Characterization of magnetically impelled arc butt welded T11 tubes for high pressure applications

Defence Technology（防务技术） 2015年第3期11卷 244-254页

作者： R.SIvASANKARI v.balusamy P.R.vENKATESWARAN G.BUvANASHEKARAN K.GANESH KUMAR Department of Metallurgical Engineering PSG College of Engineering Welding Research Institute Bharat Heavy Electricals Limited

Magnetically impelled arc butt(MIAB) welding is a pressure welding process used for joining of pipes and tubes with an external magnetic field affecting arc rotation along the tube circumference. In this work, MIAB welding of low alloy steel(T11) tubes were carried out to study the microstructural changes occurring in thermo-mechanically affected zone(TMAZ). To qualify the process for the welding applications where pressure could be up to 300 bar, the MIAB welds are studied with variations of arc current and arc rotation time. It is found that TMAZ shows higher hardness than that in base metal and displays higher weld tensile strength and ductility due to bainitic transformation. The effect of arc current on the weld interface is also detailed and is found to be defect free at higher values of arc currents. The results reveal that MIAB welded samples exhibits good structural property correlation for high pressure applications with an added benefit of enhanced productivity at lower *** study will enable the use of MIAB welding for high pressure applications in power and defence sectors.

关键词：磁控电弧磁场影响高压力应用压力焊接特性对焊驱动

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

In-Situ Corrosion Monitoring of Scratched Epoxy Coated Carbon Steel in Saturated Ca(OH)₂ with or without 3% NaCl by Scanning Electrochemical Microscopy and Electrochemical Impedance Spectroscopy

引用

American Journal of Analytical Chemistry 2016年第7期7卷 533-547页

作者： Thangaraj balusamy Toshiyasu Nishimura Corrosion Resistant Steel Group Research Center for Structural Materials (RCSM) National Institute for Materials Science Tsukuba Japan

The present work is investigated the in-situ monitoring of local corrosion process of scratched epoxy coated carbon steel in saturated Ca(OH)2 with and without 3% NaCl using SECM and correlated with EIS. The results obtained from EIS analysis showed that the corrosion resistance of scratched epoxy coated carbon steel decreases in Cl- containing solution as the increase in wet/ dry corrosion cycles. This was indicated by decrease in film resistance (Rf) and charge transfer resistance (Rct), while the coated steel maintain the resistance values in saturated Ca(OH)2, most of which recovered after drying. The corrosion process was monitored using SECM by setting the tip potential at -0.70 v vs Ag/AgCl, where the consumption of dissolved oxygen occurred at the surface of test sample. The consumption of dissolved oxygen current (I’oxy-c) values was increased during the immersion in a solution with 3% NaCl. However, in wet/dry corrosion cycles, I’oxy-c was decreased due to the coverage of hydroxides/oxides at scratch area which suppressed the consumption of dissolved O2. It was found that the continuous decrease in corrosion was mainly attributed to continuous formation of corrosion products at anodic spots.

关键词： Epoxy Coated Carbon Steel Alkaline Solution Chlorides SECM Wet/Dry Corrosion Cycles

来源：

维普期刊数据库评论

在线全文

维普期刊数据库

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：