Fatigue Property of Additively Manufactured Ti-6Al-4V under Nonproportional Multiaxial Loading

Chinese Journal of Mechanical Engineering 2021年第6期34卷 76-84页

作者： Yuya Kimura Fumio Ogawa takamoto itoh Graduate School of Science&Engineering Ritsumeikan UniversityShiga 5258577Japan Fracture and Reliability Research Institute Graduate School of Tohoku UniversityMiyagi 9808579Japan Department of Mechani-cal Engineering Ritsumeikan UniversityShiga 5258577Japan

The low cycle fatigue strength properties of the additively manufactured Ti-6Al-4V alloy are experimentally investi-gated under proportional and nonproportional multiaxial *** fatigue tests were conducted using hollow cylinder specimens with and without heat treatments,at room temperature in *** fatigue tests were conducted:one for proportional loading and one for nonproportional *** proportional loading was represented by a push-pull strain path(PP)and the nonproportional loading by a circle strain path(Cl).The failure lives of the additively manufactured specimens were clearly reduced drastically by internal voids and ***,the sizes of the defects were measured,and the defects were found not to cause a reduction in fatigue strength above a critical *** fracture surface was observed using scanning electron microscopy to investigate the fracture mechanisms of the additively manufactured specimens under the two types of strain *** fracture patterns were recognized for each strain paths;however,both showed retention of the crack propagation,despite the presence of numerous defects,probably because of the interaction of the *** crack propagation properties of the materials with numerous defects under nonproportional multiaxial loading were clarified to increase the reliability of the additively manufactured components.

关键词： Additive manufacturing Ti-6Al-4V Low cycle fatigue Multiaxial stress Nonproportional loading Internal defect

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：