BEHAVIOR Of SHORT fATIGUE CRACKS AT BLUNT NOTCHES IN A MEDIUM CARBON STEEL

在线全文

学校读者我要写书评

暂无评论

Acta Metallurgica Sinica(English Letters) 1997年第5期10卷 430-436页

作者： Wu, Z.X. sun, X.f. Southwest Jiaotong Univ Chengdu China

The behavior of part-through and through short cracks in single edge blunt notched specimens of a medium carbon steel was investigated by a replication method. It is found that the fatigue failure of these notched specimens is caused mainly by the growth of short surface cracks originating from the surface of notch root. More than 70% of the fatigue life is spent in the regimes in which short surface cracks initiate and propagate as part-through cracks before joining up to form a single through-thickness crack. The effect of original crack profile which is formed through the coalescence of multiple part-through cracks is the main reason causing the 'anomalous' propagation behavior of the through-thickness crack in its early stage.

关键词： Carbon steel Crack initiation Crack propagation fatigue of materials fracture mechanics Surfaces

Relationship between wind-stress coefficient and wave height entropy

在线全文

学校读者我要写书评

暂无评论

Chinese Science Bulletin 1997年第7期42卷 585-588页

作者： Qi, JH sun, f Guo, Pf Physical Oceanography Laboratory Okean University of Qingdao Qingdao China

1 Wind-stress relation THE wind-stress coefficient of sea surface, C_D, is defined

关键词： wind-stress coefficient wave height entropy Charnock coefficient.

Entropy　of　sea　wave　height　field　and　its　annual　variation　in　Northwest　Pacific　Ocean

在线全文

学校读者我要写书评

暂无评论

Acta Oceanologica Sinica 1997年第3期16卷 327-337页

作者： sun f. Gou P. Laboratory of Physical Oceanography Ocean University of Qingdao Qingdao 266003 China Department of Oceanography Ocean University of Qingdao Qingdao 266003 China

ＥｎｔｒｏｐｙｏｆｓｅａｗａｖｅｈｅｉｇｈｔｆｉｅｌｄａｎｄｉｔｓａｎｎｕａｌｖａｒｉａｔｉｏｎｉｎＮｏｒｔｈｗｅｓｔＰａｃｉｆｉｃＯｃｅａｎＳｕｎＦｕａｎｄＧｕｏＰｅｉｆａｎｇ（ＲｅｃｅｉｖｅｄＯｃｔｏｂｅｒ６，１... 详细信息

ＥｎｔｒｏｐｙｏｆｓｅａｗａｖｅｈｅｉｇｈｔｆｉｅｌｄａｎｄｉｔｓａｎｎｕａｌｖａｒｉａｔｉｏｎｉｎＮｏｒｔｈｗｅｓｔＰａｃｉｆｉｃＯｃｅａｎＳｕｎＦｕａｎｄＧｕｏＰｅｉｆａｎｇ（ＲｅｃｅｉｖｅｄＯｃｔｏｂｅｒ６，１９９５；ａｃｃｅｐｔｅｄＯｃｔｏｂ...

关键词： wave height sea field Northwest Entropy

STUDY ON THE VARIATION MECHANISM Of CARBON CONTENT Of LIQUID IRON IN MELTING GASIfIER

在线全文

学校读者我要写书评

暂无评论

Acta Metallurgica Sinica(English Letters) 2003年第2期16卷 132-138页

作者： Q.Lu L.f sun Y.Xu Q.f.Chan Hebei University of Technology Tangshan 063009ChinaHebei University of TechnologyTangshan 063009ChinaHebei University of TechnologyTangshan 063009ChinaHebei Institute of Vocation and TechnologvShiiiazhuang 050031China

This paper studied the changing principles of carbon content in direct reduction iron (DRI) and liquid iron in the COREX melting gasifier. Under the normal working conditions of experimental equipment, liquid nitrogen was poured into the melting gasifier from its tuyere to cool down quickly. And then seven cross sections were made to study the carburization reaction and its characteristics of the solid iron and the liquid iron, and also the reaction of carbon between the slag and the metal. According to the results, the influences of the thickness of the semi-coke layer and the temperature on the carbon content of liquid iron in the COREX melting gasifier were confirmed.

关键词： melting gasifier direct reduction iron (DRI) liquid iron carbon content

friction stir spot welding of SPCC low carbon steel plates at extremely low welding temperature

在线全文

学校读者我要写书评

暂无评论

Journal of Materials Science & Technology 2019年第5期35卷 733-741页

作者： Y.f.sun H.fujii Y.Sato Y.Morisada Joining and Welding Research Institute Osaka University 11-1 Mihogaoka Ibaraki 567-004Japan School of Materials Science and Engineering Zhengzhou University Zhengzhou 450001 China

friction stir spot welding (fSSW) was applied to 2.0 mm thick steel plate cold-rolled commercial (SPCC) low carbon steel plates at a very low rotation speed that ranged from 5 to 50rpm, which was much lower than that generally used for the conventional fSSW technique. Due to the very low heat input, the welding processes could therefore be completed at a peak welding temperature below 160℃. As a result, a significantly refined microstructure with an average grain size of about 0.41μm was formed in the stir zone of the joints and the JI {0-11 } and J2{1-1O} shear textures were the dominant components, which are different from the D1{11-2} and D2{-1-12} shear textures formed in the conventional fSSW joints. In addition, no heat affected zone could be detected along the crosssectional plane of the joints. Although a few void-like non-bonded areas were still observed along the interface between the upper and lower steel plates, the shear tensile loads of the joints increased to about 10.0 kN when welded at a condition of 8t, 20rpm and 30 s, and the joints fractured through the plug failure mode.

关键词： friction stir spot welding Dynamic recrystallization Microstructure Steel

Effect of post-bond heat treatment on the microstructure and high temperature mechanical property of a TLP bonded γ'-strengthened co-based single crystal superalloy

在线全文

学校读者我要写书评

暂无评论

Journal of Materials Science & Technology 2021年第21期80卷 244-258页

作者： S.Y.Wang Y.sun C.Y.Cui X.f.sun Y.Z Zhou Y.M.Ma H.L.An Institute of Metal Research Chinese Academy of SciencesShenyang 110016China School of Materials Science and Engineering University of Science and Technology of ChinaHefei 230026China Harbin Welding Institute China Academy of Machinery Science and TechnologyHarbin 150028China

Post-bond heat treatment(PBHT) applied to a transient liquid phase(TLP) bonding joint is an effective approach to remove the brittle borides and improve its ***,we proposed two types of PBHT strategies to obtain a TLP bonded γ'-strengthened Co-based single crystal superalloy,and the microstructural characteristics and tensile properties of the two heat treated joints were compared to identify the optimal PBHT *** evolution of the brittle boride in the joint after the PBHT was studied by using in-situ *** experimental results allowed to provide a theoretic model to quantitatively evaluate the distribution of the brittle phase after the optimal PBHT and analyze the joint fractures to understand the failure *** obtained results revealed that a post-bond solid solution treatment performed to the joint at a high temperature(over 1275℃) could decrease the area fraction of the boride from 7.2 % to 1.4 % and increase the elongation from 1.9 % to 7.8 %.This work emphasizes the relevance of solid solution temperature when a PBHT strategy is applied.

关键词： Transient liquid phase(TLP) γ'-strengthened co-based single crystal superalloy Heat treatment sequence Brittle boride Tensile property

IMPROVED METHOD Of PARTIAL SIMILARITY Of BOUNDARY LAYER ALONG CURVED SURfACE

在线全文

学校读者我要写书评

暂无评论

Journal of Hydrodynamics 2001年第2期13卷 77-79页

作者： sun, f.Z. Shi, Y.T. sun, H.J. Ping, Y.M. Zhang, M.Y. Inst. of Energy and Power Shandong Univ. Jinan 250061 China

The solution of boundary layer along a curved surface was discussed in this article. According to the principle of the theory of similarity, the method of partial similarity was proposed, in which the profile of object is divided into many tiny sections, the method of similarity was used in each section and the error in each section was fully considered. This method is proved to be feasible.

关键词： Cylinders (shapes) Differential equations Error analysis Surfaces

Nonlinear mechanics of a ring structure subjected to multi-pairs of evenly distributed equal radial forces

在线全文

学校读者我要写书评

暂无评论

Acta Mechanica Sinica 2017年第5期33卷 942-953页

作者： Q. Chen f. sun Z. Y. Li L. Taxis N. Pugno Biomechanics Laboratory School of Biological Science and Medical Engineering Southeast University State Key Laboratory of Mechanics and Control of Mechanical Structures Nanjing University of Aeronautics and Astronautics School of Chemistry Physics and Mechanical EngineeringQueensland University of Technology (QUT) Laboratory of Bio-Inspired and Graphene Nanomechanics Department of Civil Environmental and Mechanical Engineering University of Trento School of Engineering and Materials Science Queen Mary University of London Ket Lab Italian Space Agency Via del Politecnico snc

Combining the elastica theory, finite element (fE) analysis, and a geometrical topological experiment, we studied the mechanical behavior of a ring subjected to multi-pairs of evenly distributed equal radial forces by looking at its seven distinct states. The results showed that the theoretical predictions of the ring deformation and strain energy matched the fE results very well, and that the ring deformations were comparable to the topological experiment. Moreover, no matter whether the ring was compressed or tensioned by N-pairs of forces, the ring always tended to be regular polygons with 2N sides as the force increased, and a proper compressive force deformed the ring into exquisite flower-like patterns. The present study solves a basic mechanical problem of a ring subjected to lateral forces, which can be useful for studying the relevant mechanical behavior of ring structures from the nano- to the macro-scale.

关键词： Ring structures Mechanical properties Shape Strain energy

Evaluation of dynamic development of grain structure during friction stir welding of pure copper using a quasi in situ method

在线全文

学校读者我要写书评

暂无评论

Journal of Materials Science & Technology 2019年第7期35卷 1412-1421页

作者： X.C.Liu Y.f.sun T.Nagira K.Ushioda H.fujii Joining and Welding Research Institute Osaka University11-1 MihogaokaIbarakiOsaka567-0047Japan School of Materials Science and Engineering Northwestern Polytechnical UniversityXi'an710072China School of Materials Science and Engineering Zhengzhou UniversityZhengzhou450001China

By employing a quasi in situ method, we investigated the dynamic evolution of the grain structure con-sidering the material flow, strain, and strain rate in the friction stir welding of pure copper. The tool' stop action' and rapid cooling were employed and a brass foil was used as a marker to show the material flow path. The grain structure along the material flow path was characterised using electron backscatter diffraction. Static recrystallization occurs for the work-hardened base material in the preheating stage in front of the tool In the acceleration flow stage, grains are significantly refined by plastic deforma-tion, discontinuous dynamic recrystallization, annealing twinning during the strain-induced boundary migration and slight continuous dynamic recrystallization. In the deceleration flow stage, due to a strain reversal, the grain first coarsens, and is thereafter refined again. finally, the hot-deformed material in the shoulder-affected zone is ‘frozen’ directly whereas that in the probe-affected zone undergoes signif-icant annealing;thus, the recrystallized microstructure and 45°-rotated cube texture are obtained in the probe-affected zone.

关键词： friction stir welding Grain structure Material flow Pure copper EBSD