Micro powder injection molding of boron carbide components with SiC-Al_(2)O_(3)-Y_(2)O_(3)sintering additives

在线全文

同方期刊数据库

学校读者我要写书评

暂无评论

Chinese Journal of Aeronautics 2022年第5期35卷 429-440页

作者： Changrui WANG zhiyou li Wei TIAN Yuxian li lina TANG Qilong PANG Minghe CHEN National Key Laboratory of Science and Technology on Helicopter Transmission Nanjing University of Aeronautics and AstronauticsNanjing 210016China Ji’nan Technician College Jinan 250000China Shanghai Aerospace Equipments Manufacturer Co.Ltd. Shanghai 200245China College of Mechanical and Electrical Engineering Nanjing Forestry UniversityNanjing 210037China

Sintering additives and micro-powder injection molding offer an effective method to densify boron carbide(B_(4)C)and make B_(4)C components with complex shapes.By adjusting the proportion of three kinds of powders(SiC,Al_(2)O_(3)and Y_(2)O_(3)),four kinds of sintering additives were prepared.The feedstock uniformity,debinding behavior,phase composition and microstructure of micro injection molded B_(4)C components with different sintering additives were studied.The results showed that the defects such as lattice distortion and vacancy were introduced into ball milling,which increase the surface energy and benefit subsequent sintering densification.The feedstock had good uniformity and rheology that met the requirements of micro powder injection molding.After debinding,B_(4)C components had enough strength and showed certain sintering characteristics.The addition of sintering additives was beneficial to densification and sintering temperature reduction.The addition of sintering additives formed a second phase in the B_(4)C crystal and at the grain boundary of B_(4)C crystal,which changed the fracture mode from transgranular fracture to mixed fracture mechanism with transgranular fracture.

关键词： Composite materials Fracture Injection molding Microstructure Phase composition

2~6 GHz 100 W高效率平衡式功率放大器的研制

在线全文

学校读者我要写书评

暂无评论

电子科技大学学报 2024年第1期53卷 8-13页

作者：来晋明徐会博李志友倪涛王超杰银军王海龙马晓华西安电子科技大学微电子学院西安710071 中国电子科技集团公司第二十九研究所成都610036 中国电子科技集团公司第十三研究所石家庄050050

为解决传统宽带大功率放大器工作效率低的问题,采用新型电阻电抗连续B/J类功放模式拓展晶体管高效率的输出负载阻抗空间,从而提高宽带功放的漏级输出效率。提出了一款基于0.25μm栅长的氮化镓高电子迁移率晶体管(GaN HEMT)的平衡式功放... 详细信息

为解决传统宽带大功率放大器工作效率低的问题,采用新型电阻电抗连续B/J类功放模式拓展晶体管高效率的输出负载阻抗空间,从而提高宽带功放的漏级输出效率。提出了一款基于0.25μm栅长的氮化镓高电子迁移率晶体管(GaN HEMT)的平衡式功放。该功放将LC匹配网络和切比雪夫阻抗变换器相结合实现GaN HEMT器件宽带输入输出阻抗匹配,并利用3 dB Lange耦合器实现宽带平衡式功率合成。在连续波测试条件下,该平衡式功放在2~6 GHz频带内输出功率大于100 W,漏极效率大于45%,功率增益大于9.0 dB,抗负载失配比优于5:1。

关键词： GaN HEMT 宽带平衡式功率合成功率放大器

在线全文

学校读者我要写书评

暂无评论

黄河特细砂3D打印砂浆的配制

河南大学学报（自然科学版） 2024年第2期54卷 229-235页

作者：贺东青李春萌张国政李志友邓洋洋河南大学土木建筑学院河南开封475004

随着3D打印混凝土在工程中应用的扩大,为缓解天然中粗砂资源短缺,使用黄河特细砂替代部分中粗砂制备3D打印砂浆,设计了3因素(黄河特细砂掺量、水胶比、减水剂)三水平的正交试验,通过测定砂浆的可打印性,确定其配合比,并测定了3D打印砂浆... 详细信息

随着3D打印混凝土在工程中应用的扩大,为缓解天然中粗砂资源短缺,使用黄河特细砂替代部分中粗砂制备3D打印砂浆,设计了3因素(黄河特细砂掺量、水胶比、减水剂)三水平的正交试验,通过测定砂浆的可打印性,确定其配合比,并测定了3D打印砂浆3个方向的抗压强度.结果表明:当黄河特细砂掺量20%、水胶比0.34、减水剂0.12%时满足3D打印砂浆的可打印性,其抗压强度存在着各向异性,沿X轴向(打印方向)最大,7 d抗压强度为22 MPa,且小于同期浇筑试件.

关键词： 3D打印砂浆黄河特细砂可打印性能抗压强度

Effect of WC Addition on The Microstructure and Mechanical Properties of TiN-based Cermets

在线全文

学校读者我要写书评

暂无评论

Effect of WC Addition on The Microstructure and Mechanical P...

Preparation of li-B Alloy and Study of Its Microstructure and Discharge Characteristics

第十八届中国科协年会——分7全国稀有及贵金属材料学术...

作者： Wenmiao ZENG Xueping GAN zhiyou li Kechao ZHOU State Key Laboratory of Powder Metallurgy Central South University

The application of TiN, up to now, is strongly limited to the coating material for various cutting tools and ornaments, while the synthesis of adequate bulk titanium nitride materials would be desirable for several applications to better meet different demands. In this paper, the TiN-WC-Ni-Co system cermets with nearly full density were successfully fabricated by conventional vacuum sintering with the addition of WC and were systematically investigated by scanning electron microscopy, X-ray diffraction and mechanical properties tests. Effect of WC addition on the microstructure and mechanical properties of TiN-based cermets was studied in this work. The results show that WC significantly helps to improve the wettability between TiN and Ni/Co through the formation of typical core-rim structure, which is rather beneficial to obtain the cermets with full densification and homogeneous microstructure. As the addition of WC content increases from 0 wt% to 25 wt%, the microstructure has an obvious trend to become denser and finer and the mechanical properties of the TiN-based cermets are enhanced greatly. When the WC content is 20 wt%, the relative density, transverse rupture strength, fracture toughness and Rockwell hardness of the cermets reach 99.5%, 1235 MPa, 12.6 MPa m and 88.2, respectively.

关键词： Ti N-based cermets WC Mechanical properties Microstructure

来源： cnki会议评论

在线全文

cnki会议

学校读者我要写书评

暂无评论

Journal of Materials Science & Technology 2000年第6期16卷 581-584页

作者： Zhijian liU, zhiyou li, Wei DUAN, Xuanhui QU, Baiyun HUANG and Siqi ZHANG (State Key Laboratory for Powder Metallurgy , Central-South University of Technology, Changsha 410083, China) [Manuscript received November 2, 1999] State Key Lab. for Powder Metall. Central South Univ. of Technol. Changsha 410083 China

A li-B alloy has been prepared using a pretreated amorphous B powder and pure li ingot as starting materials by continually slow addition of B powder and intensified stirring in the process of melting. The microstructure and the discharge characteristic of the materials have been investigated- Results show that the problem of temperature control in synthesis would be modified by means of continual addition of B powder, the li7B6 would be more finely distributed in the metal li by means of intensified stirring. The discharge characteristic of the li-B alloy using amorphous B as starting materials is almost the same with that of using crystalline B.

关键词： li Preparation of li-B Alloy and Study of Its Microstructure and Discharge Characteristics

在线全文

学校读者我要写书评

暂无评论

一体化温补均衡器设计

电子科技大学学报 2022年第3期51卷 397-401页

作者：卢子焱王超杰曾超姚瑞林李志友周丽中国电子科技集团公司第29研究所成都610036 四川省宽带微波电路高密度集成工程研究中心成都610036

提出一种工作在6~18 GHz的温补均衡器的一体化设计方法,该均衡器的核心电路由温度补偿电路、幅度均衡电路及3 dB电桥构成。温度补偿电路与幅度均衡电路采用一体化设计,可以提高在系统中的集成度。同时利用3 dB电桥的隔离特性,改善温补... 详细信息

提出一种工作在6~18 GHz的温补均衡器的一体化设计方法,该均衡器的核心电路由温度补偿电路、幅度均衡电路及3 dB电桥构成。温度补偿电路与幅度均衡电路采用一体化设计,可以提高在系统中的集成度。同时利用3 dB电桥的隔离特性,改善温补均衡器的输入输出驻波。测试结果表明,所加工的温补均衡器在6~18 GHz频段范围内能够实现3~5 dB的幅度均衡量、6 dB的温度补偿。

关键词： 3 dB电桥 90°电桥幅度均衡器温补衰减器

Mo_(2)C增强M2高速钢球磨粉末的致密化及力学性能

在线全文

学校读者我要写书评

暂无评论

粉末冶金材料科学与工程 2022年第2期27卷 161-170页

作者：陈楠龙学湖滕浩李志友中南大学粉末冶金国家重点实验室长沙410083 广州塞隆增材制造有限公司广州510700 南华大学机械工程学院衡阳421001

采用高能球磨对M2高速钢粉末进行破碎,然后添加含量(质量分数,下同)为0~10%的碳化钼(Mo_(2)C)粉末,混合均匀后将混合粉末冷压成形,在真空下烧结得到M2钢与Mo_(2)C增强M2钢,研究烧结样品的致密化行为和力学性能,分析Mo_(2)C对M2钢粉末烧... 详细信息

采用高能球磨对M2高速钢粉末进行破碎,然后添加含量(质量分数,下同)为0~10%的碳化钼(Mo_(2)C)粉末,混合均匀后将混合粉末冷压成形,在真空下烧结得到M2钢与Mo_(2)C增强M2钢,研究烧结样品的致密化行为和力学性能,分析Mo_(2)C对M2钢粉末烧结致密化的影响。结果表明,高能球磨对原料粉末的细化可提高粉体的烧结活性,促进压坯在烧结中期的致密化。通过1180℃固相烧结获得近全致密(相对密度>98%)的M2钢与Mo_(2)C增强M2钢。烧结过程中,Mo_(2)C在950℃基本完全与Fe基体反应转变为M6C相,由此带来的反应烧结与活化烧结促进了烧结中期坯体致密度的提高。烧结中后期形成的大量弥散分布的M_(6)C与M_(2)C碳化物可抑制基体晶粒长大,提高烧结体的硬度和抗弯强度。添加10%Mo_(2)C烧结所得M2钢的抗弯强度达到3135 MPa,硬度(HRC)达到59.6。通过原料粉末细化、Mo_(2)C的反应扩散以及金属颗粒的氧化还原反应能有效提高M2高速钢的烧结性能和力学性能,有望为其他难烧结高速钢的制备提供技术参考。

关键词：高速钢高能球磨显微组织碳化物烧结性能

生物有机肥对蓝莓根区土壤养分及微生物学特性的影响

在线全文

学校读者我要写书评

暂无评论

水土保持研究 2017年第2期24卷 36-42页

作者：李志友安顺学院农学院贵州安顺561000

以蓝莓为试材,研究了生物有机肥对蓝莓根区土壤养分及微生物学特性的影响。结果表明:(1)生物有机肥(BOF)显著增加了蓝莓根区土壤含水量(p0.05);(3)BOF处理下蓝莓根区土壤酸性磷酸酶活性、脲酶活性、蔗糖酶活性和过氧化氢酶活性均显著高... 详细信息

以蓝莓为试材,研究了生物有机肥对蓝莓根区土壤养分及微生物学特性的影响。结果表明:(1)生物有机肥(BOF)显著增加了蓝莓根区土壤含水量(p0.05);(3)BOF处理下蓝莓根区土壤酸性磷酸酶活性、脲酶活性、蔗糖酶活性和过氧化氢酶活性均显著高于CK(p<0.01);(4)BOF处理下蓝莓根区土壤微生物量碳(MBC)、微生物量氮(MBN)含量均显著高于CK(p<0.01),土壤微生物量碳和氮较养分的变化更为敏感,能有效评价生物有机肥的改良效果;(5)BOF处理下蓝莓根区土壤微生物周转速率加快,周期缩短,转移量增加,土壤微生物活性增强,有利于土壤养分的循环和保持。综合比较来看,生物有机肥可有效促进蓝莓根区土壤养分的吸收和营养代谢协调均衡,确保蓝莓的高产优质。

关键词：生物有机肥蓝莓土壤养分土壤微生物学特性

热处理对挤压铸造n-SiC_p/AZ91D镁基复合材料组织和力学性能的影响

在线全文

学校读者我要写书评

暂无评论

稀有金属材料与工程 2015年第6期44卷 463-468页

作者：张从阳冯荣宇李文珍清华大学北京100084

采用金相、X射线衍射、扫描电镜(SEM)、拉伸试验等方法分析和测试了挤压铸造纳米Si C颗粒增强AZ91D镁基复合材料在铸态(F)、固溶态(T4)和人工时效态(T6)下的组织和力学性能。结果表明,固溶处理可使n-Si Cp/AZ91D铸态组织中的β-Mg17Al1... 详细信息

采用金相、X射线衍射、扫描电镜(SEM)、拉伸试验等方法分析和测试了挤压铸造纳米Si C颗粒增强AZ91D镁基复合材料在铸态(F)、固溶态(T4)和人工时效态(T6)下的组织和力学性能。结果表明,固溶处理可使n-Si Cp/AZ91D铸态组织中的β-Mg17Al12共晶相溶入到基体中,形成单一的过饱和α-Mg固溶体,合金抗拉强度和伸长率均有大幅提高,分别达到265 MPa和13.7%;经时效处理后,复合材料的抗拉强度和屈服强度进一步提高,分别为275,145 MPa;SEM结果显示,β-Mg17Al12相主要以连续析出/非连续析出方式分别在晶内及晶界上析出,特别是纳米Si C颗粒分布对二次析出相β-Mg17Al12的形貌、尺寸、分布有一定的影响,使二次析出相变得细小和弥散分布,从而充分发挥了二次析出相的沉淀强化作用;最后对n-Si Cp/AZ91D复合材料不同热处理条件下的断口形貌进行了SEM观察,并且对其断裂方式进行了分析和讨论。

关键词：镁基纳米复合材料挤压铸造热处理微观组织力学性能