Improvement in hot corrosion resistance of dissimilar alloy 825 and AISI 321 CO2-laser weldment by HVOF coating in aggressive salt environment at 900℃

引用

International Journal of Minerals,Metallurgy and Materials 2020年第11期27卷 1536-1550页

作者： S.M.Muthu M.Arivarasu T.Hari Krishna supriyo ganguly K.V.Phani Prabhakar Saurav Mohanty School of Mechanical Engineering Vellore Institute of TechnologyVelloreTamil Nadu 632014India Center for Innovative Manufacture Research Vellore Institute of TechnologyVelloreTamil Nadu 632014India Welding Engineering and Laser Processing Centre Cranfield UniversityBedfordUnited Kingdom CLPM International Advanced Research Centre for Powder Metallurgy&New Materials(ARCI)HyderabadIndia Department of Mechanical Engineering North Carolina State UniversityRaleighUSA

This study investigated the hot corrosion performance of a dissimilar weldment of Ni-based superalloy and stainless steel joined by CO2-laser welding and improved by high-velocity oxy-fuel(HVOF)coating in a Na2SO4-60wt%V2O5 environment at 900℃.A dissimilar butt joint of AISI 321 and alloy 825 was fabricated by CO2-laser welding with low heat input after obtaining the optimum welding parameters by bead-on-plate *** metallurgical and mechanical properties of the laser weldment were *** tensile test results indicated the occurrence of fracture in the base metal AISI 321 *** HVOF process was employed to coat Ni-20wt%Cr on the *** evaluate the surface morphology of the corrosion products formed on the uncoated and Ni-20wt%Cr-coated weldments,scanning electron microscopy(SEM)analysis was ***-dispersive spectroscopy(EDS)was used to determine the different elements present on the surface *** existence of oxide phases on the weldments was determined by X-ray diffraction(XRD).The cross sections of the weldments were characterized by SEM with EDS line mapping *** results indicated that the Ni-20wt%Cr-coated weldment exhibited superior hot corrosion resistance due to the development of Cr2O3 and NiCr2O4 protective oxide scales.

关键词： nickel-based superalloy dissimilar welding weldment corrosion high-velocity oxy-fuel coating corrosion kinetics

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

Investigation of latest generation pulsed fiber laser in dissimilar joining of Al and Mg alloys

引用

Chinese Optics Letters 2018年第6期16卷 50-53页

作者： Qiong Gao Sonia Meco Kehong Wang Qi Zhou Shun Guo supriyo ganguly School of Material Science and Engineering Nanjing University of Science and Technology Nanjing 210094 China Welding Engineering and Laser Processing Centre Cranfield University Bedford MK43 OAL United Kingdom

Dissimilar metal joining of magnesium to aluminum was investigated using the latest generation nanosecond pulsed fiber laser. The tensile shear test shows that the average tensile shear strength of a joint was 86 MPa,which was 75% of the aluminum substrate. The weld interface exhibited a mixture phase（Mg solid solution and Mg（17）Al（12）） that improves the strength and toughness of the joint. A thin Mg–Al intermetallic compound layer was formed on both sides of the weld seam toward the Al side. Fracture occurred toward the Al substrate side rather than the Mg–Al interface, indicating a high joining strength at the weld interface.

关键词： Fiber lasers High power lasers Laser beams Laser materials processing Pulsed fiber lasers Pulsed operation

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：