Synthesis of metallic glasses and metallic glass based composites in the Cu-Mo-Hf system by ion beam mixing

在线全文

学校读者我要写书评

暂无评论

Science China(Technological Sciences) 2012年第5期55卷 1353-1358页

作者： BAI Xue wang tongle CUI YuanYuan DING Ning LI JiaHao LIU BaiXin Advanced Materials Laboratory Department of Materials Science and EngineeringTsinghua UniversityBeijing 100084China

Single-phase and dual-phase metallic glasses as well as metallic glass based composites were synthesized in the Cu-Mo-Hf ternary metal system by 200 keV xenon ion beam mixing of far-from-equilibrium. It was found that Mo-Hf-based and Cu-Mo-based single-phase metallic glasses could be obtained at compositions around CulTMo20Hf63 and Cu34Mo57Hf9, respectively. Interestingly, at the nearly equal-atomic stoichiometry of Cu38Mo31Hf3i, a dual-phase Cu-Mo-Hf metallic glass, consisting both of the Mo-Hf-based and Cu-Mo-based phases, was first obtained at relatively low irradiation doses ranging from （1-5）×10^15 Xe＋/cm2, and a single-phase metallic glass was eventually obtained at a dose of 7×10^15 Xe＋/cm2. In addition, two glass-based composites were obtained at the compositions of Cu14Mo62Hf24 and Cu77Mo14Hf9, and they consisted of the Mo-Hf based and Cu-Mo based metallic glasses, dissolved with some uniformly distributed BCC Mo-based and FCC Cu-based crystalline solid solutions, respectively. The formation mechanism of the above described non-equilibrium alloy phases was also discussed in terms of the atomic collision theory.

关键词： Cu-Mo-Hf system ion beam mixing metallic glass dual-phase metallic glass glass-based composite

Non-equilibrium alloy phase formation and transformation driven by ion beam mixing in the Fe-Hf-Nb multilayers

在线全文

学校读者我要写书评

暂无评论

Science China(Technological Sciences) 2012年第3期55卷 640-645页

作者： LI Nan wang tongle DING Ning DAI Ye BAI Xue LIU BaiXin Advanced Materials Laboratory Department of Materials Science and EngineeringTsinghua UniversityBeijing 100084China

In the ion beam mixing experiments,eight Fe-Hf-Nb multilayered films,with overall compositions of Fe67Hf22Nb11,Fe67Hf11Nb22,Fe54Hf38Nb8,Fe54Hf30Nb16,Fe54Hf11Nb35,Fe25Hf67Nb8,Fe25Hf50Nb25 and Fe25Hf11Nb64,were irradiated by 200 keV xenon ions to doses ranging from 3×1014 Xe+/cm2 to 7×1015 Xe+/*** results showed that unique amorphous phases were obtained at designed alloy compositions,falling in the favored glass-forming region deduced from three binary metal ***,at some alloy compositions,the crystal-amorphous-crystal transformations were observed back and forth while varying the irradiation *** addition,at the alloy composition of Fe25Hf67Nb8,a metastable FCC phase was formed through an HCP-FCC structural phase transformation and it had a large lattice constant identified to be a=4.51 .Besides,the formation mechanism of non-equilibrium alloy phases was also discussed in terms of thermodynamics of solids and atomic collision theory.

关键词： phase transformation ion beam mixing amorphous phase Fe-Hf-Nb system shearing mechanism

在线全文

学校读者我要写书评

暂无评论

基于概率矩阵分解的多失真图像质量评估算法

计算机应用与软件 2019年第7期36卷 264-272页

作者：王同乐王慈华东师范大学计算机科学与技术系

图像质量评价(Image Quality Assessment,IQA)是视觉感知模型研究的重要分支,使用IQA算法自动化地评估图像质量有广阔的应用前景。基于概率矩阵分解(Probability Matrix Factorization)提出一种多失真图像质量评价算法,主要贡献有:提出... 详细信息

图像质量评价(Image Quality Assessment,IQA)是视觉感知模型研究的重要分支,使用IQA算法自动化地评估图像质量有广阔的应用前景。基于概率矩阵分解(Probability Matrix Factorization)提出一种多失真图像质量评价算法,主要贡献有:提出一种图像质量评价的新思路,即利用PMF方法从失真图像估计参考图像,把失真图像和估计参考图像之间的信息损失作为图像质量的度量;构建新颖的特征向量描述这种信息损失;使用支持向量回归(Support Vector Regression,SVR)完成图像质量模型的训练。提出的算法在多个公开的图像质量评价数据库上超过了经典方法,实验结果证明该方法与人的主观质量评价具有更好的一致性。

关键词：盲图像质量评价概率矩阵分解支持向量回归人眼视觉系统

Dynamic Modeling and Simulation Analysis on Micro-grid Based on DIgSILENT

在线全文

学校读者我要写书评

暂无评论

Dynamic Modeling and Simulation Analysis on Micro-grid Based...

2011 International Conference on Advanced Power System Automation and Protection(APAP 2011)

作者： DING tongle, wang Gang, LI HaiFeng School of Electric Power, South China University of Technology, Guangzhou 510640, China

In this paper, dynamic models of main micro-generation sources are described and built based on their mathematical model in particular, the models of Micro-turbine, Wind turbine with full rated converter, Photovoltaic Systems and Battery Energy Storage System （BESS）. In addition, control mode of their power electronic interfaces are given and analyzed based on the characteristic of Distributed Generations （DGS）. A micro-grid adopting peer-to-peer control mode is then built comprising these micro-generation source and a battery energy storage system. Dynamic characteristics of frequency response and voltage response are made under operating mode switch of micro-grid between grid connected mode and islanded mode. According to the simulation case study, the battery energy storage system using droop control is essential to the micro-grid in islanded, which can increase the speed of response of micro-grid efficiently.

关键词： DIgSILENT micro-grid distributed generation peer-to-peer BESS

来源： cnki会议评论

在线全文

cnki会议

学校读者我要写书评

暂无评论

消失模铸钢醇基涂料的开发

特种铸造及有色合金 2014年第5期34卷 519-520页

作者：徐峰冯小明刘艳王同乐陕西理工学院材料科学与工程学院

以锆铝石粉为耐火骨料,酚醛树脂和硅溶胶混合使用做粘结剂,CMC和钠基膨润土混合使用做悬浮剂,采用异丙醇作载体,开发出消失模铸钢醇基涂料。通过试验确定了消失模铸钢醇基涂料的最佳配比,并对涂料综合性能进行了测试。

关键词：消失模铸造锆铝石醇基涂料

在线全文

学校读者我要写书评

暂无评论

等通道挤压对2A12铝合金组织性能的影响

热加工工艺 2014年第11期43卷 106-108页

作者：张会王同乐王玉梅王永善陕西理工学院材料学院陕西汉中723003

对2A12铝合金进行了等通道挤压工艺研究,进行了组织观察,分析了晶粒细化效果。试验表明:在320℃下,对2A12铝合金棒材进行等通道转角挤压,可以获得宏观外形完整无裂纹的试样;经过不同道次的等通道挤压后,晶内、晶界出现大量的Al2Cu、Al2C... 详细信息

对2A12铝合金进行了等通道挤压工艺研究,进行了组织观察,分析了晶粒细化效果。试验表明:在320℃下,对2A12铝合金棒材进行等通道转角挤压,可以获得宏观外形完整无裂纹的试样;经过不同道次的等通道挤压后,晶内、晶界出现大量的Al2Cu、Al2CuMg弥散相;以Bc、C路径进行挤压,随变形道次的增加,基体得到细化,且过程稳定,细化效果好。

关键词：等通道挤压 2A12铝合金挤压路径细化效果

在线全文

学校读者我要写书评

暂无评论

低温熔盐法制备片状氧化铝

陶瓷 2011年第9期 21-22页

作者：王同乐陕西理工学院材料学院陕西汉中723003

研究了以氢氧化铝为原料,氯化钠-氯化钾为熔盐,以及熔盐加入量对试样物相的影响。研究结果表明,熔盐加入量为67%时,在1000℃保温4h,得到了结晶完整的,边长为5～10μm,厚度为0.6～1.4μm的片状α-Al2O3;熔盐加入量为50%时,不能得到片状... 详细信息

研究了以氢氧化铝为原料,氯化钠-氯化钾为熔盐,以及熔盐加入量对试样物相的影响。研究结果表明,熔盐加入量为67%时,在1000℃保温4h,得到了结晶完整的,边长为5～10μm,厚度为0.6～1.4μm的片状α-Al2O3;熔盐加入量为50%时,不能得到片状氧化铝。

关键词：氢氧化铝氯化钠-氯化钾制备片状氧化铝

Zr-Nb-Cu合金非晶化反应的热力学计算及离子束混合实验

在线全文

学校读者我要写书评

暂无评论

热加工工艺 2013年第2期42卷 5-8页

作者：梁苏会王同乐李家好国核电力规划设计研究院北京100095 德润特数字影像科技北京有限公司北京100195 清华大学材料科学与工程系北京100084

利用超高真空镀膜法制备了Zr-Nb-Cu合金系统五个不同成分点多层膜样品,成分点分别为Zr63Nb19Cu18、Zr42Nb19Cu39、Zr41Nb39Cu20、Zr19Nb18Cu63和Zr14Nb70Cu16。对样品进行离子束混合实验及相关表征后发现,Zr-Nb-Cu合金系统能形成非晶态... 详细信息

利用超高真空镀膜法制备了Zr-Nb-Cu合金系统五个不同成分点多层膜样品,成分点分别为Zr63Nb19Cu18、Zr42Nb19Cu39、Zr41Nb39Cu20、Zr19Nb18Cu63和Zr14Nb70Cu16。对样品进行离子束混合实验及相关表征后发现,Zr-Nb-Cu合金系统能形成非晶态合金,但是Nb元素的加入并不利于非晶形成。Zr19Nb18Cu63和Zr41Nb39Cu20多层膜样品得到了非晶态和固溶体的双相结构,此类双相结构比单一非晶相结构具有更好的力学性能。

关键词：非晶态离子束混合热力学计算

模具结构对等通道挤压2A12铝合金组织和性能的影响

在线全文

学校读者我要写书评

暂无评论

特种铸造及有色合金 2014年第6期34卷 596-599页

作者：张会张昌明王永善王玉梅王同乐陕西理工学院材料学院

等通道转角挤压工艺(ECAP)通过不同路经的多道次挤压变形,产生大的塑性变形,可以达到细化晶粒的目的,同时也是超细晶材料制备的一种有效渠道。但试样在通过转角处会产生强烈的拉应力,累积的拉应力极易达到材料的抗拉极限,导致开裂,甚至... 详细信息

等通道转角挤压工艺(ECAP)通过不同路经的多道次挤压变形,产生大的塑性变形,可以达到细化晶粒的目的,同时也是超细晶材料制备的一种有效渠道。但试样在通过转角处会产生强烈的拉应力,累积的拉应力极易达到材料的抗拉极限,导致开裂,甚至断裂。为了减少这一现象发生的几率,减小试样开裂倾向,便于后一道次的挤压,对转角为90°的模具进行了改进。对2A12铝合金进行挤压研究结果表明,在C路径下4道次挤压效果较好,增强了晶粒细化效果,伸长率最大提高了10.3%,硬度最大提高了46.4%。

关键词：等通道挤压 2A12铝合金挤压路径细化效果