Influence of Al Content on the Atmospheric Corrosion Behaviour of Magnesium-Aluminum Alloys

维普期刊数据库评论

在线全文

维普期刊数据库

学校读者我要写书评

暂无评论

Journal of Materials Science & Technology 2009年第2期25卷 225-229页

作者： ruiling jia Chuanwei Yan Fuhui Wang College of Materials Science ＆ Chemistry Engineering Key Laboratory of Superlight Materials and Surface Technology Ministry of Education Harbin Engineering University Harbin 150001 China State Key Laboratory for Corrosion and Protection Institute of Metal Research Chinese Academy of Sciences Shenyang 110016 China College of Materials Science ＆ Engineering Inner Mongolia University of Technology Hohhot 010051 China

The influence of AI content on the Mg-AI alloys corrosion performance during sodium chloride induced atmospheric corrosion has been studied. It was found that the corrosion rate of three Mg-AI alloys was accelerated with increasing AI content. The poor corrosion resistance was attributed to the galvanic coupling between the phase and eutectic phase or α phase and the formation of porous corrosion products.

关键词： Magnesium alloys Al content Atmospheric corrosion

Effect of Intermetallic Phases on Corrosion Initiation of AZ91 Alloy With Rare Earth Y Addition

在线全文

学校读者我要写书评

暂无评论

Journal of Materials Science & Technology 2015年第5期31卷 504-511页

作者： Li-na Zhang ruiling jia Dan Li Wei Zhang Feng Guo School of Materials Science and Engineering Inner Mongolia University of Technology State Key Laboratory for Corrosion and Protection Institute of Metal ResearchChinese Academy of Sciences

The effect of the rare earth（RE） element Y on the microstructure of AZ91 Mg alloy is investigated.A detailed description of the procedure of identifying the intermetallic phases containing Y in the AZ91 Mg alloy with 0.9 wt%Y addition is *** results shows that there are two different kinds of RE phases in scanning electron microscopy（SEM） *** dispersive spectrum（EDS） analysis shows that one is rich in Y element and the other is rich in Mn *** to the element mapping of electron probe microanalysis（EPMA）.the element Al can be found not only in the β-Mg17Al12phase but also in these two RE phases.X-ray diffraction（XRD） and transmission electron microscopy（TEM） results further confirm one of the two RE phases is AI2Y;the phase of Al10Mn2Y has just been determined by transmission electron microscopy（TEM） instead of XRD probably because it is *** shapes of these two RE intermetallic phases are pretty *** 3D digital microscopy is employed to observe in-situ the effect of the(5 phase and the above two RE intermetallic phases on the corrosion initiation of the *** results show that the corrosion attack of AZ91 Mg alloy without Y addition starts around the eutectic phase β-*** the addition of 0.9 wt%Y,the two kinds of Y-rich intermetallic phases act as cathodic effect and a phase in the adjacent of them was activated and cathodic effect of the β-Mg17Al12phase was inhibited.

关键词： Mg alloy Yttrium Intermetallic phase Corrosion ini

Indiscriminate Dietary Compositions of Two Asian Horseshoe Crabs,Tachypleus tridentatus and Carcinoscorpius rotundicauda:Evidence from Hemolymph Stable Isotopes

在线全文

学校读者我要写书评

暂无评论

Journal of Ocean University of China 2022年第3期21卷 583-590页

作者： LI Yuhong FENG jianxiang KWAN Kit Yue TAN Yiran WENG Bosen jia ruiling Department of Environmental Science and Engineering Huaqiao UniversityXiamen361021China School of Marine Sciences Sun Yat-sen UniversityZhuhai519082China College of Marine Sciences Beibu Gulf UniversityQinzhou535011China

Knowledge of dietary compositions is essential to the recovery of the dwindling populations of horseshoe crabs in *** feeding habits of Tachypleus tridentatus and Carcinoscorpis rotundicauda of Pearl Bay in southwestern China were studied by stable isotope *** samples of the two species were obtained from two age groups living in different habitats(inner,central,and outer Bay).In addition,their potential food source samples were collected in May *** showed that the mean values ofδ^(13)C andδ^(15)N in *** individuals ranged from−19.01‰to−16.47‰and from 10.49‰to 13.5‰,respectively,and those of *** ranged from−19.12‰to−14.96‰and from 8.78‰to 13.48‰,*** values indicated that the horseshoe crabs have a wide variety of food sources and therefore are highly *** remarkably correlations were found betweenδ^(13)C andδ^(15)N values and individual widths in the two *** potential food sources were selected,in which Sipunculus nudus,Batillaria zonalisi,and Ulva lactuca contributed largely to the dietary compositions of the two species of horseshoe *** significant correlation was found between the feeding habits and habitat geochemical characteristics of the horseshoe *** these results possibly indicate the high diversity of their food sources and the indiscriminate dietary compositions of the two Asian horseshoe crabs.

关键词： Tachypleus tridentatus Carcinoscorpius rotundicauda stable isotope hemolymph growth stage

基于表型性状的干旱半干旱区谷子骨干种质构建

在线全文

学校读者我要写书评

暂无评论

干旱地区农业研究 2025年第1期43卷 21-31页

作者：赵小琴贾瑞玲刘军秀文殷花刘彦明师丽丽张娟宁马宁定西市农业科学研究院甘肃定西743000

以871份谷子种质资源为材料,基于植物学类型分组,平方根法确定取样量,组内按17个表型数据进行UPGMA聚类分析,类内随机取样构建骨干种质;同时通过t检验、F测验、卡方测验、表型保留比例等对骨干种质代表性进行检验和评价;并利用主成分分... 详细信息

以871份谷子种质资源为材料,基于植物学类型分组,平方根法确定取样量,组内按17个表型数据进行UPGMA聚类分析,类内随机取样构建骨干种质;同时通过t检验、F测验、卡方测验、表型保留比例等对骨干种质代表性进行检验和评价;并利用主成分分析和直方图对骨干种质进行确认,共构建包含85份种质的干旱半干旱地区谷子骨干种质,占全部资源的9.8%,包括白粒21份、黄粒49份、橙粒3份、青粒5份、红粒4份、黑粒2份和褐粒1份。显著性分析结果表明,谷子骨干种质17个性状与全部种质之间的方差(P=0.047~0.986)、变异系数(0.965)、香农多样性指数(0.873)差异均不显著(P>0.05);且骨干种质保留了全部种质的分布范围、表型保留比例(0.812~1.402);相关性分析结果表明,骨干种质较好地保持了全部种质各性状间的遗传关联和分布频率。综上可知,构建的干旱半干旱区谷子骨干种质既能代表全部种质的遗传变异又减小了全部种质的遗传群体,可为谷子资源评价、种质创新和新品种选育奠定良好的基础。

关键词：谷子表型性状骨干种质取样策略代表性评价干旱半干旱区

同方期刊数据库

在线全文

学校读者我要写书评

暂无评论

甜荞种质资源抗倒性评价及鉴定指标筛选

植物遗传资源学报 2025年第1期26卷 120-132页

作者：贾瑞玲赵小琴陈富刘彦明南铭马宁张娟宁陈丽萍向达兵刘军秀定西市农业科学研究院甘肃定西743000 甘肃省农业科学院作物研究所兰州730070 安定区凤翔镇政府甘肃定西743000 成都大学食品与生物工程学院成都610106

倒伏是影响甘肃中部甜荞产量的重要因素。本研究以76份国内外甜荞种质资源为试验材料,通过计算23个与抗倒伏密切相关的性状的遗传多样性,应用相关性分析、主成分分析、回归分析、聚类分析及逐步判别分析等方法,对甜荞种质资源抗倒性进... 详细信息

倒伏是影响甘肃中部甜荞产量的重要因素。本研究以76份国内外甜荞种质资源为试验材料,通过计算23个与抗倒伏密切相关的性状的遗传多样性,应用相关性分析、主成分分析、回归分析、聚类分析及逐步判别分析等方法,对甜荞种质资源抗倒性进行综合评价。结果表明,76份甜荞种质材料的遗传多样性较高,不同性状的遗传多样性指数分布范围为2.349~4.331,其中,主茎第二节间长最大,主茎分枝数最小。相关性分析表明,23个性状之间存在着不同程度的相关性。主成分分析表明,前5个主成分能够代表76份甜荞种质23个性状81.421%的信息量。利用隶属函数法计算甜荞种质资源抗倒性综合得分值(D值),D值平均为0.469,云甜荞1号D值最低(0.200),TQ10-07 D值最高(0.819)。通过逐步回归分析,筛选出株高、茎秆重心高度、主茎第一节间长及壁厚、主茎第二节间长、主茎分枝数、弯曲度和茎秆抗折力等8个性状可作为甜荞种质资源抗倒性的综合评价指标。聚类分析将76份供试材料分为4个类群,其中类群Ⅳ的10份材料D值最高,抗倒伏能力最强,可作为种质创新及抗倒育种的亲本材料。本研究表明采用多元化统计分析方法对甜荞种质资源抗倒性进行综合评价是可行的,为甘肃中部地区甜荞种质创新和抗倒伏育种提供依据和借鉴。

关键词：甜荞旱作区茎秆抗倒性综合评价

(Gd,Y)相对GW103K时效合金局部腐蚀的影响

在线全文

学校读者我要写书评

暂无评论

材料研究学报 2019年第3期33卷 199-208页

作者：于爽贾瑞灵张函张伟郭锋内蒙古工业大学材料科学与工程学院内蒙古薄膜与涂层重点实验室呼和浩特010051 中国科学院金属研究所金属腐蚀与防护实验室沈阳110016

对Mg-10Gd-3Y-0.4Zr(GW103K)合金进行193 h时效处理,使用扫描电子显微镜(SEM)和透射电子显微镜(TEM)观测块状和链状相的微观结构和腐蚀形貌,使用扫描开尔文探针显微镜(SKPFM)测试块状相和链状相与基体之间的相对电势差,研究了这些相对GW... 详细信息

对Mg-10Gd-3Y-0.4Zr(GW103K)合金进行193 h时效处理,使用扫描电子显微镜(SEM)和透射电子显微镜(TEM)观测块状和链状相的微观结构和腐蚀形貌,使用扫描开尔文探针显微镜(SKPFM)测试块状相和链状相与基体之间的相对电势差,研究了这些相对GW103K合金局部腐蚀的影响。结果表明:分布在晶内和晶界的单独块状相为Mg2(Gd, Y)相,(Gd, Y)固溶体与Mg2(Gd, Y)相交替排列形成链状相。(Gd, Y)固溶体和Mg2(Gd, Y)相的相对电势均高于基体,与相邻基体形成微电池,(Gd, Y)固溶体和Mg2(Gd, Y)相作为阴极促进了周围基体的腐蚀。尽管(Gd,Y)固溶体与基体之间的相对电势差更大,但是与基体的相界面为共格界面,界面能低、化学稳定性高,因此对基体腐蚀没有更强烈的影响。

关键词：金属材料镁合金腐蚀微电偶 SKPFM (Gd,Y)相相对电势

Al含量对镁铝合金大气腐蚀产物膜结构与性能的影响

在线全文

学校读者我要写书评

暂无评论

材料研究学报 2007年第5期21卷 471-476页

作者：贾瑞灵严川伟王福会哈尔滨工程大学材料科学与化学工程学院中国科学院金属研究所金属腐蚀与防护国家重点实验室沈阳110016

采用X射线衍射(XRD)和扫描电镜能谱(EDS)面扫描分析技术,研究了Al含量对实验室模拟的潮湿大气中由NaCl盐粒诱发的3种镁合金腐蚀产物膜结构和成分的影响.结果表明,腐蚀产物主要为Mg(OH)_2和Mg_2(OH)_3Cl·4H_2O,随着合金中Al含量的增加,... 详细信息

采用X射线衍射(XRD)和扫描电镜能谱(EDS)面扫描分析技术,研究了Al含量对实验室模拟的潮湿大气中由NaCl盐粒诱发的3种镁合金腐蚀产物膜结构和成分的影响.结果表明,腐蚀产物主要为Mg(OH)_2和Mg_2(OH)_3Cl·4H_2O,随着合金中Al含量的增加,腐蚀产物中Al参与生成的产物增多,但腐蚀产物膜的结构变得疏松多孔.采用电化学交流阻抗(EIS)测试了膜层的保护性.结果表明,3种不同Al含量镁合金腐蚀产物膜的保护性能均随着暴露时间的延长而提高;在相同的暴露时间内,镁合金中Al含量越高,腐蚀产物膜的阻抗值愈小,膜层的保护性愈差.其原因是Al的含量越高,腐蚀产物膜的结构变得愈加疏松和多孔.

关键词：材料失效与保护镁合金大气腐蚀产物交流阻抗

稀土对AZ91镁合金干湿交替循环腐蚀行为的影响

在线全文

学校读者我要写书评

暂无评论

稀有金属材料与工程 2017年第7期46卷 1893-1899页

作者：周伟光贾瑞灵张贵龙郭锋张伟内蒙古工业大学内蒙古呼和浩特010051 中国科学院金属研究所辽宁沈阳110016

镧铈(La,Ce)混合稀土的添加改变了AZ91镁合金微观组织和元素分布。La元素与Ce元素在AZ91镁合金中以不同的形式存在,一部分固溶在镁合金基体中,一部分参与生成了针状的Al4(La,Ce)相和粒状的Al_(10)Ce_2Mn_7相。稀土添加后AZ91镁合金中β... 详细信息

镧铈(La,Ce)混合稀土的添加改变了AZ91镁合金微观组织和元素分布。La元素与Ce元素在AZ91镁合金中以不同的形式存在,一部分固溶在镁合金基体中,一部分参与生成了针状的Al4(La,Ce)相和粒状的Al_(10)Ce_2Mn_7相。稀土添加后AZ91镁合金中β相的体积分数有所降低,Al元素分布由晶界向晶内迁移。对不同添加量的稀土镁合金在模拟融雪剂溶液中的干湿交替循环腐蚀行为的研究结果表明,La、Ce混合稀土的添加,可以增加镁合金表面膜的致密度。虽然混合稀土降低了镁合金的自腐蚀电位,但腐蚀电流密度相比较于AZ91明显降低。SECM结果则表明,稀土添加可以减少镁合金表面微区的活性点数量。

关键词：镁合金稀土腐蚀干湿交替

2009—2019年中国期刊发表的皮肤疾病临床指南报告质量评价

在线全文

学校读者我要写书评

暂无评论

中华皮肤科杂志 2021年第3期54卷 236-241页

作者：王禹毅贾瑞玲林茂刁庆春重庆市中医院皮肤科 400011

目的评价我国期刊发表的皮肤疾病临床指南的报告质量。方法计算机检索中国知网、维普医药、万方医学、中国生物医药数据库,检索日期为2009年1月至2019年10月,收集在我国期刊上公开发表的皮肤疾病临床指南。由2位评价员独立筛选文献,提... 详细信息

目的评价我国期刊发表的皮肤疾病临床指南的报告质量。方法计算机检索中国知网、维普医药、万方医学、中国生物医药数据库,检索日期为2009年1月至2019年10月,收集在我国期刊上公开发表的皮肤疾病临床指南。由2位评价员独立筛选文献,提取资料并交叉核对。使用临床实践指南报告标准(RIGHT)评价指南质量,采用Excel 2017对数据进行统计分析。结果共纳入17篇皮肤疾病临床指南,包括13篇西医指南和4篇中医指南。13篇西医指南中,RIGHT标准的7个评价领域即基本信息、背景、证据、推荐意见、评审和质量保证、资助与利益冲突、其他方面的报告篇数分别为9、6、0、4、0、1、1;4篇中医指南中,上述领域报告篇数分别为4、3、3、3、3、2、2。结论近10年我国期刊发表的皮肤疾病临床指南总体报告质量具有较大进步空间,建议在以后指南制订过程中参考RIGHT规范加强报告质量。

关键词：指南皮肤 RIGHT 报告质量