A comparative investigation on wear behaviors of physical and chemical vapor deposited bronze coatings for hydraulic piston pump

在线全文

学校读者我要写书评

暂无评论

Chinese Journal of Aeronautics 2024年第3期37卷 391-403页

作者： Wei HAO Andrews LARBI Hongkang DONG Dongyun wang Shenghu li zhejiang Provincial Key Laboratory of Urban Rail Transit Intelligent Operation and Maintenance technology and Equipment Zhejiang Normal UniversityJinhua 321004China college of engineering Zhejiang Normal UniversityJinhua 321004China hangzhou lilong Hydraulic Co. LtdHangzhou 311200China

The cylinder block/valve plate interface is one of the most critical frictional interfaces of the swashplate-type axial piston ***,the poor lubrication interface caused rapid wear and high friction loss in an elastohydrodynamic lubrication system,decreasing the pump *** resistant bronze coatings were fabricated on 3.CrMoAl substrate by Physical Vapor Deposition(PVD)and Chemical Vapor Deposition(CVD),***-on-disc wear tests were performed to comparatively investigate the wear behaviors of the coatings and bulk ductile iron *** can be found that the PVD-bronze coating exhibited better wear resistance than the other two *** enhanced wear resistance was attributed to the unique composite microstructure and desired mechanical strength,which could resist to mechanical shear and spallation,decreasing friction *** appropriate hardness of(1.3.±0.07)GPa could be beneficial for enhancing its wear *** PVD-bronze coating possessed a much lower and stable coefficient of friction(about 0.1)and wear rate(about 6000μm3.N-1.m-1)under the loading forces of about 100 N after 20 *** wear mechanism was the abrasive wear.

关键词： Aircraft hydraulic pump Bronze Coatings Wear resistance Mechanisms

Convenient room-temperature synthesis of sulfur and nitrogen co-doped NiCo-LDH coupled with CNTs on NiCo foam as battery-type electrode for high performance hybrid supercapacitor

在线全文

学校读者我要写书评

暂无评论

Rare Metals 2024年第9期43卷 4286-4301页

作者： li Song Xiao-Hong Zhong Fang-lin wang Zhi-Hui Huang Zhe Hong Yun-Fang Gao Hai-Dong wang Jian-Wei Ren Sheng-Jie Peng Lei li college of Biological Chemical Sciences and EngineeringJiaxing UniversityJiaxing 314001China college of Chemical engineering Zhejiang University of TechnologyHangzhou 310014China college of Materials Science and technology Nanjing University of Aeronautics and AstronauticsNanjing 210016China Research and Development Department Jiangxi Ganfeng LiEnergy Technology Co.Ltd.Xinyu 338000China Department of mechanical engineering Science University of JohannesburgAuckland ParkJohannesburg 2092South Africa

The convenient synthesis of the composite electrode with high supercapacitance performance plays an important role in practical application but is ***,the carbon nanotubes(CNTs)coupled with lowcrystalline sulfur and nitrogen co-doped Ni Co-LDH(denoted as SN-Ni Co-LDH)nanosheets array are grown on Ni Co foam(NCF)substrate by two convenient steps of metal induced self-assembly and corrosion engineering,which present the advantages of operating at roomtemperature and low preparation *** from the S–N co-doping and low-crystallinity of Ni Co-LDH,the prepared SN-Ni Co-LDH@CNTs@NCF electrode presents a topping charge capacity of 2470 C·g^(-1)(4.94 C·cm^(-2))at 5 m A·cm^(-2).Furthermore,the fabricated asymmetry supercapacitor(ASC)achieves an extraordinary energy density of 77 Wh·kg^(-1)(0.617 m Wh·cm^(-2))at a power density of 43. W·kg^(-1)(3.5 m W·cm^(-2))and outstanding stability(91%capacity retention after 5000 cycles at20 m A·cm^(-2)).Impressively,the structure evolution of Ni Co-LDH during the charge/discharge processes has been thoroughly elucidated by in-situ Raman ***,this work verifies a powerful strategy and practical value for preparing composite electrodes with high supercapacitance performance,and also provides guidance for the rational design of the smart electrodes.

关键词： Supercapacitor NiCo-LDH Carbon nanotubes Sulfur and nitrogen co-doped Convenient synthesis

Investigation of Breaking Efficiency of N-Glycosidic Bond Between Sulfonamide and Honey

在线全文

学校读者我要写书评

暂无评论

Chemical Research in Chinese Universities 2012年第2期28卷 195-199页

作者： wang Yan-hua li li CHEN Chia-hung CHENG Shuenn-ren LEE Mu-sheng YU Pu-ping CHANG-CHIEN Guo-ping college of Biology and Enviornmental engineering Zhejiang Shuren University Hangzhou 310015 P. R. China Super Micro Mass Research ＆ technology Center Department of Business Administration Department of mechanical engineering Cheng Shiu University Kaohsiung 833 Taiwan P. R. China Environmental Protection Bureau Kaohsiung City Government Keelung 20143 Taiwan P. R. China

Sulfonamide residue in honey existed in a form bonded to sugar via the N-glycosidic *** would result in the possible underestimation of concentration of sulfonamide if it is not decomposed by chemical ***,in China's Mainland and Taiwan（***）,the regulation for sulfonamide residue analysis does not include hydrolysis and has been applied to a very broad range of samples,for example,egg,milk,meat,seafood as well as *** paper demonstrates the necessity of hydrolysis of it prior to extracting *** breaking efficiencies of N-glycosidic bond were investigated by 2 mol/L hydrochloric acid,pure methanol and 0.5 mol/L hydrochloric acid in methanol,*** was found that acid plays the key role in breaking the N-glycosidic bond,and it was also noticed that the dissolution of liberated sulfonamide in methanol could carry the reaction forward in favor of breaking the N-glycosidic bond.

关键词： Sulfonamide Honey liquid chromatography-electrospray ionization tandem mass spectrometry(LC-ESIMS/MS) N-Glycosidic bond

Layered niobium carbide enabling excellent kinetics and cycling stability of li-Mg-B-H hydrogen storage material Layered niobium carbide enabling excellent kinetics

在线全文

学校读者我要写书评

暂无评论

Rare Metals 2024年第3期43卷 1153-1166页

作者： li-Wen Lu Hui Luo Guang-Xu li Yun li Xin-Hua {3. Cun-Ke Huang Zhi-QiangLan Wen-Zheng Zhou Jin Guo Mohammad Ismail Hai-Zhen liu Guangxi Novel Battery Materials Research Center of engineering technology Guangxi Colleges and Universities Key Laboratory of Blue Energy and Systems IntegrationSchool of Physical Science and TechnologyGuangxi UniversityNanning530004China State Key Laboratory of Featured Metal Materials and life-Cycle Safety for Composite Structures Nanning530004China School of mechanical and Electrical engineering Quzhou College of TechnologyQuzhou324000China Department of Materials Science and engineering Zhejiang UniversityHangzhou310027China Faculty of Ocean engineering technology and Informatics Universiti Malaysia Terengganu21030Kuala NerusTerengganuMalaysia Key Laboratory of Advanced Energy Materials Chemistry(Ministry of Education) Nankai UniversityTianjin300071China

The li-Mg-B-H composite(2liBH_(4)+MgH_(2))has a high capacity of 11.4 wt%as a hydrogen storage ***,the slow kinetics and poor cycling stability severely restrict its practical *** this work,a layered Nb_(2)C MXene was first synthesized and then introduced to tailor the kinetics and cycling stability of the li-Mg-B-H *** milled 2liH+MgB_(2)composites were initially hydrogenated to obtain the 2liBH_(4)+MgH_(2)*** 2liBH_(4)+MgH_(2)+5wt%Nb_(2)C can release 9.0 wt%H_(2)in 3. min at 400℃,while it is only 2.7 wt%for the undoped 2liBH_(4)+MgH_(2).The dehydrogenation activation energies of MgH_(2)and liBH_(4)are 123.and 154 kJ·mol^(-1)respectively for the 5 wt%Nb_(2)C-doped composite,lower than the undoped composite(164 and 165 kJ·mol^(-1)).The 2liBH_(4)+MgH_(2)+5 wt%Nb_(2)C possesses excellent cycling stability,with the reversible capacity only slightly reduced from 9.4 wt%for the 1st cycle to 9.3.wt%for the 20th ***_(2)C keeps stable in the composite and acts as an efficient catalyst for the li-Mg-B-H *** is believed that both the layered structure and the active Nb element contribu te to the enhanced hydrogen storage performances of the li-Mg-B-H *** work confirms that the Nb_(2)C MXene with layered stru cture has a significant enhancing impact on the li-Mg-B-H hydrogen storage materials,which is different from the bulk NbC.

关键词： Hydrogen storage lithium borohydride Magnesium hydride Nb_(2)C MXene

Effect of heat treatment on microstructural evolution,mechanical properties and tribological properties of H13.steel prepared using selective laser melting

在线全文

学校读者我要写书评

暂无评论

Journal of Iron and Steel Research International 2024年第5期31卷 1246-1259页

作者： li-xiong Han Yan wang Shi-feng liu Zhao-hui Zhang Wei liu Xin Yang Dang-shen Ma Jian Zhou Ying-kang Wei college of Metallurgical engineering Xi’an University of Architecture and TechnologyXi’an710055ShaanxiChina zhejiang university City college Hangzhou310015ZhejiangChina China Iron and Steel Research Institute Group Co. Ltd.Beijing100081China

H13.tool steel was successfully prepared by selective laser melting(SLM)*** effects of heat treatment on the microstructure,mechanical properties,and tribological properties of SLMed H13.steel were *** heat treatment process involved a solution treatment and a double aging treatment of the deposited H13.tool steel prepared by *** aim is to optimize the microstructure and mechanical properties of SLMed H13.*** to the rapid heating and cooling effects of SLM,carbide precipitation in the deposited H13.steel was not uniform and residual stresses were *** purpose of the solution treatment is to dissolve the solution at a high temperature to eliminate the residual stresses and defects introduced by the SLM-forming *** solution treatment and first aging treatment produced the precipitation of small carbides at the grain boundaries and inside the crystals,which increased the hardness of SLMed H13.*** hardness increased from 53.±4.0 HV of the as-deposited sample to 548±5.8 HV of samples after the first aging ***,the ultimate tensile strength and the elongation at break decreased from 1882 MPa and 11.5%in the as-deposited sample to 1697 MPa and 7.9%in those after the first aging treatment,***,the friction coefficient and wear rate in the as-deposited sample decreased from 0.5160 and 2.3.×10^(–6)mm^(−3.N^(−1)m^(−1)to 0.4244 and 1.04×10^(–6)mm^(−3.N^(−1)m^(−1),***,the distribution of carbides inside the crystals was not *** second aging treatment adjusted the morphology of carbide precipitation and made it more uniform,but the precipitation of carbides grew and settled at the bottom of the grain *** hardness decreased to 53.±6.7 HV compared with that with the first aging treatment,but the ultimate tensile strength and plasticity reached a balance(1807 MPa,14.05%).Accordingly,the friction coefficient and wear rate also showed a stable and decreasin

关键词： Selective laser melting H13.steel Solution aging Double aging Friction and wear Retained austenite

The marriage of immunomodulatory,angiogenic,and osteogenic capabilities in a piezoelectric hydrogel tissue engineering scafold for military medicine

维普期刊数据库评论

在线全文

维普期刊数据库

学校读者我要写书评

暂无评论

Military Medical Research 2024年第3期11卷 323-344页

作者： Ping Wu lin Shen Hui-Fan liu Xiang-Hui Zou Juan Zhao Yu Huang Yu-Fan Zhu Zhao-Yu li Chao Xu li-Hua Luo Zhi-Qiang Luo Min-Hao Wu lin Cai Xiao-Kun li Zhou-Guang wang Key Laboratory of Imaging Diagnosis and Minimally Invasive Intervention Research the Fifth Affiliated Hospital of Wenzhou Medical UniversityLishui 323000ZhejiangChina Oujiang Laboratory(zhejiang Lab for Regenerative Medicine Vision and Brain Health)School of Pharmaceutical ScienceWenzhou Medical UniversityWenzhou 325000ZhejiangChina Department of Spine Surgery and Musculoskeletal Tumor Zhongnan Hospital of Wuhan UniversityWuhan 430071China National engineering Research Center for Nanomedicine College of Life Science and TechnologyHuazhong University of Science and TechnologyWuhan 430074China Department of Overseas Education college Jimei UniversityXiamen 361021FujianChina School and Hospital of Stomatology Wenzhou Medical UniversityWenzhou 325035ZhejiangChina

Background:Most bone-related injuries to grassroots troops are caused by training or accidental *** establish preventive measures to reduce all kinds of trauma and improve the combat effectiveness of grassroots troops,it is imperative to develop new strategies and scafolds to promote bone ***:In this study,a porous piezoelectric hydrogel bone scafold was fabricated by incorporating polydopamine(PDA)-modified ceramic hydroxyapatite(PDA-hydroxyapatite,PHA)and PDA-modified barium titanate(PDABaTiO_(3.,PBT)nanoparticles into a chitosan/gelatin(Cs/Gel)*** physical and chemical properties of the Cs/Gel/PHA scafold with 0–10 wt%PBT were *** and animal experiments were performed to characterize the immunomodulatory,angiogenic,and osteogenic capabilities of the piezoelectric hydrogel scafold in vitro and in ***:The incorporation of BaTiO_(3. into the scafold improved its mechanical properties and increased self-generated *** to their endogenous piezoelectric stimulation and bioactive constituents,the prepared Cs/Gel/PHA/PBT hydrogels exhibited cytocompatibility as well as immunomodulatory,angiogenic,and osteogenic capabilities;they not only effectively induced macrophage polarization to M2 phenotype but also promoted the migration,tube formation,and angiogenic differentiation of human umbilical vein endothelial cells(HUVECs)and facilitated the migration,osteodifferentiation,and extracellular matrix(ECM)mineralization of MC3.3.E1 *** in vivo evaluations showed that these piezoelectric hydrogels with versatile capabilities significantly facilitated new bone formation in a rat large-sized cranial injury *** underlying molecular mechanism can be partly attributed to the immunomodulation of the Cs/Gel/PHA/PBT hydrogels as shown via transcriptome sequencing analysis,and the PI3./Akt signaling axis plays an important role in regulating macrophage M2 ***:The piezoelectric Cs/Gel/PHA/PBT hy

关键词： Piezoelectric hydrogel Tissue engineering scafold Immunomodulation Angiogenesis Osteogenic differentiation

在线全文

学校读者我要写书评

暂无评论

插秧机导航路径跟踪改进纯追踪算法

农业机械学报 2018年第5期49卷 21-26页

作者：李革王宇郭刘粉童俊华何勇浙江理工大学机械与自动控制学院杭州310018 浙江省种植装备技术重点实验室杭州310018 浙江大学生物系统工程与食品科学学院杭州310058

插秧机田间行驶路径包括直线作业段和地头曲线转弯段,因此需要对传统的纯追踪算法进行改进,使其满足曲线路径跟踪。以约翰迪尔Starfire3.00型接收机、GS263.型显示器和ATU200型电动方向盘为主要硬件设备,针对给定的曲线路径,提出了一种... 详细信息

插秧机田间行驶路径包括直线作业段和地头曲线转弯段,因此需要对传统的纯追踪算法进行改进,使其满足曲线路径跟踪。以约翰迪尔Starfire3.00型接收机、GS263.型显示器和ATU200型电动方向盘为主要硬件设备,针对给定的曲线路径,提出了一种路径跟踪控制算法,并通过模型仿真和田间试验相结合的方法,对该导航控制算法进行了验证分析。该导航控制算法首先根据车辆速度和路径弯曲程度来动态调整前视距离,其次在利用预见控制求得车辆目标点的基础上,利用改进的纯追踪算法设计控制器,最后按照插秧机作业时的路径进行仿真和试验。试验结果表明,车辆以1 m/s的速度行驶且在转弯半径为0.9 m时,最大跟踪误差可控制在0.159 m以内。

关键词：插秧机路径跟踪纯追踪算法前视距离

Physicochemical characterization of Dendrobium officinale polysaccharides and regulation of immunometabolic homeostasis in Sub-health mice based on the CD4-Th17/Treg immunity axis

在线全文

学校读者我要写书评

暂无评论

Food Science and Human Wellness 2024年

作者： Bo li Ze-Hua Zhang Hao-Ru Guan Xing-li-Shang He Ning wang Ying-Jie Dong Mei Rong Jiu-Jie Jia Ting-Ting Chen Zhi-Yuan li Gui-Yuan Lv lin-Nan Zhang Su-Hong Chen Collaborative Innovation Center of Yangtze River Delta Region Green Pharmaceuticals， zhejiang university of technology zhejiang Provincial Key Laboratory of TCM for Innovative R & D and Digital Intelligent Manufacturing of TCM Great Health Products.Huzhou college of Pharmaceutical Science， zhejiang Chinese Medical university

The aim of this study was to investigate the role of DOPS and DOPS100 in attenuating immune dysfunction in subfertile mice. The results of the study revealed several noteworthy findings. First， DOPS and DOPS100 treatments led to significant improvement in weight gain and reversal of fatigue-related behaviors compared to the normal group. Second， both DOPS and DOPS100 showed effectiveness in reducing immune organ swelling， modulating immunoglobulin （IgA and IgM） levels， and restoring complement （C3. and C4） levels. In addition， they demonstrated a significant ability to enhance the integrity of the intestinal {3. barrier by differentially upregulating the tight junction proteins Occludin and ZO-1. In addition， it was found that DOPS100 specifically enhanced the CD4+-Th17/Treg immune axis in the gut， as evidenced by increased expression of Foxp3.as well as decreased expression of RORγt， and further modulation of IL-10， IL-22， and IL-17A expression levels of inflammatory factors. These findings collectively suggest that DOPS100 holds significant potential in improving sub-healthy status by repairing the intestinal barrier， restoring local immune homeostasis， and activating the intestinal immune regulatory network. The study's outcomes provide valuable insights into the therapeutic implications of DOPS and DOPS100 in addressing immune dysfunction in sub-healthy conditions.

关键词：

热处理对自反应淬熄法制备低频liZn铁氧体空心微珠的影响（英文）

在线全文

同方期刊数据库

学校读者我要写书评

暂无评论

Journal of zhejiang university-Science A(Applied Physics & {3.) 2018年第5期19卷 409-416页

作者： Xu-dong CAI Jian-jiang wang Xiao-jun JIANG Jun liNG Yi XU Zhan-tong GAO The First Scientific Research Institute of Wuxi Wuxi 214035China The Seventh Department Mechanical Engineering CollegeShijiazhuang 050003China Cadres Office Mechanical Engineering CollegeShijiazhuang 050003China

目的:自反应淬熄法制备的liZn铁氧体空心微珠密度小,低频吸波性能良好,但微珠表面晶型生长不充分。对其采用特定热处理工艺不仅可以使晶体充分发育,获得特定晶型,还可以实现对低频吸波性能的有效调控。本文旨在研究热处理工艺对liZn铁... 详细信息

目的:自反应淬熄法制备的liZn铁氧体空心微珠密度小,低频吸波性能良好,但微珠表面晶型生长不充分。对其采用特定热处理工艺不仅可以使晶体充分发育,获得特定晶型,还可以实现对低频吸波性能的有效调控。本文旨在研究热处理工艺对liZn铁氧体空心微珠表面形貌、相结构和低频吸波性能的影响。创新点:1.通过热处理工艺,实现对liZn铁氧体空心微珠表面形貌、相结构和低频吸波性能的有效调控;2.深入分析热处理工艺对liZn铁氧体空心微珠低频吸波性能的改善机理。方法:1.通过工艺探索,确定热处理的详细工艺参数。2.通过扫描电子显微镜检测和X射线衍射分析,获得热处理前后liZn铁氧体空心微珠的微观形貌(图2)和物相组成(图3.。3.通过矢量网络分析仪,获得热处理前后材料的电磁参数(图4);在此基础上对比其吸波性能(图5),并研究吸波影响机理。结论:1.采用240°C/min升温至1200°C并保温4 h的热处理后,liZn铁氧体空心微珠表面晶粒明显长大;2.热处理后,微珠四个电磁参数均有所增大,低频吸波性能明显提高,吸收峰值向低频移动;3.表面多种形状微纳米晶粒的形成和长大可能是liZn铁氧体空心微珠低频吸波性能得以提高的主要原因。

关键词： liZn铁氧体热处理低频吸波性能