Metal-Organic Deposition of Epitaxial La0.7Sr0.3CoO3Thin Films on LaAlO3Substrates

引用

Crystal Structure Theory and Applications 2015年第1期4卷 1-8页

作者： Kais Daoudi zied othmen Saoussen El Helali Meherzi Oueslati Tetsuo Tsuchiya Department of Applied Physics College of Sciences University of Sharjah Sharjah UAE Unité Nanomaté riaux et Photonique Faculty of Sciences of Tunis Tunis El Manar University Tunis Tunisia Laboratoire de Physico-Chimie des Maté riaux Faculty of Science of Monastir University of Monastir Tunis Tunisia National Institute of Advanced Industrial Science and Technology (AIST) Tsukuba Japan

La0.7Sr0.3CoO3 (LSCO) thin films were epitaxially grown on (001)-single crystalline LaAlO3 substrates by metal organic deposition. The evolution of the crystallinity of the films having various thicknesses and obtained at various annealing temperatures is investigated using Raman spectroscopy. The Raman mode associated to the Jahn-Teller distortions in the LSCO films is found to be dependent on the annealing temperature and sensitive to the strain state evolution with film thickness. The microstructure and morphology of the obtained films were investigated using transmission electron microscopy observations on cross-sections and atomic force microscopy. The obtained films are characterized by nanocrystalline morphology, with an average roughness around 5 nm. By increasing the annealing temperature to 1000℃ and the film thickness to 100 nm, the electrical resistivity was decreased by several orders of magnitude. The film resistivity reaches approximately 2.7 × 10–4 Ω•cm in a wide interval of temperature of 77 - 320 K, making this material a promising candidate for a variety of applications.

关键词： La0.7Sr0.3CoO3 Thin Films MOD TEM Raman Spectroscopy Resistivity

来源：

维普期刊数据库评论

在线全文

维普期刊数据库

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：