,correlation radius,and coordination number at the approximate tem-perature,which shows the microstructural change of the Cu65Sn35 *** the results,it was confirmed that the Cu6Sn5 compound occurs in the melt,which leads to the structural change of the melt.

关键词： Cu-Sn alloy melt structure

Effect of Laser Welding Process Parameters on Microstructure and Mechanical Properties on Butt Joint of New Hot-Rolled Nano-scale Precipitation-Strengthened Steel

在线全文

学校读者我要写书评

暂无评论

Acta Metallurgica Sinica(English Letters) 2014年第3期27卷 521-529页

作者： Min Zhang Xiaonan Wang Guangjiang Zhu Changjun Chen jixin hou Shunhu Zhang Hemin Jing Laser Processing Research Center School of Mechanical and Electrical Engineering Soochow University Shagang School of Iron and Steel Soochow University School of Materials Science & Engineering Anhui University of Technology

A 4 kW fiber laser was chosen to weld the new hot-rolled nano-scale precipitation-strengthened steel with a thickness of 4.5 mm. The effect of laser power, defocusing distance, and welding speed on the welded joint appearance was examined, and the microstructure and mechanical properties on the typical butt joints were investigated. Results showed that increasing laser welding power may cause faster downward flow of molten metal to produce greater root humping. With the welding speed increasing, the average welding seam （WS） width decreased, and the average WS and heat-affected zone （HAZ） hardness increased. The microstructures of WS, fusion line, and coarse grain heat-affected zone were lath martensite, but the growth direction of the original austenite grain boundaries was significantly different. The microstructures of fine grain heat-affected zone were ferrite and martensite, and the microstructure of mixed grain heat- affected zone contained ferrite, massive M/A island, and a small amount of martensite. The micro-hardness values of WS, HAZ, and base metal （BM） were 358, 302, and 265 HV, respectively. The butt joint fracture at the BM far from the WS and the welded joint tensile strength are observed to follow proportional relationship with hardness.

关键词： Laser welding Microstructure Mechanical properties Microalloyed steel

316L不锈钢表面激光熔化沉积CoCrNiCu中熵合金的界面相容性

在线全文

学校读者我要写书评

暂无评论

金属学报 2024年第9期60卷 1213-1228页

作者：于云鹤谢勇陈鹏董浩凯侯纪新夏志新苏州大学沙钢钢铁学院苏州215137 华南理工大学机械与汽车工程学院广州510641

异种材料界面相容性是制约结合强度的关键因素,然而其内在机制仍待完善。本工作开展了316L不锈钢表面激光熔化沉积CoCrNiCu中熵合金实验,借助SEM、STEM、EBSD、透射Kikuchi衍射(TKD)等手段对异种材料显微组织与界面特征进行表征,测试了... 详细信息

异种材料界面相容性是制约结合强度的关键因素,然而其内在机制仍待完善。本工作开展了316L不锈钢表面激光熔化沉积CoCrNiCu中熵合金实验,借助SEM、STEM、EBSD、透射Kikuchi衍射(TKD)等手段对异种材料显微组织与界面特征进行表征,测试了异种材料界面力学性能,进而通过系统研究界面组织与晶体学相容性提出改善结合强度的方法。结果表明,CoCrNiCu中熵合金与316L不锈钢异种材料界面处形成了CoCrNiCuFe高熵合金全固溶过渡区,异种材料剪切强度可达324 MPa。在C元素界面配分引发奥氏体稳定性降低以及残余应力引发塑性变形的协同作用下,316L不锈钢靠近异种材料界面处的部分奥氏体晶粒发生应变诱导马氏体相变,这在促进相变诱导塑性(TRIP)效应的同时也会导致界面匹配程度降低。因此,对于物性差异较小的异种材料应保持相同晶体结构的单相匹配,通过提高界面晶体学相容性改善界面结合强度;对于物性差异较大的异种材料可借助TRIP效应设计双相结构以提高协调变形能力。

关键词：增材制造激光熔化沉积异种材料界面设计中熵合金不锈钢

重熔处理对铝基非晶合金腐蚀性能的影响（英文）

在线全文

学校读者我要写书评

暂无评论

稀有金属材料与工程 2017年第2期46卷 296-300页

作者：刘景涛侯纪新张晓蓉郭晶许令峰樊桂菊山东农业大学山东泰安271018 山东省园艺机械与装备重点实验室山东泰安271018 苏州大学江苏苏州215021

通过极化扫描,EIS,XRD和SEM技术研究了Gd_(56)Al_(26)Co_(18)和Sm_(56)Al_(26)Co_(18)非晶合金在0.01 mol/L氢氧化钠溶液中的腐蚀行为,同时通过DSC研究了自由体积。非晶合金在0.01 mol的NaOH碱溶液中腐蚀后发现经过重熔处理增加了它的... 详细信息

通过极化扫描,EIS,XRD和SEM技术研究了Gd_(56)Al_(26)Co_(18)和Sm_(56)Al_(26)Co_(18)非晶合金在0.01 mol/L氢氧化钠溶液中的腐蚀行为,同时通过DSC研究了自由体积。非晶合金在0.01 mol的NaOH碱溶液中腐蚀后发现经过重熔处理增加了它的耐腐蚀性能。Gd基非晶条带在0.01 mol/L的NaOH碱溶液中的耐腐蚀性要优于Sm基非晶条带。另外通过研究发现,重熔后的非晶条带含有的自由体积比第1次制备的非晶条带要少。

关键词：腐蚀行为非晶合金电化学阻抗图谱自由体积

Co_(79.5)Sn_(20.5)合金结构及等效磁导率的变化

在线全文

学校读者我要写书评

暂无评论

稀有金属材料与工程 2010年第3期39卷 528-530页

作者：詹成伟侯纪新田学雷马兆领王永志山东大学材料液态结构及其遗传性教育部重点实验室山东济南250061

使用DSC分析Co79.5Sn20.5合金在降温过程中的热量变化,并使用自主设计的等效磁导率测量仪测量此合金在降温过程中等效磁导率的变化情况。当Co79.5Sn20.5合金发生结构变化时,其热量和等效磁导率都存在明显的突变。研究Co79.5Sn20.5合金... 详细信息

使用DSC分析Co79.5Sn20.5合金在降温过程中的热量变化,并使用自主设计的等效磁导率测量仪测量此合金在降温过程中等效磁导率的变化情况。当Co79.5Sn20.5合金发生结构变化时,其热量和等效磁导率都存在明显的突变。研究Co79.5Sn20.5合金在固态的无序-有序相变过程中结构及等效磁导率的变化,比较不同物理性质对合金结构变化的表征情况的结果表明,合金等效磁导率的变化可以表征其液-固相变、居里转变以及固态相变等结构转变。

关键词： Co-Sn合金结构磁导率

在线全文

学校读者我要写书评

暂无评论

新型Fe基非晶复合涂层的制备及性能研究

中国激光 2015年第11期42卷 100-105页

作者：侯纪新章顺虎周巍王晓南蒋小舟朱广江苏州大学沙钢钢铁学院江苏苏州215021 安徽工业大学材料科学与工程学院安徽马鞍山243002

利用IPG YLS4000光纤激光器,采用激光熔覆工艺在某高强钢基体上制备了一种新型含氮Fe基非晶复合涂层。通过X射线衍射仪物相分析发现,在3种不同激光工艺下制备的涂层在非晶基体上出现了不同含量的晶化相,分别对3种工艺下制备的涂层与基... 详细信息

利用IPG YLS4000光纤激光器,采用激光熔覆工艺在某高强钢基体上制备了一种新型含氮Fe基非晶复合涂层。通过X射线衍射仪物相分析发现,在3种不同激光工艺下制备的涂层在非晶基体上出现了不同含量的晶化相,分别对3种工艺下制备的涂层与基体材料的硬度、耐磨及耐蚀性能进行了测试分析。结果表明,与基体材料相比,3种涂层的硬度、耐磨及耐蚀性均有明显提高,其中在1.5 k W激光功率、180 mm/min扫描速度条件下制备的涂层非晶含量最高,表现出最好的性能。研究认为合适的工艺才能制备出性能优良的涂层,涂层中非晶相含量的增加能够明显改善涂层的性能。

关键词：激光光学激光熔覆 Fe基非晶复合涂层硬度耐磨损性耐蚀性

耐腐蚀桥梁钢板超声波探伤缺陷分析及改进措施

在线全文

学校读者我要写书评

暂无评论

热加工工艺 2015年第24期44卷 232-234,237页

作者：侯纪新肖震东王晓南章顺虎苏州大学沙钢钢铁学院江苏苏州215021

利用金相、扫描电镜及金属原位统计分析等技术研究了某桥梁钢板超声波探伤缺陷区域,发现在钢板厚度中心区域存在严重的带状组织,C元素在带状组织中分布极不均匀,存在明显偏析。同时,在该区域还存在大量的非金属夹杂物。结果表明:钢板厚... 详细信息

利用金相、扫描电镜及金属原位统计分析等技术研究了某桥梁钢板超声波探伤缺陷区域,发现在钢板厚度中心区域存在严重的带状组织,C元素在带状组织中分布极不均匀,存在明显偏析。同时,在该区域还存在大量的非金属夹杂物。结果表明:钢板厚度中心区域C元素严重偏析及大量非金属夹杂物的耦合作用是引起钢板超声波探伤不合格的主要原因。

关键词：桥梁钢超声波探伤偏析夹杂物

新工科背景下金属材料工程专业创新型人才培养体系的探究与实践

在线全文

学校读者我要写书评

暂无评论

中国现代教育装备 2023年第23期 97-99页

作者：王慧华侯栋侯纪新苏州大学沙钢钢铁学院江苏苏州215137

探讨了新工科背景下金属材料工程专业创新型人才培养的改革方案。为了培养创新型人才,需要以实践能力培养和创新方法训练为主要抓手,通过理论强化、现场认知、模拟仿真、工程实践4个环节提升学生的工程实践能力,同时以TRIZ创新方法和6... 详细信息

探讨了新工科背景下金属材料工程专业创新型人才培养的改革方案。为了培养创新型人才,需要以实践能力培养和创新方法训练为主要抓手,通过理论强化、现场认知、模拟仿真、工程实践4个环节提升学生的工程实践能力,同时以TRIZ创新方法和6σ理论为基础,通过方法集成和创新应用培养学生的创新能力。通过研究与探索,形成一套适应新经济发展需求、多学科交叉融合的金属材料工程专业新课程体系,实现传统专业的改造升级,构建创新型人才培养新模式。

关键词：创新型人才信息技术 TRIZ创新方法 6σ理论课程体系

激光熔覆工艺参数及微合金元素对Fe基非晶复合涂层显微硬度的影响

在线全文

学校读者我要写书评

暂无评论

应用激光 2015年第4期35卷 402-407页

作者：侯纪新章顺虎蒋小舟陈长军王晓南苏州大学沙钢钢铁学院江苏苏州215021 苏州大学机电工程学院江苏苏州215021

采用预置粉末的方法,在700 MPa钢板表面利用激光熔覆技术制备了含氮Fe基非晶复合涂层。通过分析扫描速度及功率对熔覆层显微硬度的影响,发现只有在适当的扫描速度下制备的熔覆层才具有较高的显微硬度;而在一定扫描速率下,当激光功率在1.... 详细信息

采用预置粉末的方法,在700 MPa钢板表面利用激光熔覆技术制备了含氮Fe基非晶复合涂层。通过分析扫描速度及功率对熔覆层显微硬度的影响,发现只有在适当的扫描速度下制备的熔覆层才具有较高的显微硬度;而在一定扫描速率下,当激光功率在1.5kW时制备的熔覆层具有相对较高的显微硬度。与此同时,讨论了微合金元素Nb的添加以及N元素的含量对熔覆层显微硬度的影响。

关键词：激光熔覆 Fe基非晶复合涂层工艺参数微合金元素显微硬度