Influence of nickel and copper on liquid structure of CuAlNi shape memory alloys

Chinese Science Bulletin 2002年第1期47卷 85-88页

作者： pan xuemin & bian xiufangkey laboratory of liquid structure and heredity of materials, education ministry, shandong university, ji’nan 250061, china Key laboratory of liquid structure Education Ministry Shandong University Ji'nan 250061 China

liquid structure of molten pure Cu, Cu-12Al, Cu-12Al-4Ni (mass fraction, %) alloys has been investigated using the X-ray diffraction method. It is found that the main peak of the structure factor of pure Cu is symmetrical. In the front of main peak, the curve takes on a shape of parabola, whereas a distinct pre-peak has been found around a scattering vector magnitude of 18.5 nm-1 in the structure factor of the liquid Cu-12Al alloy. This pre-peak increases its inten-sity with the addition of Ni in the liquid Cu-12Al-4Ni alloy. The appearance of a pre-peak is a mark of the mediate-range order. Based on Daken-Gurry theory and according to mu-tual interaction between unlike atoms, the analysis of corre-lation between different composition and liquid structure was done: the strong interaction exists between Cu and Ni, so Cu-Al can form strong chemical bond which causes compound-forming behavior. Therefore, the medium-range size clusters can form in melt. The presence of the pre-peak corresponds to these

关键词： Cu-12Al-4Ni alloy liquid structure shape memory alloy X-ray diffraction.

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

Influence of liquid structure on Solid Transformation of CuAINi Shape Memory Alloy

引用

Journal of materials Science & Technology 2003年第2期19卷 147-149页

作者： xuemin pan, Xiufang bian Weimin WANG and jingyu QIN1) State Key laboratory of materials Modification by Laser, Ion and Electron Beams, Dalian university of Technology, Dalian 116023, china2) Key laboratory of liquid structure and heredity of materials, ministry of education, shandong university, jinan 250061, china

Molten Cu-13AI and Cu-13AI-4Ni (mass fraction) alloys have been investigated using X-ray diffraction method. A distinct pre-peak has been found in the structure factors. The pre-peak increases its intensity with decreasing temperature and addition of Ni. The structural unit size corresponding to the pre-peak equals to magnitude of (111) planar distance of phase. The appearance of a pre-peak is due to existence of clusters with -phase-like structure in melt. Quantity and size of clusters increase with decreasing temperature but their structural unit size remains constant. Cu-13AI-4Ni shape memory alloy ribbons can be fabricated by rapid solidification technique. Order degree of martensite and temperature of the reverse martensitic transformation increase with decreasing liquid quenching temperature. phase particles develop from incorporating and growing of the clusters during solidification, thus result in the correlation between liquid structure and solid transformation.

关键词： CuAINi alloy liquid structure Shape memory alloy X-ray diffraction

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

Al-TM合金熔体的中程有序结构及其演化规律

引用

化学学报 2002年第7期60卷 1215-1219页

作者：边秀房王伟民潘学民秦绪波山东大学材料液态结构及其遗传性教育部重点实验室济南250061

用高温熔体X射线衍射仪对Al TM (TM =Fe,Ni)合金的熔体结构进行了实验研究 .在Al 1.0at%Fe(原子百分比 )合金的结构因子曲线S(Q)上 ,温度为 6 70℃时 ,存在预峰 ,即中程有序结构 ,当温度过热到 140 0℃时 ,预峰消失 .Al 2 0at%Ni合金熔... 详细信息

用高温熔体X射线衍射仪对Al TM (TM =Fe,Ni)合金的熔体结构进行了实验研究 .在Al 1.0at%Fe(原子百分比 )合金的结构因子曲线S(Q)上 ,温度为 6 70℃时 ,存在预峰 ,即中程有序结构 ,当温度过热到 140 0℃时 ,预峰消失 .Al 2 0at%Ni合金熔体温度在≤ 130 0℃范围内 ,存在预峰 ;温度高于 140 0℃时 ,预峰逐渐消失 .这些实验结果表明 ,Al Ni,Al Fe合金熔体中除存在短程有序结构外 ,还存在中程有序结构 .这种中程有序结构的存在与消失与温度有关 .在相似的条件下 ,Al Si合金中没有发现中程有序结构 .

关键词： AL-TM合金熔体中程有序结构演化规律铝合金 X射线

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：