China Foundry 2023年第1期20卷 49-56页

作者： tian-yu liu Kun Shi Jun Zhao Shi-bing liu You-wei Zhang Hong-yu liu tian-yi liu Xiao-ming Chen Xin-min Mei Shenyang Research Institute of Foundry Co. Ltd.Shenyang 110022China State Key Laboratory of Light Alloy Casting Technology for High-end Equipment Shenyang 110022China

Hot isostatic pressing parameters are critical to Ti60 high temperature titanium alloy castings which have wide application perspective in *** order to obtain optimal processing parameters,the effects of hot isostatic pressing parameters on defects,composition uniformity,microstructure and mechanical properties of Ti60 cast high temperature titanium alloy were investigated in *** show that increasing temperature and pressure of hot isostatic pressing can reduce defects,especially,the internal defects are substantially eliminated when the temperature exceeds 920℃or the pressure exceeds 125 *** higher temperature and pressure can improve the microstructure ***,the higher pressure can promote the composition *** the temperature increases from 880℃to 960℃,α-laths are *** with increasing pressure,the grain size of prior-βphase,the widths ofα-laths andα-colony are *** tensile strength of Ti60 alloy is 949 MPa,yield strength is 827 MPa,and the elongation is 11%when the hot isostatic pressing parameters are 960℃/125 MPa/2 h,which exhibits the best match between the strength and plasticity.

关键词： hot isostatic pressing processing parameters Ti60 titanium alloy defects composition uniformity microstructure mechanical properties

High-strength Ti-Al-V-Zr cast alloys designed using α and β cluster formulas

在线全文

学校读者我要写书评

暂无评论

China Foundry 2023年第1期20卷 23-28页

作者： Zhi-hao Zhu yu-han liu Zhi-peng Chen tian-yu liu Shuang Zhang Dan-dan Dong Chuang Dong Key Laboratory for Materials Modification by Laser Ionand Electron Beams and School of Materials Science and EngineeringDalian University of TechnologyDalian 116024LiaoningChina State Key Laboratory of Light Alloy Casting Technology for High-end Equipment Shenyang Research Institute of Foundry Co.Ltd.Shenyang 110022China School of Materials Science and Engineering Dalian Jiaotong UniversityDalian 116028LiaoningChina College of Physical Science and Technology Dalian UniversityDalian 116622LiaoningChina

Ti-Al-V-Zr quaternary titanium alloys were designed followingα-{[Al-Ti12](AlTi2)}17-n+β-{[Al-Ti12Zr2](V3)}n,where n=1-7(the number ofβunits),on the basis of the dual-cluster formula of popular Ti-6Al-4V *** an alloying strategy aims at strengthening the alloy via Zr and V co-alloying in theβ-Ti unit,based on the originalβformula[Al-Ti14](V2Ti)of Ti-6Al-4V *** microstructures of the as-cast alloys by copper-mold suction-casting change from pureα(n=1)toα+α’martensite(n=7).When n is 6,Ti-5.6Al-6.8V-8.1Zr alloy reaches the highest ultimate tensile strength of 1,293 MPa and yield strength of 1,097 MPa,at the expense of a low elongation of 2%,mainly due to the presence of a large amount of acicularα’*** specific strength far exceeds that of Ti-6Al-4V alloy by 35%.

关键词： titanium alloy cluster-plus-glue-atom model composition design microstructure mechanical properties

A New Method to Locate the Region of Interest( ROI) of Palmprint

在线全文

学校读者我要写书评

暂无评论

Journal of Harbin Institute of Technology(New Series) 2013年第2期20卷 111-117页

作者： Ping Xue Wen-Chao Li tian-yu liu College of Automation Harbin University of Science and Technology

Biometric identification was a kind of identity recognition technology by making use of the human's unique physiological or behavioral characteristics,it provided a high reliability and stability way for the identification. Global threshold binarization palmprint image is used in this paper,and the bio-morphological methods are used to get the sensitive area of palmprint image's positioning point,so as to extract the region of interest. The palmprint collection is realized on the FPGA chip,and this kind of collection method uses the DSP Builder toolbox to realize visual programming in Matlab / Simulink and achieve fast modeling and development. The practice proves that this method is simple,flexible and its equipment is portable and fast.

关键词： DSP builder FPGA palmprint identification region of interest( ROI)

Composition formula of Al-TMs high-entropy alloys derived by cluster-plus-glue-atoms model and its experimental verification

在线全文

学校读者我要写书评

暂无评论

China Foundry 2022年第6期19卷 544-550页

作者： tian-yu liu Kun Shi Jun Zhao Shi-bing liu Hong-yu liu Bo-liang liu Xin-min Mei Zhao-sheng Ning Xiao-ming Chen State Key Laboratory of Light Alloy Casting Technology for High-end Equipment Shenyang Research Institute of Foundry Co.Ltd.Shenyang 110022China

High-entropy alloys(HEAs)are based on solid solutions which characterized by chemical short-range ordering(CSRO),but there is no accurate structural tool to address CSRO characteristic,which obstacles precise composition design for *** this study,based on the cluster-plus-glue-atoms model,the composition law of Al-TMs(TMs,transition metals)HEAs with BCC and FCC structures was *** BCC structure,with five elements in equi-atomic ratio,the composition formula of Al-TMs HEAs can be expressed by a cluster formula[Al-M_(14)]Al_(3),and in non equi-atomic ratio can be expressed by[Al-M_(14)]Al,where M is the average atom of the *** in FCC structure,both Al-TMs HEAs with five elements in equiatomic and non equi-atomic ratios can be expressed by a cluster formula[Al-M_(12)]*** confirm the effectiveness of cluster formula for Al-TMs,two alloys were designed,[Al-Ti_(4)V_(3)Nb_(4)Mo_(3)]Mo and[Al-Ti_(3)V_(3)Nb_(4)Mo_(4)]*** show that the[Al-Ti_(3)V_(3)Nb_(4)Mo_(4)]Al alloy has both higher strength and higher plastic deformation at room ***,[Al-Ti_(3)V_(3)Nb_(4)Mo_(4)]Al alloy shows slower soften effect at 800℃,contributed to its higher *** substituting Ta for some of Mo,the strength of[Al-Ti_(3)V_(3)Nb_(4)Mo_(3)Ta]Al at room temperature and high temperature drastically decreases,suggesting that Ta element deteriorates the properties of Al-TMs alloys.

关键词： Al-TMs high-entropy alloys composition design short-range order cluster-plus-glue-atom model

Microstructure and mechanical properties of laser additive manufactured novel titanium alloy after heat treatment

在线全文

学校读者我要写书评

暂无评论

China Foundry 2021年第6期18卷 574-580页

作者： tian-yu liu Hong-yu liu Qian Yao Shi-bing liu Kun Shi Zhi-yong Zhang Chong-yang Li Shenyang Research Institute of Foundry Co. Ltd.Shenyang 110022China State Key Laboratory of Light Alloy Casting Technology for High-end Equipment Shenyang 110022China

A novel α+β titanium alloy with multi-alloying addition was designed based on the cluster formula 12[Al-Ti_(12)](AlTi_(2))+5[Al-Ti_(14)](AlV_(1.2)Mo_(0.6)Nb_(0.2))which was derived from *** nominal composition of this novel alloy was determined as *** this study,the novel alloy and Ti-6Al-4V alloy samples were prepared by laser additive *** microstructure,micro-hardness,room/high temperature tensile properties of the as-deposited samples were *** to Ti-6Al-4V,the novel alloy has much higher room and high temperature(600℃)tensile strengths,which are 1,427.5 MPa and 642.2 MPa,respectively;however,it has a much lower elongation(3.2%)at room temperature because of the finer *** improve the elongation of the novel alloy,heat treatment was *** solution at 960℃ or 970℃ for 1 h followed by air cooling and aging at 550℃ for 4 h followed by air cooling,a unique bi-modal microstructure which contains crab-like primaryαand residual β phase is obtained,improving the compression elongation by 80.9% compared to the as-deposited *** novel alloy can be used as a high-temperature and high-strength candidate for laser additive manufacturing.

关键词： laser additive manufacturing titanium alloy composition design heat treatment

Effect of processing parameters on formability, microstructure, and micro-hardness of a novel laser additive manufactured Ti-6.38Al-3.87V-2.43Mo alloy

在线全文

学校读者我要写书评

暂无评论

China Foundry 2022年第2期19卷 158-168页

作者： tian-yu liu Zhi-hao Zhu Shuang Zhang Xiao-hua Min Chuang Dong School of Materials Science and Engineering Dalian University of TechnologyDalian 116024LiaoningChina School of Materials Science and Engineering Dalian Jiaotong UniversityDalian 116028LiaoningChina

A novel Ti-6.38Al-3.87V-2.43Mo alloy was designed with a cluster formula of 12[Al-Ti12](V0.75Mo0.25Ti2)+4[Al-Ti12](Al3)by replacing Ti with Mo/V on the basis of the Ti-Al congruent *** effects of laser power and scanning speed on the molten pool size,surface roughness,relative density,microstructure,and micro-hardness of single-track and bulk Ti-6.38Al-3.87V-2.43Mo samples prepared via laser additive manufacturing(LAM)were *** results show that processing parameters significantly affect the formability,microstructure,and micro-hardness of the *** decreasing laser power from 1,900 W to 1,000 W,the relative density is decreased from 99.86%to 90.91%due to the increase of lack-of-fusion;however,with increasing scanning speed,the relative density does not change significantly,but exceeds 99%.In particular,Ti-6.38Al-3.87V-2.43Mo samples of single-track and bulk exhibit a good formability under an input laser power of 1,900 W and a scanning speed of 8 mm·s_(-1),and display the lowest surface roughness(Ra=13.33μm)and the highest relative density(99.86%).Besides,the microstructure of LAM Ti-6.38Al-3.87V-2.43Mo alloy coarsens with increasing laser power or decreasing scanning speed due to the greater input energy reducing the cooling *** coarsening of the microstructure decreases the microhardness of the alloy.

关键词： laser additive manufacturing composition design cluster-plus-glue-atom model microstructure properties

A 4-aminonaphthalimide based environmentally sensitive fluorescence probe

在线全文

学校读者我要写书评

暂无评论

Chinese Chemical Letters 2013年第5期24卷 359-361页

作者： Zhi-Yong Wu Jing-Nan Cui Xu-Hong Qian tian-yu liu State Key Laboratory of Fine Chemicals Dalian University of Technology Shanghai Key Laboratory of Chemical Biology East China University of Science and Technology

A simply synthesized 4-aminonaphthalimide derivative 1 expresses both polarity and viscosity sensitive fluorescence spectra,indicating its potential usage as an environmentally sensitive fluorescence probe. By comparing the fluorescence behavior of 1 with that of a known 4-aminonaphthalimide derivative 2,it was found that the substitution of the 4-amino group has profound influence on the environmentally sensitive fluorescence properties of 4-aminonaphthalimide.

关键词： 4-Aminonaphthalimide Environmentally sensitive Fluorescence probe Substitution effects

A novel Ti-5.55Al-6.70Zr-1.50V-0.70Mo-3.41Nb-0.21Si alloy designed using cluster-plus-glue-atom model for laser additive manufacturing

在线全文

学校读者我要写书评

暂无评论

中国铸造:英文版 2023年第5期20卷 414-422页

作者： tian-yu liu Yan-chun Lou Shuang Zhang Zhi-hao Zhu Jun Zhao Shi-bing liu Kun Shi Ning Zhao National Key Laboratory of Advanced Casting Technologies Shenyang Research Institute of Foundry Co.Ltd.CAMShenyang 110022China School of Materials Science and Engineering Beihang UniversityBeijing 100191China School of Materials Science and Engineering Dalian Jiaotong UniversityDalian 116028LiaoningChina School of Materials Science and Engineering Dalian University of TechnologyDalian 116024LiaoningChina

A novel Ti-5.55Al-6.70Zr-1.50V-0.70Mo-3.41Nb-0.21Si alloy was designed using the cluster formula approach(cluster-plus-glue-atom model)and prepared by laser melting deposition(LMD).Its composition formula 12[Al-Ti_(12)](AlTi_(2))+5[Al_(0.8)Si_(0.2)-Ti_(12)Zr_(2)](V_(0.8)Mo_(0.2)Nb_(1)Ti)features an enhancedβ-Ti via co-alloying of Zr,V,Mo,Nb and *** experimental results show that the cluster formula ofαandβphases in the novel alloy are respectivelyα-[Al-Ti_(11.5)Zr_(0.5)](Al_(1)Ti_(2))andβ-[Al_(0.8)Si_(0.2)-Ti_(13.2)Zr_(0.8)](V_(1)Mo_(0.4)Nb_(1.6)),both containing Zr *** fitted composition via the α andβphase cluster formulas has little difference with the actual alloy composition,suggesting that the validity of cluster-plus-glue-atom model in the alloy composition *** hot isostatic pressing(HIP),both the Ti-6Al-4V and the novel alloy by LMD are characterized by prior-βcolumnar grains,while the typicaltexture *** with Ti-6Al-4V,Ti-5.55Al-6.70Zr-1.50V-0.70Mo-3.41Nb-0.21Si alloy exhibits a combination of higher strength(1,056 MPa)and higher ductility(14%)at room temperature and higher strength(580 MPa)at 550℃ after HIP,and can potentially serves as LMD materials.

关键词： additive manufacturing laser melting deposition novel titanium alloy composition design cluster-plus-glue-atom model

Corrosion and wear properties of in situ(TiB+TiC)/TA15 composites with a high volume percentage of reinforcement

在线全文

学校读者我要写书评

暂无评论

中国铸造:英文版 2023年第5期20卷 423-431页

作者： Wei-long Wang Kun Shi Jun Zhao Shi-bing liu Jiao-jiao Cheng Wei-chen Qiu tian-yu liu Zhi-yong Zhang Shenyang Research Institute of Foundry Co. Ltd.CAMShenyang 110022China National Key Laboratory of Advanced Casting Technologies Shenyang 110022China

The in situ(TiC+TiB)/TA15 composites with different volume percentages of reinforcement(10%,15%,20%and 25%)were prepared by water-cooled copper crucible vacuum suspension melting *** structures and compositions of the TA15 alloy and its composites were analyzed by XRD and EDS,and their electrochemical corrosion behaviors in the 3.5%NaCl solution were *** wear testing was conducted using a reciprocating ball-on-disc wear tester under a 10 N *** show that the in situ fibrous TiB phase and the granular TiC phase are uniformly distributed on the composite *** microhardness can reach up to 531 HV as 25vol.%TiC+TiB reinforcement is *** with the TA15 alloy,the volume wear rate decreases from(2.21±0.07)×10^(-4)to(1.75±0.07)×10^(-4)mm^(3)·N^(-1)·m^(-1)by adding 15vol.%TiC+TiB reinforcement,and the wear mechanism is adhesive *** the volume percentage of the reinforcement phase reaches 25%,the volume wear rate increases from(1.75±0.07)×10^(-4)to(2.41±0.07)×10^(-4)mm^(3)·N^(-1)·m^(-1),and the wear mechanism changes into abrasive *** volume loss resulted by the interaction between corrosion and wear accounts for more than 27%of the total wear *** volume loss due to wear-induced corrosion changes from 1.94%to 4.06%with different additions of *** volume loss caused by corrosion-induced wear initially increases from 24.08%to 26.90%as the reinforcement increases from 0 to 15%due to the increase of corrosion potential,and then decreases from 26.90%to 25.68%as the reinforcement increases from 15%to 25%due to the peeling of TiC phase.

关键词： titanium matrix composites high volume percentage corrosion wear wear mechanism

Design for Ti-Al-V-Mo-Nb alloys for laser additive manufacturing based on a cluster model and on their microstructure and properties

在线全文

学校读者我要写书评

暂无评论

China Foundry 2021年第4期18卷 424-432页

In this study,α+βTi-Al-V-Mo-Nb alloys with the addition of multiple elements that are suitable for laser additive manufacturing(LAM)were designed according to a Ti-6Al-4V cluster *** formula can be expressed as 12[Al-Ti12](AlTi2)+5[Al-Ti14]((Mo,V,Nb)2Ti),in which Mo and Nb were added into the alloys partially instead of V to give alloys with nominal compositions of Ti-6.01Al-3.13V-1.43Nb,Ti-5.97Al-2.33V-2.93Mo,and Ti-5.97Al-2.33V-2.20Mo-0.71Nb(wt.%).The microstructures and mechanical properties of the as-deposited and heat-treated samples prepared via LAM were *** sizes of theβcolumnar grains andαlaths in the Nb-containing samples are found to be larger than those of the Ti-6Al-4V alloy,whereas Mo-or Mo/Nb-added alloys contain finer *** indicates that Nb gives rise to coarsenedβcolumnar grains andαlaths,while Mo significantly refines ***,the single addition of Nb improves the elongation,whereas the single addition of Mo enhances the strength of the *** simultaneous addition of Mo/Nb significantly improves the comprehensive mechanical properties of the alloys,leading to the best properties with an ultimate tensile strength of 1,070 MPa,a yield strength of 1,004 MPa,an elongation of 9%,and micro-hardness of 355 *** fracture modes of all the alloys are ductile-brittle mixed fracture.

关键词： titanium alloy laser additive manufacturing cluster-plus-glue-atom model composition design microstructure mechanical properties