Surface characteristics of chemical conversion coating for Mg-Al alloy

在线全文

学校读者我要写书评

暂无评论

中国有色金属学会会刊：英文版 2009年第4期19卷 892-897页

作者： Masazumi OKIDO ryoichi ichino Seong-Jong KIM Seok-Ki JANG Nagoya University Division of Marine Engineering Mokpo Maritime University

The chemical conversion coating was formed on Mg alloy for low cost and harmlessness in environment by using the colloidal silica as the main *** film formed at 298 K was thick,which was thought to be the combination of Si and *** salt spray test,the ratio of black rust on the specimen that did not conducted chemical conversion treatment was five times or more than those of the chemical conversion treated *** film of chemical conversion coating produced by alkali treatment process was thinner than the specimen produced in basic chemical conversion treatment solution.

关键词：化学转化膜镁铝合金表面特性环境无害化盐雾试验涂膜厚度低成本硅溶胶

Electrochemical characteristics and surface morphology in non-chromate chemical conversion coating for Zn-electroplated steel sheets

在线全文

学校读者我要写书评

暂无评论

中国有色金属学会会刊：英文版 2009年第B9期19卷 45-49页

作者： Masazumi OKIDO ryoichi ichino Seok-Ki JANG Seong-Jong KIM Graduate School of Engineering Nagoya University Division of Marine Engineering Mokpo Maritime University

The corrosion protection property and morphology of colloidal silica conversion films as an alternative to chemical conversion coating(CCC) films were examined. The corrosion behavior was investigated in 3% NaCl solution using electrochemical techniques. Corrosion was implied by the appearance of red rust on the specimen surface. The results show that in 3% NaCl solution, red rust appears at 15-20, 55-70, and 75-85 d on Zn-electroplated steel, colloidal silica conversion-coated specimens, and chemical conversion-coated, specimens, respectively. In the salt spray test, the colloidal silica film provides better corrosion protection than CCC film, i.e., red rust appears at 96 h on the Zn-electroplated steel sheet, at 432 h on the CCC films, and at 888 h on silica conversion coating.

关键词：化学转化膜电镀钢板表面形貌电化学特性 3%NaCl溶液胶体二氧化硅二氧化硅薄膜 CCC认证

Effect of Additives on Bi electrodeposition

在线全文

学校读者我要写书评

暂无评论

Effect of Additives on Bi electrodeposition

Osteoconductivity of Superhydrophilic Anodized TiO<sub>2</sub>Coatings on Ti Treated with Hydrothermal Processes

2006年上海电子电镀学术报告会

作者： Hitoshi Wada ryoichi ichino Masazumi Okido Department of Materials Science and Engineering Graduate School of Engineering Nagoya University Furo-cho Chikusa-ku Nagoya 464-8603 Japan Department of Materials Science and Engineering Graduate School of Engineering Nagoya University Furo-cho Chikusa-ku Nagoya 464-8603 Japan Department of Materials Science and Engineering Graduate School of Engineering Nagoya University Furo-cho Chikusa-ku Nagoya 464-8603 Japan

＜正＞Lead has been uscd in many industrial ficlds by its good characteristics such as malleability, corrosion resistance and the low melting point. However, the use of lead is strongly limited because it is harmful to the living bodies and the environment. Bismuth has a low melting point near that of lead and the other characteristics is also similar to these of lead. Bismuth is, however, little influence on the human body and the environment. In this paper, we have

关键词：

来源： cnki会议评论

在线全文

cnki会议

学校读者我要写书评

暂无评论

Journal of Biomaterials and Nanobiotechnology 2013年第1期4卷 45-52页

作者： Dai Yamamoto Kazushi Arii Kensuke Kuroda ryoichi ichino Masazumi Okido Azusa Seki Department of Materials Science & Engineering Graduate School of Engineering Nagoya University Nagoya Japan EcoTopia Science Institute Nagoya University Nagoya Japan Hamri Co. Ltd. Tokyo Japan

Surface hydrophilicity is considered to have a strong influence on the biological reactions of bone-substituting materials. However, the influence of a hydrophilic surface on osteoconductivity is not completely clear, especially for superhydrophilic surfaces. In this study, we conferred superhydrophilic properties on anodized TiO2 coatings using a hydrothermal treatment, and developed a method to maintain this surface until implantation. The osteoconductivity of these coatings was evaluated with in vivo tests. A hydrothermal treatment made the surface of as-anodized samples more hydrophilic, up to a water contact angle of 13 (deg.). Storage in both air and distilled water increased the water contact angle after several days because of the adsorption of hydrocarbon. However, storage in phosphate buffered solution led to a reduction in the water contact angle, because of the adsorption of the inorganic ions in the solution, and the sample retained its high hydrophilicity for a long time. As the water contact angle decreased, the hard tissue formation ratio increased continuously up to 58%, which was about four times higher than the hard tissue formation ratio on as-polished Ti.

关键词： Titanium Anodizing Superhydrophilic Hydrothermal Treatment Phosphate Buffered Saline Osteoconductivity

Influence of Alloy Elements on the Osteoconductivity of Anodized Ti-29Nb-13Ta-4.6Zr Alloy

维普期刊数据库评论

在线全文

维普期刊数据库

学校读者我要写书评

暂无评论

Journal of Biomaterials and Nanobiotechnology 2013年第3期4卷 229-236页

作者： Dai Yamamoto Atsushi Waki Kensuke Kuroda ryoichi ichino Masazumi Okido Masato Ueda Masahiko Ikeda Mitsuo Niinomi Azusa Seki Department of Materials Science & Engineering Graduate School of Engineering Nagoya University Nagoya Japan EcoTopia Science Institute Nagoya University Nagoya Japan Faculty of Chemistry Materials and Bioengineering Kansai University Suita Japan Hamri Co. Ltd. Tokyo Japan Institute for Materials Research Tohoku University Sendai Japan

Anodizing is expected to be an effective method to improve the osteoconductivity of the Ti-29Nb-13Ta-4.6Zr (TNTZ) alloy because the bioactivity of anodized Ti is good. However, it is not known how the alloy elements influence the surface roughness, composition, hydrophilicity, and osteoconductivity of the anodized film on the Ti alloy. In this study, we investigated the effects of anodizing on the surface properties and the osteoconductivity of the anodized TNTZ alloy, focusing on the functions of the individual alloy elements. The anodized oxides of the Nb, Ta, and Zr metals were hydrophobic at all the voltages applied, in contrast to the anodized oxide of Ti. As well as pure Ti, a TiO2-based oxide film formed on TNTZ after anodizing. However, the oxide film also contained large amounts of Nb species and the molar Nb/Ti ratio in the TNTZ alloy was high, which makes the surface more hydrophobic than the anodized oxide on Ti. In vivo tests showed that the osteoconductivity of the TNTZ alloy was sensitive to both its surface roughness and hydrophilicity. When the TNTZ alloy was anodized, the process increased either the surface hydrophobicity or the surface roughness at the voltage used in this study. These changes in the surface properties did not improve its osteoconductivity.

关键词： Ti-29Nb-13Ta-4.6Zr Anodizing Titanium Dioxide Alloy Element Hydrophilicity Osteoconductivity

NaBH_4的水性还原法制备纳米铜颗粒(英文)

维普期刊数据库评论

在线全文

维普期刊数据库

学校读者我要写书评

暂无评论

Transactions of Nonferrous Metals Society of China 2012年第1期22卷 117-123页

作者：刘清明周德璧山本雄也市野良一兴户正纯中南大学化学化工学院中国长沙410083 名古屋大学工学研究科日本名古屋4648603

在碱性溶液中用NaBH4还原Cu2+制备纳米铜颗粒,研究NaBH4浓度和滴加速率对Cu纳米颗粒制备的影响。反应的最佳条件是:0.2mol/LCu2+,溶液pH12,温度313K,1%明胶作为分散剂,将0.4mol/LNaBH4溶液以50mL/min的速率加入CuSO4溶液中。氨水是最佳... 详细信息

在碱性溶液中用NaBH4还原Cu2+制备纳米铜颗粒,研究NaBH4浓度和滴加速率对Cu纳米颗粒制备的影响。反应的最佳条件是:0.2mol/LCu2+,溶液pH12,温度313K,1%明胶作为分散剂,将0.4mol/LNaBH4溶液以50mL/min的速率加入CuSO4溶液中。氨水是最佳的络合剂。采用一系列实验研究不同时间点的反应进程。

关键词：纳米铜颗粒水性还原法前驱体反应进程

在线全文

学校读者我要写书评

暂无评论

电化学沉积生物陶瓷新方法

稀有金属与硬质合金 2002年第1期30卷 6-8页

作者：赵中伟李洪桂孙培梅李运姣霍广生兴户正纯市野良一中南大学冶金科学与工程系湖南长沙410083 名古屋大学工学部

在钛基板上电沉积了致密的、结合良好的磷酸钙生物陶瓷膜。在 5 5℃下使用含钙离子 0 0 1mol/dm3 ,磷酸根离子 0 0 0 6mol/dm3 ,NaCl浓度为 0 14 5mol/dm3 的溶液 ,考察了添加H2 O2 的影响。无论使用H2 O2 与否 ,所得的沉积物均为羟... 详细信息

在钛基板上电沉积了致密的、结合良好的磷酸钙生物陶瓷膜。在 5 5℃下使用含钙离子 0 0 1mol/dm3 ,磷酸根离子 0 0 0 6mol/dm3 ,NaCl浓度为 0 14 5mol/dm3 的溶液 ,考察了添加H2 O2 的影响。无论使用H2 O2 与否 ,所得的沉积物均为羟基磷灰石 (hydroxyapatite,HAp) ,但是在使用H2 O2 时 ,阴极电位约为 - 0 2V(vsSCE)即开始有阴极电流 ,而且没有氢气析出。与此形成对照的是在不使用H2 O2 时 ,需要极化到 - 1.4V(vsSCE)才有阴极电流 ,并且伴随着大量氢气析出。H2 O2

关键词：电化学沉积生物陶瓷羟基磷灰石包覆双氧水薄膜