Casting fluidity,viscosity,microstructure and tensile properties of aluminum matrix composites with different Mg_(2)Si contents

引用

Rare Metals 2022年第8期41卷 2767-2776页

作者： reza vatankhah barenji Department of Industrial Engineering Hacettepe UniveristyBeytepe Campus06800AnkaraTurkey

The effect of Mg_(2)Si amount on the properties of Al-Mg_(2)Si as-cast composites was investigated in this *** with different amounts of Mg_(2)Si(15 wt%,20 wt%and 25 wt%)were fabricated,and the fluidity,viscosity,porosity formation and tensile properties were then *** addition,optical microscope and scanning electron microscope were used for micros tructural studies and *** results reveal that with the amount of Mg_(2)Si increasing,the morphology of the primary Mg_(2)Si becomes irregular,the size of primary Mg_(2)Si increases,fluidity decreases,viscosity increases,and porosity amount *** reason for the higher amounts of porosities is the lower fluidity and higher *** addition,Al-15%Mg_(2)Si shows better tensile properties and higher quality index compared to other ***,the fracture surface of the composite with lower Mg_(2)Si amount reveals more ductile mode than those with higher Mg_(2)Si amount.

关键词： Al-Mg_(2)Si Microstructure Fluidity Tensile behavior Porosity

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

Effect of reinforcement amount, mold temperature, superheat, and mold thickness on fluidity of in-situ Al-Mg_2Si composites

引用

China Foundry 2018年第1期15卷 66-74页

作者： reza vatankhah barenji Department of lndustrial Engineering Hacettepe University Beytepe Campus Ankara 06800 Turkey

In the present study, the effects of mold temperature, superheat, mold thickness, and Mg_2Si amount on the fluidity of the Al-Mg_2Si as-cast in-situ composites were investigated using the mathematical models. Composites with different amounts of Mg_2Si were fabricated, and the fluidity and microstructure of each were then analyzed. For this purpose, the experiments were designed using a central composite rotatable design, and the relationship between parameters and fluidity were developed using the response surface method. In addition, optical and scanning electron microscopes were used for microstructural observation. The ANOVA shows that the mathematical models can predict the fluidity accurately. The results show that by increasing the mold temperature from 25℃ to 200℃, superheat from 50℃ to 250℃, and thickness from 3 mm to 12 mm, the fluidity of the composites decreases, where the mold thickness is more effective than other factors. In addition, the higher amounts of Mg_2Si in the range from 15 wt.% to 25 wt.% lead to the lower fluidity of the composites. For example, when the mold temperature, superheat, and thickness are respectively 100℃, 150℃, and 7 mm, the fluidity length is changed in the range of 11.9 cm to 15.3 cm. By increasing the amount of Mg_2Si, the morphology of the primary Mg_2Si becomes irregular and the size of primary Mg_2Si is increased. Moreover, the change of solidification mode from skin to pasty mode is the most noticeable microstructural effect on the fluidity.

关键词： Al-Mg2Si composites microstructure fluidity

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：