Journal of Harbin Institute of Technology(New Series) 2015年第2期22卷 118-122页

作者： xingdong yuan Bin Xu Yucheng Cai School of Materials Science and Engineering Shandong University School of Materials Science and Engineering Shandong Jianzhu University

In this paper, fast multiple rotation rolling （FMRR） is applied to fabricate a nanostructured layer on the surface of steel 45. The FMRR samples are then Cr-Rare earth-boronized under low-temperature. The boride layer is characterized by using Scanning electron microscopy （SEM） and X-ray diffraction （XRD）. Experimental results indicate that the thickness of the boride layer is greatly increased by surface nanocrystallization. The boride layer with relatively continuous structure instead of the zigzag teeth structure is obtained, and the penetrating rate is enhanced by 2. 5-3.7 times when the FMRR samples are Cr-Rare earth- boronized at the temperature of 570 %, 600℃ and 650℃ for 6 h. The boride layer fabricated on the FMRR sample consists of single phase Fe2B. Severe plastic deformation with the grain size of approximately 100 nm in the top surface layer of steel 45 is observed, and the thickness of the plastic deformation layer is about 30 6xm. The microstructure in the top surface layer is characterized by Transmission electron microscopy （TEM）. Grain boundaries are largely increased with high stacking fault energy after FMRR, leading to a significant enhancement of RE boron-chromizing speed.

关键词： surface nanocrystallization fast multiple rotation roiling Cr-Rare earth-boronizing low temperature boride layer

Surface Nanocrystallization of Steel 20 Induced by Fast Multiple Rotation Rolling

在线全文

学校读者我要写书评

暂无评论

Journal of Harbin Institute of Technology(New Series) 2015年第5期22卷 38-41页

作者： xingdong yuan Bin Xu Yucheng Cai School of Materials Science and Engineering Shandong University School of Materials Science and Engineering Shandong Jianzhu University

In order to expand the application of steel 20 in precision device,fast multiple rotation rolling( FMRR) is applied to fabricate a nanostructured layer on the surface of steel 20. The FMRR samples are then Cr-Rare earth-boronized under low-temperature. The microstructure of the top surface layer is characterized by transmission electron microscopy( TEM). Microhardness of the top surface is measured by a Vickers microhardness tester. The boride layer is characterized by using scanning electron microscopy( SEM).Experimental results show that a nanostructured layer with their grain size range from 200 to 400 nm is obtained in the top surface layer. The microhardness of FMRR sample changes gradiently along the depth from about274 HV in the top surface layer to about 159 HV in the matrix,which is nearly 1.7 times harder than that of the original sample. The penetrating rate is enhanced significantly when the FMRR samples are Cr-Rare earthboronized at 600 ℃ for 6 h. Thickness of the boride layer increases to around 20 μm,which is nearly twice thicker than that of the original sample.

关键词： fast multiple rotation rolling steel 20 surface nanocrystallization dislocation Cr-Rare earth-boronizing

Effect of Surface Nanocrystallization on Cr-Rare Earth-Boriding for Steel Q235 at Low-Temperature

在线全文

学校读者我要写书评

暂无评论

Journal of Harbin Institute of Technology(New Series) 2018年第1期25卷 79-84页

作者： xingdong yuan Xiaojie Yang Feng Tian Bin Xu School of Materials Science and Engineering Shandong Jianzhu University Jinan 250101 China Shandong Institute for Product Quality Inspection Jinan 250100 China Shandong Quality and Technical Examination Assess Center Jinan 250014China

A nanostructured layer was fabricated on the surface of steel Q235 by using fast multiple rotation rolling( FMRR). The Cr-Rare earth-boriding process was carried out followed at different *** results showed that the thickness of the boride layer was significantly increased by surface nanocrystallization. The morphology of the boride layer was saw-toothed. An uniform,continuous and dense boride layer was obtained and adhered well to the substrate. The penetrating speed of FMRR specimens was enhanced by 1.9,1.7 and 1.5 times when the Cr-Rare earth-boriding temperature was 843,873 and 923 *** plastic deformation,which grain size was approximately 100 nm,was observed on steel Q235 *** of Cr-Rare earth-boriding was also studied.

关键词： nanostructure low temperature steel Q235 boride layer

日间腹腔镜子宫肌瘤剔除手术中腹横肌平面阻滞复合全身麻醉的作用观察

在线全文

学校读者我要写书评

暂无评论

实用妇科内分泌电子杂志 2023年第13期10卷 28-30页

作者：袁星东盐城市大丰区第三人民医院麻醉科江苏大丰224100

目的探究日间腹腔镜子宫肌瘤剔除手术中腹横肌平面阻滞复合全身麻醉的作用。方法选取60例行日间腹腔镜子宫肌瘤剔除手术治疗的患者,采用随机数字表法分为研究组与对照组,各30例。对照组患者给予全身麻醉,研究组在对照组基础上进行腹横... 详细信息

目的探究日间腹腔镜子宫肌瘤剔除手术中腹横肌平面阻滞复合全身麻醉的作用。方法选取60例行日间腹腔镜子宫肌瘤剔除手术治疗的患者,采用随机数字表法分为研究组与对照组,各30例。对照组患者给予全身麻醉,研究组在对照组基础上进行腹横肌平面阻滞麻醉。比较两组临床疗效。结果研究组患者丙泊酚及瑞芬太尼剂量少于对照组,且术后1h视觉模拟评分法(VAS)评分低于对照组(P0.05);气腹时及术闭后,研究组患者HR、MAP指标低于对照组(P<0.05)。研究组患者自主呼吸恢复时间、拔管时间、麻醉唤醒时间均短于对照组(P<0.05)。研究组患者并发症发生率为3.33%,低于对照组的23.33%(P<0.05)。结论日间腹腔镜子宫肌瘤剔除手术过程中使用腹横肌平面阻滞复合全身麻醉效果较好,安全性较高,值得推广。

关键词：腹腔镜子宫肌瘤剔除术腹横肌平面阻滞全身麻醉日间手术

磷钨酸改性介孔分子筛SBA-15催化剂的酸性及水热稳定性的研究

在线全文

学校读者我要写书评

暂无评论

石油化工 2005年第3期34卷 222-225页

作者：杨丽娜亓玉台袁兴东沈健杨晓勇哈尔滨工业大学应用化学系黑龙江哈尔滨150001 辽宁石油化工大学石油化工学院辽宁抚顺113001

采用直接合成法和后合成法制备磷钨酸改性介孔分子筛SBA-15催化剂,通过Hammett指示剂法对两种合成方法得到的催化剂的酸性进行了比较,在索氏抽提器中采用质量分数95%的乙醇对催化剂进行水热处理,通过测定催化剂总酸量的变化和分子筛结... 详细信息

采用直接合成法和后合成法制备磷钨酸改性介孔分子筛SBA-15催化剂,通过Hammett指示剂法对两种合成方法得到的催化剂的酸性进行了比较,在索氏抽提器中采用质量分数95%的乙醇对催化剂进行水热处理,通过测定催化剂总酸量的变化和分子筛结构的变化比较两者的水热稳定性。以丙烯酸和正丁醇的酯化反应为探针反应,考察两种催化剂的重复使用性。实验结果表明,用直接合成法制备的磷钨酸改性介孔分子筛SBA-15催化剂比后合成法制备的催化剂总酸量低、酸强度相近、水热稳定性好、重复使用效果好,用直接合成法制备的催化剂在磷钨酸质量分数为30%时的酸量最高。

关键词：磷钨酸介孔分子筛水热稳定性直接合成法后合成法酸催化

在线全文

学校读者我要写书评

暂无评论

45钢低温硼-铬-稀土共渗研究

热加工工艺 2012年第8期41卷 209-211页

作者：王豪许斌袁兴栋李森山东建筑大学材料科学与工程学院山东济南250101

为提高低温硼-铬-稀土共渗渗速,经多次共渗试验,筛选出以硼铁为供硼剂,氟硼酸钾为主要活化剂,效果最佳的低温共渗剂配方。结果表明:利用此共渗剂对45钢进行650℃×6h的低温共渗处理,可获得深约22μm的共渗层,共渗层呈梳齿状,具有较高的... 详细信息

为提高低温硼-铬-稀土共渗渗速,经多次共渗试验,筛选出以硼铁为供硼剂,氟硼酸钾为主要活化剂,效果最佳的低温共渗剂配方。结果表明:利用此共渗剂对45钢进行650℃×6h的低温共渗处理,可获得深约22μm的共渗层,共渗层呈梳齿状,具有较高的硬度及较好的耐磨粒磨损性能。

关键词：低温硼-铬-稀土共渗深度硬度耐磨粒磨损性能

甲醇与异丁烯在改性β分子筛上的吸附行为研究

在线全文

学校读者我要写书评

暂无评论

离子交换与吸附 2001年第3期17卷 209-216页

作者：袁兴东李国辉周敬来中国科学院山西煤炭化学研究所!太原 030001 抚顺石油学院石油化工系!抚顺 113001

采用过渡应答技术对甲醇和异丁烯在改性(分子筛上的吸附行为进行了研究。研究结果表明：异丁烯和甲醇在改性(分子筛上符合先快吸附后慢吸附的Elovich吸附规律。甲醇的吸附量大，但速率慢；异丁烯吸附量小，速率快。由于甲醇的饱和吸... 详细信息

采用过渡应答技术对甲醇和异丁烯在改性(分子筛上的吸附行为进行了研究。研究结果表明：异丁烯和甲醇在改性(分子筛上符合先快吸附后慢吸附的Elovich吸附规律。甲醇的吸附量大，但速率慢；异丁烯吸附量小，速率快。由于甲醇的饱和吸附量大于异丁烯的饱和吸附量，对合成MTBE反应的选择性具有重要意义。对它们的吸附行为进行动力学研究，得到不同温度下吸附活化能随吸附量变化的关系。不同温度下相对饱和吸附量预测表明：当温度从288K升高到383K时，qMeOH/qIB从6.1降低到4.6，甲醇的相对饱和吸附量随温度升高而减小，但仍保持较高值，证明了甲醇在分子筛上是强吸附的观点，为解释选择性高和动力学方程的建立提供依据，对反应机理的研究有指导作用。

关键词：分子筛吸附甲醇异丁烯动力学

Ti_3(PW_(12)O_(40))_4催化氧化吸附脱硫的研究

在线全文

同方期刊数据库

学校读者我要写书评

暂无评论

石油炼制与化工 2005年第3期36卷 20-24页

作者：张艳维沈健袁兴东亓玉台辽宁石油化工大学石油化工学院抚顺113001

用溶胶凝胶法制备了Ti3(PW12O40)4/SiO2Al2O3催化氧化吸附剂,用于二苯并噻吩的氧化吸附脱除实验,考察了吸附剂中钛含量、反应温度、吸附剂用量、双氧水用量及反应时间对脱硫效果的影响。结果表明,在最佳的实验条件(n(Ti)/n(H)为3、吸附... 详细信息

用溶胶凝胶法制备了Ti3(PW12O40)4/SiO2Al2O3催化氧化吸附剂,用于二苯并噻吩的氧化吸附脱除实验,考察了吸附剂中钛含量、反应温度、吸附剂用量、双氧水用量及反应时间对脱硫效果的影响。结果表明,在最佳的实验条件(n(Ti)/n(H)为3、吸附剂用量为5%、n(H2O2)/n(S)为3、反应温度为70℃)下反应2h,该吸附剂可将二苯并噻吩的石油醚溶液中的硫质量分数由200μg/g降至2μg/g,脱硫率达99%,且具有较好的再生性能。

关键词：吸附剂反应温度催化氧化溶胶一凝胶法反应时间石油醚 Al2O3 吸附脱硫二苯并噻吩脱硫效果

在线全文

学校读者我要写书评

暂无评论

表面纳米化对45钢硼铬稀土低温共渗的影响

热加工工艺 2014年第10期43卷 170-172页

作者：蔡玉成许斌袁兴栋温振兴山东建筑大学材料科学与工程学院山东济南250101

采用快速多重旋转技术（FMRR）对45钢进行表面纳米化处理，然后对其进行650-Cx6h的硼铬稀土低温共渗，并利用TEM、SEM、电子显微硬度计进行表征。结果表明：快速多重旋转技术处理后的45钢表面发生了剧烈塑性变形，产生了纳米级晶粒，变... 详细信息

采用快速多重旋转技术（FMRR）对45钢进行表面纳米化处理，然后对其进行650-Cx6h的硼铬稀土低温共渗，并利用TEM、SEM、电子显微硬度计进行表征。结果表明：快速多重旋转技术处理后的45钢表面发生了剧烈塑性变形，产生了纳米级晶粒，变形层厚度约30μm，硬度比基体提高40％；处理后的45钢表面硼铬稀土低温共渗层无明显的梳齿状、较为连续，平均厚度27μm，其硬度为1200-1700HV，共渗层主要由单相Fe2B组成。

关键词：快速多重旋转碾压表面纳米化硼-铬-稀土共渗硬度

介孔分子筛SiW_(12)/SBA-15的制备及性能研究

在线全文

学校读者我要写书评

暂无评论

精细石油化工 2009年第1期26卷 25-28页

作者：武宝萍许前会袁兴东赵跃强淮海工学院化工系江苏连云港222005 辽宁石油化工大学石油化工学院辽宁抚顺113001

采用后合成法制备了SiW_(12)/SBA-15催化剂,并用X射线衍射、N_2吸附脱咐法、热失重法分析催化剂的物理性能。结果表明,SiW_(12)/SBA-15仍保持了介孔分子筛SBA-15的晶体结构,比表面积和孔径分别为589 m^2/g和6.1 nm,且SiW_(12)/SBA-15催... 详细信息

采用后合成法制备了SiW_(12)/SBA-15催化剂,并用X射线衍射、N_2吸附脱咐法、热失重法分析催化剂的物理性能。结果表明,SiW_(12)/SBA-15仍保持了介孔分子筛SBA-15的晶体结构,比表面积和孔径分别为589 m^2/g和6.1 nm,且SiW_(12)/SBA-15催化剂在400～450℃温度区失去结晶水,在650～700℃范围内SiW_(12)的Keggin结构破坏。选用月桂酸和乙醇的酯化反应考察SiW_(12)/SBA-15的催化活性和再生性能。SiW_(12)/SBA-15具有良好的催化活性和再生性能,得到最佳的酯化反应条件为:反应温度90℃、催化剂质量分数1%、酸醇摩尔比1:2.5、反应时间5 h。

关键词：介孔分子筛酯化反应月桂酸 SiW12/SBA-15