Effects of the two-step ageing treatment on the microstructure and properties of 7B04 alloy pre-stretched thick plates

在线全文

学校读者我要写书评

暂无评论

Rare Metals 2007年第3期26卷 193-199页

作者： li zhihui xiong baiqing zhang yong ＇an ZHU Baohong wang feng liU Hongwei State Key Laboratory for Fabrication and Processing of Nonferrous Metals General Research Institute for Nonferrous Metals Beijing 100088 China

The effects of the two-step ageing parameters （temperature and time） on the mechanical properties and electrical conductivity of 7B04 （A1-Zn-Mg-Cu） pre-stretched thick plates were studied. The results reveal that the initial T1 ageing contributes a major increase of the tensile strength, and the 0.2% proof stress value reaches 482 MPa after ageing for 7 h at 115℃. Behavioral differences in the tensile properties of the alloy after the two-step ageing treatment were less with the first-step ageing at 115~C for different time periods （7, 14, and 21 h）. The effects of the second ageing parameters on the properties and microstructure of the 7B04 alloy were remarkable. TEM analysis of the samples aged at Temper I （7 h at 115℃ ＋ 12 h at 160℃） and Temper II （7 h at 115℃ ＋ 16 h at 165℃） indicates that two kinds of phases, i.e. 11＇ and 11 phases, precipitate from the matrix and efficiently improve the tensile strength of the alloy, and the grain boundary precipitates are coarse and discrete. There are obvious precipitate free zones （PFZs） along the grain boundary in the microstructure of the alloy after the two-step ageing treatment.

关键词： 7B04 alloy two-step ageing mechanical properties electrical conductivity microstructure

Ageing behavior of an Al-Zn-Mg-Cu alloy pre-stretched thick plate

在线全文

学校读者我要写书评

暂无评论

Journal of University of Science and Technology Beijing 2007年第3期14卷 246-250页

作者： zhihui li baiqing xiong yongan zhang Baohong Zhu feng wang Hongwei liu State Key Laboratory for Fabrication and Processing of Non-ferrous Metals General Research Institute for Non-ferrous Metals Beijing 100088 China

The ageing behavior of a pre-stretched thick plate of Al-Zn-Mg-Cu alloy was systemically studied including one-step ageing, two-step ageing, and retrogression and reageing treatment （RRA）. One-step ageing of the alloy resulted in peak ultimate tensile strengths of 595 and 575 MPa after 22 and 6 h at 120 and 135°C, respectively. The strengthening phase in peak aged （T6 temper） alloy contained GP zones and the η′ phase predominantly. After two-step ageing, the electrical conductivity was increased markedly, but the pre-stretched thick plate sacrificed a great loss of strength. RRA treatment provided a method for maintaining the strength close to that obtained by T6 temper and for obtaining the high electrical conductivity close to that obtained by T7 temper; the ultimate tensile strength and electrical conductivity were 583 MPa and 21.0 MS/m, respectively. TEM analysis of T7 and RRA specimens revealed two types of precipitates that contributed to age strengthening i.e. the η′ and η phases.

关键词： Al-Zn-Mg-Cu alloy pre-stretched thick plate ageing tensile properties precipitation

Effect of Zn addition on microstructure and mechanical properties of an Al–Mg–Si alloy

在线全文

学校读者我要写书评

暂无评论

Progress in Natural Science:Materials International 2014年第2期24卷 97-100页

作者： lizhen Yan yongan zhang Xiwu li zhihui li feng wang Hongwei liu baiqing xiong State Key Laboratory of Nonferrous Metals and Processes General Research Institute for Nonferrous Metals

In the present work, an Al–0.66Mg–0.85Si–0.2Cu alloy with Zn addition was investigated by electron back scattering diffraction(EBSD), high resolution electron microscopy(HREM), tensile and Erichsen tests. The mechanical properties of the alloy after pre-aging met the standards of sheet forming. After paint baking, the yield strength of the alloy was improved apparently. GP(Ⅱ) zones and η'phases were formed during aging process due to Zn addition. With the precipitation of GP zones, β″ phases, GP(Ⅱ) zones and η'phases, the alloys displayed excellent mechanical properties.

关键词： Al–Mg–Si alloy Paint baking response Skin panels

The Microstructural Evolution of AA6111 Aluminum Alloy during Homogenization Treatment

在线全文

同方期刊数据库

学校读者我要写书评

暂无评论

The Microstructural Evolution of AA6111 Aluminum Alloy durin...

多级断续时效对Al-Cu-Mg-Ag-Zr合金组织和性能的影响

中国材料大会2012

作者： Shijiao zhang baiqing xiong yongan zhang Xiwu li feng wang zhihui li Hongwei liu State Key Laboratory of Nonferrous Metals and Processes General Research Institute for Nonferrous Metals

ISBN: (纸本)9783037856093

The microstructures of AA6111 automotive aluminum alloy were investigated by optical microscopy（OM）,scanning electron microscopy with energy dispersive X-ray spectroscopy（SEM-EDX）,differential scanning calorimetry（DSC）,X-ray diffraction analysis（XRD） and transmission electron microscope（TEM）.The results indicated that as-cast AA6111 alloy has a complex *** were many kinds of intermetallic phases,such as lath-shaped β-Al5FeSi,Al15（FeMn）3Si2 and Mg2Si on the grain *** Al5Cu2Mg8Si6 precipitates presented non-equilibrium eutectic morphology in the grain *** homogenization treatment（6h at 470℃）,the low melting point Mg2Si phase began *** eutectic Al5Cu2Mg8Si6 phase were dissolved completely after 530℃/24h homogenization *** Al15（FeMn）3Si2 phase started to be spheroidized at 560℃.Increasing treatment temperature will promote Mn to substitute for Fe in this phase.

关键词： 6111 aluminum alloy Microstructure Homogenization treatment.

来源： cnki会议评论

在线全文

cnki会议

学校读者我要写书评

暂无评论

稀有金属 2011年第2期35卷 170-175页

作者：张建波张永安朱宝宏王锋李志辉熊柏青北京有色金属研究总院有色金属制备加工国家重点实验室北京100088

采用硬度测试、透射电镜(TEM)和差示扫描量热分析(DSC)等方法,研究了多级断续时效对高Cu/Mg比Al-Cu-Mg-Ag-Zr合金组织和性能的影响。结果表明,断续时效第二级低温时效对合金硬度无明显影响,第三级高温时效对硬度影响较大,随着时间的延长... 详细信息

采用硬度测试、透射电镜(TEM)和差示扫描量热分析(DSC)等方法,研究了多级断续时效对高Cu/Mg比Al-Cu-Mg-Ag-Zr合金组织和性能的影响。结果表明,断续时效第二级低温时效对合金硬度无明显影响,第三级高温时效对硬度影响较大,随着时间的延长,硬度先增大且在160℃时效20 h左右达到最大值后减小。透射电镜和DSC证明在断续时效的不同阶段,合金的沉淀析出特征:在第一阶段高温时效中,Ω相和θ'相同时析出,两种析出相的数量无明显差别;在第二阶段低温时效中,θ'相持续析出,无明显的Ω相析出特征;在第三阶段高温再时效中,Ω相和θ'相同时析出长大,Ω相为主要强化相,θ'相相对较少。

关键词：断续时效 TEM Al-Cu-Mg-Ag DSC

热处理对7B04铝合金厚板组织与力学性能的影响

在线全文

学校读者我要写书评

暂无评论

特种铸造及有色合金 2007年第6期27卷 427-430页

作者：李志辉熊柏青张永安朱宝宏王锋刘红伟北京有色金属研究总院有色金属材料制备加工国家重点实验室

通过显微组织观察和力学性能与电导率测试,研究了热处理工艺对7B04铝合金厚板组织与性能的影响。结果表明,适宜的固溶工艺为470℃×240min。120℃×22h时效后合金可获得,抗拉强度为621MPa,但合金的电导率较低,仅为18·3MS/m;双级T74时效... 详细信息

通过显微组织观察和力学性能与电导率测试,研究了热处理工艺对7B04铝合金厚板组织与性能的影响。结果表明,适宜的固溶工艺为470℃×240min。120℃×22h时效后合金可获得,抗拉强度为621MPa,但合金的电导率较低,仅为18·3MS/m;双级T74时效时,强度下降了10%～12%(与T6态相比),电导率获得了明显提高,为21·3MS/m;三级时效(RRA)处理可使合金获得高强度和高电导率相结合,强度接近T6态,电导率与T74态相当。合金经RRA处理后,基体内分布着大量的细小弥散析出相(与T6态组织相似),晶界析出相粗大且呈完全不连续分布。

关键词： 7B04铝合金固溶时效组织力学性能

喷射成形7XXX铝合金孔隙分布规律及其演变(英文)

在线全文

学校读者我要写书评

暂无评论

稀有金属材料与工程 2014年第12期43卷 2974-2979页

作者：尹贻彬张永安熊柏青王锋刘红伟李志辉李锡武北京有色金属研究总院有色金属材料制备加工国家重点实验室北京100088 聊城大学山东聊城252059

利用喷射成形技术制备了Al-10.8Zn-2.8Mg-1.9Cu-0.16Zr合金,通过金相显微镜和场发射扫描电镜研究了喷射成形合金的微观组织,总结了沉积坯中孔隙的形貌特点,分析了合金中孔隙的形成机制,并对热等静压和均匀化热处理对沉积坯缺陷的影响进... 详细信息

利用喷射成形技术制备了Al-10.8Zn-2.8Mg-1.9Cu-0.16Zr合金,通过金相显微镜和场发射扫描电镜研究了喷射成形合金的微观组织,总结了沉积坯中孔隙的形貌特点,分析了合金中孔隙的形成机制,并对热等静压和均匀化热处理对沉积坯缺陷的影响进行了研究。结果表明,沉积坯中的孔隙主要有搭接型孔隙、连通型孔隙和气孔,缺陷种类及分布与沉积坯位置有一定的关系,沉积坯芯部缺陷主要为搭接型孔隙和气孔,沉积坯边部连通型孔隙较多,尺寸较大。气孔内壁平滑内凹,形貌类似球形,其余孔隙为不规则形貌。热等静压处理可以消除气孔以外的其他孔隙,热处理后沉积坯中的气孔重新出现。

关键词：喷射成形 7XXX铝合金孔隙缺陷

在线全文

学校读者我要写书评

暂无评论

7B04铝合金双级时效的微观组织与性能

稀有金属材料与工程 2008年第3期37卷 521-524页

作者：李志辉熊柏青张永安朱宝宏王锋刘红伟北京有色金属研究总院北京100088

研究了双级时效处理对7B04铝合金预拉伸厚板的组织和性能的影响。采用TEM对时效组织变化进行了分析,并对力学性能和电导率进行了测试。结果表明:采用双级时效处理实现了晶内和晶界析出相的长大和粗化过程;随着第二级时效温度的升高,合... 详细信息

研究了双级时效处理对7B04铝合金预拉伸厚板的组织和性能的影响。采用TEM对时效组织变化进行了分析,并对力学性能和电导率进行了测试。结果表明:采用双级时效处理实现了晶内和晶界析出相的长大和粗化过程;随着第二级时效温度的升高,合金的强度随之下降,电导率升高。采用第二级160℃时效时,时效时间在12～24h之间合金的强度与T651制度(峰时效的抗拉强度为595MPa)相比下降了10%～13%左右,而合金的电导率可达21.3～22.3MS/m之间,伸长率保持在10%～11%左右。

关键词： 7B04铝合金预拉伸厚板双级时效电导率微观组织

在线全文

学校读者我要写书评

暂无评论

快速凝固硅铝合金材料的组织与性能

稀有金属材料与工程 2010年第9期39卷 1659-1663页

作者：李志辉张永安熊柏青朱宝宏刘红伟王锋魏衍广张济山北京有色金属研究总院北京100088 北京科技大学北京100083

针对电子信息工业对新型结构功能一体化电子封装材料的应用需求,采用喷射成形与热压致密化相结合的方法制备高Si含量(质量分数为50%～70%Si)的系列Si-Al合金,并利用金相显微镜、扫描电镜、硬度测试仪、热膨胀仪等手段研究该材料的显微... 详细信息

针对电子信息工业对新型结构功能一体化电子封装材料的应用需求,采用喷射成形与热压致密化相结合的方法制备高Si含量(质量分数为50%～70%Si)的系列Si-Al合金,并利用金相显微镜、扫描电镜、硬度测试仪、热膨胀仪等手段研究该材料的显微组织、力学性能和热物理性能。结果表明,喷射成形高硅铝合金的沉积态显微组织细小弥散,初生硅呈不规则形状,均匀弥散地分布在铝基体中;对沉积坯件进行适当的热压致密化处理可以有效地消减喷射成形制坯工艺过程中所形成的疏松和孔洞,提高材料的致密度。经热压致密化处理的喷射成形高硅铝合金材料具有优越的热物理性能以及良好的力学性能,是一种综合性能优越的结构功能一体化电子封装材料。

关键词：快速凝固铝合金材料组织与性能 Materials Rapidly Solidified 喷射成形热压致密化电子封装材料致密化处理热物理性能高硅铝合金显微组织力学性能结构功能一体化硬度测试仪金相显微镜不规则形状 Si-Al合金组织细小