Characteristics of Crack Growth in High Performance Concrete Subjected to Fire

Journal of Materials Science & Technology 2005年第1期21卷 118-122页

作者： GaifeiPENG sammyyinninchan JianhuaYAN YefengLIU QuanxinYI FacultyofCivilEngineering&Architecture BeijingJiaoTongUniversityBeijing100044China Wong&ChengConsultingEngineersLtd. HongKongChina BeijingUniversityofTechnology Beijing100022China

An experimental investigation was conducted to identify the characteristics of crack growth in high performance concrete (HPC) subjected to fire, including two parts of work, i.e. crack growth resistance determinations and cracking observations, using concrete of three strength grades 40 MPa, 70 MPa, and 110 MPa. The crack growth resistance curves (R-curves ) of HPC subjected to high temperatures were determined using notched three-point bend beam specimens of 100 mm×100 mm×300mm. The R-curve (crack growth resistance curve) flattening shows that the crack growth resistance has been significantly reduced by elevated temperature. Concrete with a higher strength grade has a steeper R-curve, with a higher fracture toughness but a shorter critical crack growth. The shorter critical crack growth means that concrete of a higher strength grade has a more brittle behavior. The concrete cracking observations reveal that the consequences of rapid heating are quite different from those of slow heating. For slow heating at a rate of 0.5℃/min, HPC suffered no obvious cracking below 600℃ even if it had a high moisture content. Explosive spalling is an extreme case of the internal cracking driven mainly by vapor pressure. All these results confirmed the vapor pressure mechanism for spading behavior which should be more significant for denser concrete. The crack growth ranges obtained from the R-curve determination results are in good agreement with those measured in the concrete cracking observations.

关键词： High performance concrete Fire resistance Explosive spoiling Crack growth Vapor pressure

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：