Destruction of charge ordering phase in La_(0.4)Ca_(0.6)MnO_3 induced by low Cr doping

在线全文

学校读者我要写书评

暂无评论

Rare Metals 2011年第3期30卷 241-246页

作者： PENG Zhensheng YANG Gang WANG Guiying TANG Yonggang guo huanyin MAO Qiang Anhui Key Laboratory of Spintronic and Nanometric Materials Cultivating Base Suzhou College Suzhou 234000 China Hefei National Laboratory for Physical Sciences at the Microscale University of Science and Technology of China Hefei 230026 China Department of Electronics and Electric Engineering Suzhou College Suzhou 234000 China

Polycrystalline samples of La0.4Cao.6Mn1-xCrxO3 （x = 0.00, 0.02, 0.04, 0.06） were prepared by the solid state reaction method. The influence of Cr3＋ substitution for Mn3＋ on the magnetic property and charge ordering phase of La0.4Ca0.6MnO3 was studied through the measurements of X-ray diffraction （XRD）, magnetization-temperature （M-T） curves and electron spin resonance （ESR） spectra. The experimental results indicate that the mother＇s body of La0.4Ca0.6MnO3 has very complicated magnetic structure, exhibits charge ordering phase at 258 K, and shows long-range strongly correlated charge ordering-antiferromagnetism （CO-AFM） phase from 175 to 50 K. Spin glass state appears when the temperature decreases to about 41 K. When the Cr substitution amount is x = 0.06, the charge ordering phase of the mother＇s body is de-stroyed, because the Cr3＋ substitution for Mn3＋ destroys the spin order of CE-type antiferromagnetism, and thus leads to the melting of charge ordering. It is verified experimentally that the strong coupling between charge order and spin order exists in the charge order system of CE-type antiferromagnetism.

关键词： perovskite manganite chromium doping charge ordering spin-glass state

Research on charge ordering and magnetic properties in La_(0.3)Ca_(0.7)Mn_(1-x)W_xO_3 system

在线全文

学校读者我要写书评

暂无评论

Rare Metals 2007年第4期26卷 317-322页

作者： PENG Zhensheng guo huanyin YAN guoqing MAO Qiang Physics Department Suzhou College Suzhou 234000 China Structure Research Laboratory University of Science and Technology of China Hefei 230026 China

The perovskite manganite sample La0.3Ca0.7Mn1-xWxO3 （x = 0.08, 0.12） was prepared by the solid-state reaction method. The effect of W doping on the Mn site to La0.3Ca0.7MnO3 charge ordering phase and the changing process of magnetic properties were studied through the measurement of the M-T curve, M-H curves, and ESR curves of the sample. The results showed that when x = 0.08, the charge ordering （CO） phase exists in the system, the transition temperature Tco= 275 K, and the system exhibits PM when T 〉 275 K. The system transforms from spin-disordering paramagnetism to spin-ordering antiferromagnetism in the charge ordering state with the temperature decreasing from 275 K to 230 K. The long-range antiferromagnetism forms and AFM/CO states coexist between 230 K and 5 K. There is a little ferromagnetic component in the AFM/CO background in a low temperature range. When x = 0.12, the CO phase in the system has almost melted completely. There is a little remnant of the CO phase below 150 K. The system exhibits paramagnetism when T 〉 150 K and transforms from paramagnetism to ferromagnetism when T〈 150 K.

关键词： condensed matter physics charge ordering melting solid-state reaction method magnetic properties

Charge order and spin orderof La_(0.3)Ca_(0.7)Mn_(1-x)W_(x)O_(3) system

在线全文

学校读者我要写书评

暂无评论

Chinese Science Bulletin 2006年第7期51卷 770-776页

作者： LIU Ning YAN guoqing CAI Zhirang guo huanyin PENG Zhensheng QU Zhe ZHANG Yuheng Materials Research Laboratory Suzhou College Suzhou 234000 China Structure Research Laboratory University of Science and Technology of China Hefei 230026 China

The influences of W doping at Mn site on the charge order and spin order were studied by measuring M-T curves, M-H curves and ESR spectra of La0.3Ca0.7Mn1?xWxO3 (x = 0.00, 0.04, 0.08, 0.12, 0.15) system. The results showed that: When 0.00≤ x≤0.08, the system exhibits charge ordering (CO) phase, and its spin order experiences the change of paramagnetism (PM)-charge ordering (CO)-antiferro- magnetism (AFM) with decreasing temperature; when x≥0.12, the charge ordering (CO) phase melts, part of charge ordering (CO)phase remains in the paramagnetism (PM)background, the spin order of the system is mainly paramagnetism (PM), and ferromagnetic (FM) clusters appear at low tem- perature.

关键词： La0.3Ca0.7Mn(1-x)WxO3 稀土熔炼残渣炉料

La_(0.67-x)Sm_xSr_(0.3)3MnO_3陶瓷中的相分离和输运特性

在线全文

学校读者我要写书评

暂无评论

硅酸盐学报 2005年第6期33卷 746-752页

作者：刘宁郭焕银徐素军童伟宿州学院物理系安徽宿州234000 中国科学技术大学结构分析开放实验室合肥230026

测量了La0.67-xSmxSr0.33MnO3(x=0.00,0.10,0.20,0.30,0.40,0.50,0.60)陶瓷的磁化强度温度曲线、电子自旋共振谱曲线和电阻率温度曲线。实验结果表明:x=0.00,0.10时,样品为长程铁磁有序;x=0.20,0.30时,样品为自旋团簇玻璃态;x=0.40,0.50,0.60时,样品在低温时表现为反铁磁状态;x=0.30和0.40的样品在Curie温度TC以上温区发生相分离。高掺杂(x=0.60)样品的输运行为发生异常,在TC附近发生绝缘体-金属相变后,又发生金属绝缘体相变,这在ABO3结构中很少出现。陶瓷的磁电行为变化取决于掺杂引起的额外磁性和晶格畸变效应。

关键词：磁结构相分离输运行为多晶

Gd掺杂对La_(0.67)Sr_(0.33)CoO_3、La_(0.67)Sr_(0.33)MnO_3体系磁行为的影响(英文)

在线全文

学校读者我要写书评

暂无评论

稀有金属材料与工程 2012年第1期41卷 19-23页

作者：刘宁严国清朱光郭焕银安徽科技学院安徽凤阳233100 宿州学院安徽省高校自旋电子与纳米材料重点实验室培育基地安徽宿州234000 南京大学固体微结构物理国家重点实验室江苏南京210093

研究了La0.67-xGdxSr0.33CoO3、La0.67-xGdxSr0.33MnO3 (x=0.00, 0.05, 0.10, 0.20, 0.30, 0.40, 0.50, 0.60, 0.67)体系的M-T曲线、M-H曲线。结果表明:随Gd掺杂浓度增高,La0.67-xGdxSr0.33CoO3体系的磁结构表现为团簇玻璃态,x>0.10样品的M-T曲线出现了低温区M值急剧上升的奇特现象;La0.67-xGdxSr0.33MnO3体系的磁结构从长程铁磁有序向团簇玻璃态、反铁磁状态转变,x≥0.50样品的M-T曲线在低温区急剧下降。两种体系呈现的不同现象,来源于Gd与Co、Mn不同的耦合作用和Co的自旋态的转变。

关键词：凝聚态物理磁结构耦合作用自旋态转变

Dy和Sm部分替代La对La_(0.7)Sr_(0.3)MnO_3磁电行为的影响

在线全文

学校读者我要写书评

暂无评论

稀有金属 2005年第2期29卷 143-148页

作者：郭焕银刘宁童伟宿州学院物理系安徽宿州234000 中国科学技术大学结构分析重点实验室安徽合肥230026

通过对La0 .7-xTxSr0 .3MnO3(T =Dy ,Sm)系列样品的红外透射谱,激光拉曼谱,M T曲线和ρT曲线的测量,研究了该样品的磁电行为。结果发现,随着掺入量的增加,样品的顺磁铁磁相变温度逐渐降低,磁结构从顺磁向自旋团簇玻璃态、反铁磁状态转... 详细信息

通过对La0 .7-xTxSr0 .3MnO3(T =Dy ,Sm)系列样品的红外透射谱,激光拉曼谱,M T曲线和ρT曲线的测量,研究了该样品的磁电行为。结果发现,随着掺入量的增加,样品的顺磁铁磁相变温度逐渐降低,磁结构从顺磁向自旋团簇玻璃态、反铁磁状态转变,样品的磁电阻迅速增加。有趣的是在较低温度下,Dy掺杂M T曲线出现比较奇特的尖峰,而Sm掺杂M T曲线比较变化较平坦。对Dy ,Sm掺杂的作用可以用晶格效应和额外磁性的竞争来解释。

关键词：稀土锰氧化物额外磁性晶格效应稀土

La_(0．3)Ca_(0．7)Mn_(1-x)W_xO_3体系中电荷有序及磁性质研究

在线全文

学校读者我要写书评

暂无评论

稀有金属材料与工程 2006年第A02期35卷 202-205页

作者：彭振生郭焕银严国清毛强宿州学院材料研究室

采用固相反应法制备了钙钛矿锰氧化物La0.3Ca0.7Mn1-xWxO3(x=0．08,0．12)样品,通过M-T曲线、M-H曲线、ESR曲线研究了在Mn位掺W对La0.3Ca0.7MnO3电荷有序相的影响以及磁结构的变化过程。结果表明:当x=0．08时,体系存在电荷有序(CO)相,... 详细信息

采用固相反应法制备了钙钛矿锰氧化物La0.3Ca0.7Mn1-xWxO3(x=0．08,0．12)样品,通过M-T曲线、M-H曲线、ESR曲线研究了在Mn位掺W对La0.3Ca0.7MnO3电荷有序相的影响以及磁结构的变化过程。结果表明:当x=0．08时,体系存在电荷有序(CO)相,相变温度Tco=275 K,在T>275 K时体系表现为PM:当温度从275 K下降到230 K,体系在CO相下从自旋无序的顺磁态向自旋有序的反铁磁态转变;在230 K至5 K形成长程反铁磁态,AFM／CO态共存;低温区在AFM／CO态本底中存在一定的铁磁成分。当x=0．12时,体系的CO相已基本融化,150 K以下还残留少量CO相。在高于150 K温区表现为顺磁;在低于150 K温区从顺磁向铁磁转变。

关键词：钙钛矿锰氧化物电荷有序融化磁性质

Dy掺入对La_(0.7)Sr_(0.3)CoO_3体系磁性的影响

在线全文

学校读者我要写书评

暂无评论

稀有金属材料与工程 2010年第5期39卷 874-877页

作者：刘宁严国清郭焕银毛强蔡之让安徽科技学院安徽凤阳233100 宿州学院安徽宿州234000 南京大学南京210093

通过M-T、M-H曲线的测量,研究Dy掺入对La0.7Sr0.3CoO3体系磁性的影响。结果表明,随着Dy含量的增加,样品Tc降低、M值减弱、矫顽力增强,并出现低温下M随着T的降低继续增大的反常现象。研究表明,体系磁性的变化来源于Dy掺入引起晶格参数的... 详细信息

通过M-T、M-H曲线的测量,研究Dy掺入对La0.7Sr0.3CoO3体系磁性的影响。结果表明,随着Dy含量的增加,样品Tc降低、M值减弱、矫顽力增强,并出现低温下M随着T的降低继续增大的反常现象。研究表明,体系磁性的变化来源于Dy掺入引起晶格参数的改变和磁环境的改变,以及Dy离子诱导的Co离子自旋态的转变。

关键词： La0.7Sr0.3CoO3体系团簇玻璃态自旋态转变

La_(0.67-x)Sm_xSr_(0.33)MnO_3(x=0.40,0.50,0.60)体系的磁、电行为

在线全文

学校读者我要写书评

暂无评论

稀有金属材料与工程 2006年第3期35卷 343-347页

作者：刘宁童伟郭焕银彭振生严国清宿州学院安徽宿州234000 中国科学技术大学结构分析开放实验室安徽合肥230026

测量了La0.67-xSmxSr0.33MnO3(x=0.40,0.50,0.60)体系的M-T曲线,ρ-T曲线和MR-T曲线。实验结果表明:x=0.40时,样品为长程铁磁有序;x=0.50时,样品为自旋团簇玻璃态;x=0.60时,样品在低温时表现为反铁磁状态。高掺杂(x=0.60)样品的输运行... 详细信息

测量了La0.67-xSmxSr0.33MnO3(x=0.40,0.50,0.60)体系的M-T曲线,ρ-T曲线和MR-T曲线。实验结果表明:x=0.40时,样品为长程铁磁有序;x=0.50时,样品为自旋团簇玻璃态;x=0.60时,样品在低温时表现为反铁磁状态。高掺杂(x=0.60)样品的输运行为发生异常,在Tc附近发生绝缘体-金属相变后,又发生金属-绝缘体相变的现象,这在ABO3结构中很少出现。体系的磁电行为变化取决于掺杂引起的额外磁性和晶格畸变效应。

关键词：磁结构输运行为庞磁电阻效应