Effect of hydro co-extrusion on microstructure of duo-cast Al3003/Al4004 clad materials

在线全文

学校读者我要写书评

暂无评论

Transactions of Nonferrous Metals Society of China 2014年第S1期24卷 75-80页

作者： In-Soo SON Sang-Pill lee Jin-Kyung lee Woo-Cheol KIM Ji-Seon MOON Sangmok lee Jong-Sup lee Yong-Bae KIM geun-ahn lee Dong-Su BAE Department of Mechanical Engineering Dong-Eui University Busan Korea Department of Advanced Materials Engineering Dong-Eui University Busan Korea Advanced Forming Tech. Center Korea Institute of Industrial Technology Incheon Korea

The effects of hydro co-extrusion on the microstructure changes of aluminum hybrid duo-cast Al 3003/Al 4004 clad materials were studied. The specimen of duo-cast Al 3003/Al 4004 clad materials was in circle shape, and was composed of Al 3003(outside) and Al 4004(inside) materials. The specimen was extruded by the hydro co-extrusion equipment. The manufacturing conditions of the specimen were 423 K in temperature and 5 in extrusion ratio. The dimensions of the specimen were 80 mm in diameter of the Al 4004 material and 35 mm in thickness of the Al 3003 material before the hydro co-extrusion process, and 30 mm in diameter and about 5 mm in thickness after the extrusion process, respectively. The microstructure and the hardness for two specimens were investigated. The hardness value of cross section in the duo-cast Al 3003/Al 4004 clad materials before the extrusion process was increased in form of the parabola toward the center. However, after the extrusion process, it was almost constant in the portion of Al 4004 material. Lots of big voids above 1 mm in diameter in the specimen existed in the interfacing region of Al 3003 and Al 4004 materials before the extrusion process. These big voids disappeared after the process of hydro co-extrusion.

关键词： clad materials hydro co-extrusion process duo-casting microstructure

Prominent cycling reversibility and kinetics enabled by CaTiO3 protective layer on Zn metal for aqueous Zn-ion batteries

在线全文

学校读者我要写书评

暂无评论

Journal of Energy Chemistry 2025年第1期100卷 245-258页

作者： Gaeun lee Yong Nam ahn Seongjoon So Chanwoo Park Jong-Seong Bae Taehyun Park Il Tae Kim Jaehyun Hur School of Chemical Biological and Battery Engineering Gachon University Seongnam Busan Center Korea Basic Science Institute

Aqueous Zn-ion batteries （AZIBs） have received considerable attention owing to their various advantages such as safety,low cost,simple battery assembly conditions,and high ionic ***,they still suffer from serious problems,including uncontrollable dendrite growth,corrosion,hydrogen evolution reaction （HER） from water decomposition,electrode passivation,and unexpected *** creation of a uniform artificial nanocrystal layer on the Zn anode surface is a promising strategy for resolving these ***,we propose the use of a perovskite CaTiO3（CTO） protective layer on Zn（CTO@Zn） as a promising approach for improving the performance of *** CTO artificial layer provides an efficient pathway for Zn ion diffusion towards the Zn metal because of the high dielectric constant （εr=180） and ferroelectric characteristics that enable the alignment of dipole moments and redistribute the Zn2+ions in the CTO *** avoiding the direct contact of the Zn anode with the electrolyte solution,the uneven dendrite growth,corrosion,parasitic side reactions,and HER are mitigated,while CTO retains its mechanical and chemical robustness during ***,CTO@Zn demonstrates an improved lifespan in a symmetric cell configuration compared with bare ***@Zn shows steady overpotential （～68 m V） for 1500 h at 1 mA cm-2/0.5 mA h cm-2,excelling bare ***,when paired with the V2O5-C cathode,the CTO@Zn//V2O5-C full battery delivers 148.4 mA h g-1（based on the mass of the cathode） after 300 *** study provides new insights into Zn metal anodes and the development of high-performance AZIBs.

关键词： Artificial layer Dielectric constant Zn metal anode Zinc aqueous battery

Poly-gamma-glutamic acid from Bacillus subtilis upregulates pro-inflammatory cytokines while inhibiting NLRP3, NLRC4 and AIM2 inflammasome activation

在线全文

同方期刊数据库

学校读者我要写书评

暂无评论

Cellular & Molecular Immunology 2018年第2期15卷 111-119页

作者： Huijeong ahn Seung Goo Kang Sung-il Yoon Pyeung-Hyeun Kim Doo Kim geun-Shik lee College of Veterinary Medicine and Institute of Veterinary Science Kangwon National UniversityChuncheon24341GangwonRepublic of Korea Department of Systems Immunology College of Biomedical ScienceKangwon National UniversityChuncheon24341GangwonRepublic of Korea Department of Molecular Bioscience School of Biomedical ScienceKangwon National UniversityChuncheon24341GangwonRepublic of Korea

Poly-gamma-glutamic acid(γ-PGA)is a natural,edible and non-toxic polymer synthesized by Bacillus subtilis and is suggested as a safe biomaterial for the use in hydrogels and vaccine ***,the effect ofγ-PGA on inflammasome activation has not yet been studied in ***,which are intracellular multi-protein complexes,promote acute and chronic inflammation via interleukin-1βor interleukin-18 maturation,and they are known targets for metabolic syndromes and *** this study,we observed thatγ-PGA attenuated NLRP3,NLRC4 and AIM2 inflammasome activation,whereas it upregulated pro-inflammatory cytokine expression in human and murine ***γ-PGA had conflicting effects on cytokine production and maturation,it clearly alleviated the severity of lipopolysaccharide-induced endotoxin shock in an animal ***,we suggestγ-PGA as a candidate to control inflammasome-mediated disorders.

关键词： Cheonggukjang cytokines inflammasome macrophages poly-gamma-glutamate

Role of inflammasome regulation on immune modulators

维普期刊数据库评论

在线全文

维普期刊数据库

学校读者我要写书评

暂无评论

The Journal of Biomedical Research 2018年第6期32卷 401-410页

作者： Huijeong ahn Hyuk Moo Kwon Eunsong lee Pyeung-Hyeun Kim Eui-Bae Jeung geun-Shik lee College of Veterinary Medicine and Institute of Veterinary Science Department of Molecular Bioscience School of Biomedical ScienceKangwon National UniversityChuncheon 24341Republic of Korea Laboratory of Veterinary Biochemistry and Molecular Biology College of Veterinary MedicineChungbuk National UniversityCheongju 28644Republic of Korea.

Inflammatory responses are essential in eliminating harmful substrates from damaged tissue and inducing *** cytokines participate in and facilitate this response. Certain cytokines such as interleukin(IL)-1β and IL-18 are initially produced in precursor form in response to toll-like receptor(TLR) ligands and undergo maturation by inflammasomes, which are cytosolic multi-protein complexes containing nucleotide-binding oligomerization domain(NOD)-containing protein 2-like receptors(NLRs). Immune modulators targeting inflammasomes have been investigated to control inflammatory diseases such as metabolic syndrome. However, most immune modulators possessing anti-inflammasome properties attenuate production of other cytokines, which are essential for host defense. In this review, we analyzed the effect of anti-inflammasome agents on the production of cytokines which are not regulated by inflammasome and involving in initial immune responses. As a result, the infiammasome inhibitors are put into three categories: non-effector, stimulator, or inhibitor of cytokine production. Even the stimulator of cytokine production ameliorated symptoms resulting from inflammasome activation in mouse models. Thus, we suggest ideal immune modulators targeting inflammasomes in order to enhance cytokine production while inhibiting cytokine maturation.

关键词： immune modulator inflammasome macrophages interleukin-1β

Effect of carrier gas species on the microstructure and compressive deformation behaviors of ultra-strong pure copper manufactured by cold spray additive manufacturing

在线全文

学校读者我要写书评

暂无评论

Journal of Materials Science & Technology 2022年第2期97卷 264-271页

作者： Young-Kyun Kim Kee-ahn lee Department of Materials Science and Engineering Inha UniversityIncheon 22212Republic of Korea

Cold spray(CS)which has recently become a promising additive manufacturing(AM)technology,was used to fabricate ultra-strong pure *** addition,the effects of carrier gas species on the microstructural characteristics,mechanical properties and deformation mechanisms were systemically *** CSAM copper manufactured with N_(2) carrier gas reveals a heterogeneous bimodal microstructure consisting of ultra-fine grains at the particle interface and relatively coarse grains in inner *** He carrier gas,a homogeneous grain structure consisting of ultra-fine grains in most areas was *** tests showed that N_(2) and He carrier gasses enabled ultra-high yield strengths of 340 and415 MPa,*** values are comparable to severely plastic deformed copper,which has extremely low ductility and shape *** the other hand,both samples showed a strain-softening phenomenon that does not commonly occur at room *** deformation microstructures revealed that dynamic recovery(DRV)and dynamic recrystallization(DRX)phenomena were generated despite being deformed at room *** on the above findings,the overall deformation mechanisms according to the carrier gas species in the CSAM copper manufacturing process were ***,the work hardening and softening behaviors of CSAM Cu are predicted by using a constitutive equation.

关键词： Cold spray additive manufacturing Carrier gas Pure Cu Mechanical properties Deformation behavior

Stabilized sub-grain and nano carbides-driven 1.2 GPa grade ultra-strong CrMnFeCoNi high-entropy alloy additively manufactured by laser powder bed fusion

在线全文

学校读者我要写书评

暂无评论

Journal of Materials Science & Technology 2022年第22期117卷 8-22页

作者： Young-Kyun Kim Kee-ahn lee Department of Materials Science and Engineering Inha UniversityIncheon 22212Republic of Korea Korea Institute of Materials Science(KIMS) Changwon 51508Republic of Korea

High-entropy alloys(HEAs)with interstitial atoms that are produced by additive manufacturing have gained intensive interest in the materials science community because of their suitability for constructing high-strength net-shape ***,a strategy to additionally enhance the strength of selective laser melted carbon-containing HEAs was *** as-built carbon-containing HEAs(C_(x)(Cr_(20)Mn_(20)Fe_(20)Co_(20)Ni_(20))_(100-x)(x=0.5 at.%,1.0 at.%,and 1.5 at.%))contain supersaturated carbon,and the extent of supersaturation increases as the carbon content *** subjected to aging treatment at 650°C for 1 h,the microstructure of the three alloys did not change at the grain ***,the microstructure at the sub-grain scale changed markedly,and these changes influenced the tensile properties and deformation *** particular,the tensile strength of aged 1.5C-HEA at 650°C was∼1.2 GPa at room temperature,which is higher than those reported for CrMnFeCoNi ***,the main deformation mechanism changed from deformation twinning to dislocation-mediated slip,resulting in much higher strain hardening capacity after the aging *** work led to the development of an alternative promising method that involves tailoring the microstructure,to enhance the mechanical properties of additively manufactured metallic materials that contain interstitial atoms.

关键词： Selective laser melting High-entropy alloy Carbon contents Aging Microstructure evolution Tensile property Deformation mechanism

Influence of Processing Parameters on the Mechanical Properties of a Plasma Radical Nitrided SCM440 Steel

在线全文

学校读者我要写书评

暂无评论

Journal of Materials Science & Technology 2008年第3期24卷 356-358页

作者： Seok-Hwan ahn Insup lee School of Mechanical Engineering Pukyong National University Department of Materials and Metallurgical Engineering Dongeui University

Plasma radical nitriding was performed to harden the surface of SCM440 steel for 1-10 h at temperature range of 450-550℃. This process involved the use of NH3 gas instead of N2 gas employed for the well-established plasma nitriding method. No compound layer was formed during this process except the experiment carried out at 500℃ for 10 h. The main phase produced in the diffusion zone was identified to be γ＇-Fe4（N, C）. A diffusion depth increased with increasing treatment temperature and time （up to about 250 μm）. The surface hardness of radical nitrided layer was about two times higher than that of the untreated surface. The tensile test was carried out to estimate the mechanical properties of surface-hardened SCM440 steel prepared at various plasma radical nitriding treatment time and temperature. The influence of radical nitriding treatment on the tensile strength of the specimen was found to be insignificant. The highest value of the ultimate tensile strength was obtained in the experiment carried out at 500℃ for 1 h. However, the elongation was greatly affected by the radical nitriding processing parameters. The maximum value of elongation, which is equal to about 18.1%, was also obtained under the condition of 500℃ for 1 h.

关键词： Plasma radical nitriding Tensile strength Elongation Surface hardness Diffusion depth Compound layer

PGLYRP1 protein as a novel mediator of cellular dialogue in neuroinflammation

在线全文

学校读者我要写书评

暂无评论

Neural Regeneration Research 2025年第7期20卷 1993-1994页

作者： Anup Bhusal Won-Ha lee Kyoungho Suk Department of Pharmacology School of MedicineKyungpook National UniversityDaeguRepublic of Korea BK21 Plus KNU Biomedical Convergence Program Department of Biomedical ScienceSchool of MedicineKyungpook National UniversityDaeguRepublic of Korea School of Life Sciences BK21 plus KNU Creative BioResearch GroupKyungpook National UniversityDaeguRepublic of Korea Brain Science and Engineering Institute Kyungpook National UniversityDaeguRepublic of Korea

Neuroinflammation has been identified as a crucial element in several neurological disorders. Glial cells play a critical role in directing neuroinflammation, both in deleterious and beneficial ways.

关键词： inflammation considerably

Single-cell and spatial omics:exploring hypothalamic heterogeneity

在线全文

学校读者我要写书评

暂无评论

Neural Regeneration Research 2025年第6期20卷 1525-1540页

作者： Muhammad Junaid Eun Jeong lee Su Bin Lim Department of Biochemistry&Molecular Biology Ajou University School of MedicineSuwonSouth Korea Department of Biomedical Sciences Graduate School of Ajou UniversitySuwonSouth Korea Department of Brain Science Ajou University School of MedicineSuwonSouth Korea

Elucidating the complex dynamic cellular organization in the hypothalamus is critical for understanding its role in coordinating fundamental body functions. Over the past decade, single-cell and spatial omics technologies have significantly evolved, overcoming initial technical challenges in capturing and analyzing individual cells. These high-throughput omics technologies now offer a remarkable opportunity to comprehend the complex spatiotemporal patterns of transcriptional diversity and cell-type characteristics across the entire hypothalamus. Current single-cell and single-nucleus RNA sequencing methods comprehensively quantify gene expression by exploring distinct phenotypes across various subregions of the hypothalamus. However, single-cell/single-nucleus RNA sequencing requires isolating the cell/nuclei from the tissue, potentially resulting in the loss of spatial information concerning neuronal networks. Spatial transcriptomics methods, by bypassing the cell dissociation, can elucidate the intricate spatial organization of neural networks through their imaging and sequencing technologies. In this review, we highlight the applicative value of single-cell and spatial transcriptomics in exploring the complex molecular-genetic diversity of hypothalamic cell types, driven by recent high-throughput achievements.

关键词： cellular diversity hypothalamus multi-omics single-cell transcriptomics spatial transcriptomics