Dependence of microstructural, mechanical and electrical properties on growth rates in directional solidified Zn-Al-Bi eutectic alloy

引用

Transactions of Nonferrous Metals Society of China 2016年第9期26卷 2320-2335页

作者： yasin karamazi Umit BAYRAM Pinar ATA Sezen AKSOZ Kazim KESLIOGLU Necmettin MARASLI Department of Physics Institute of Science and TechnologyErciyes UniversityKayseri 38039Turkey Department of Physics Faculty of ScienceErciyes UniversityKayseri 38039Turkey Department of Physics Institute of Science and TechnologyNevsehir Hacl Bektas Veli UniversityNevsehir 50300Turkey Department of Physics Faculty of Arts and SciencesNevsehir Haci Bektas Veli UniversityNevsehir 50300Turkey Department of Metallurgical and Materials Engineering Faculty of Chemistry and Metallurgical EngineeringYildiz Technical UniversityDavutpasa-EsenlerIstanbul 34220Turkey

Zn-5%Al-0.2%Bi（mass fraction） alloy was directionally solidified upward at a constant temperature gradient with a wide range of growth rates using a Bridgman-type directional solidification furnace. The eutectic spacings, microhardness, ultimate tensile strength and electrical resistivity for directionally solidified Zn-Al-Bi alloy were measured. Dependence of eutectic spacings, microhardness, ultimate tensile strength and electrical resistivity on growth rates was obtained by linear regression analysis. The results obtained in the present work for low growth rates（smaller than 450.0 μm/s） are in good agreement with experimental results obtained in previous work for directional solidified Zn-Al eutectic alloy with a similar growth rate but differs from the Jackson-Hunt eutectic theory and those obtained in previous experimental works at higher growth rates. The critical growth rate might be 450.0 μm/s for the Zn-Al-Bi eutectic alloy. From the plot of heat flow versus temperature, enthalpy of fusion, specific heat difference between liquid and solid phases and melting temperature for the Zn-Al-Bi alloy are found to be 112.55 J/g, 0.291 J/（g·K） and 660.20 K, respectively.

关键词： directional solidification zinc-aluminum alloy microstructure microhardness tensile strength electrical properties

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：