Static mechanical properties of hybrid RTM-made composite Ⅰ-and Ⅱ-beams under three-point flexure

在线全文

学校读者我要写书评

暂无评论

Chinese Journal of Aeronautics 2015年第3期28卷 903-913页

作者： Fu Yu Xiong Junjiang luo chuyang Yun Xinyao School of Transportation Science and Engineering Beihang University

Abstract This paper deals with three-point flexure tests on hybrid I- and II-beams, made out of multi-layer carbon fiber/epoxy resin （including twill woven fabric CF3031/5284 and unidirectional cord fabric U3160/5284） reinforced composites, processed using the RTM （resin transfer molding） technique. Static bending properties were determined and failure initiation mechanism was deduced from experimental observations. Failure mode of the tested hybrid RTM-made I-beams can be reckoned to be characteristic of the delamination from the cutout edge within the web and the debonding propagation along the interface between the inverted triangular resin-rich zone and the adjacent curved web until local buckling within the curved webs around the conjunction fillet region. In contrast, as distinct from hybrid RTM I-beams subjected to three-point bending loading, hybrid RTM-made H-beams in three-point flexure tests experienced the resin debonding in the inverted triangular resin-rich zones and the debonding propagation along the interface between the inverted triangular resin-rich zone and the adjacent curved web until complete separation of the curved web from the flange. Progressive damage models （PDMs） were presented to predict fail- ure loads and process of hybrid RTM-made I- and N-beams under three-point flexure. Good cor- relation was achieved between experimental and numerical results.

关键词： Beam Composites Experiment Fabric Molding Simulation

Thermo-mechanical properties of RTM-made carbon fibre/polyimide composite attaching collar under transient heating

在线全文

学校读者我要写书评

暂无评论

Chinese Journal of Aeronautics 2023年第3期36卷 393-405页

作者： Shengda JIANG chuyang luo Peng ZHANG Jianwen BAO Peipei CAI Xufeng XIA Shanghai High Performance Fibers and Composites Center(Province-Ministry Joint) Center for Civil Aviation CompositesDonghua UniversityShanghai 201620China AVIC Composite Technology Center Science and Technology on Advanced Composites LaboratoryBeijing 101300China luoyang Optoelectro Technology Development Center Luoyang 471009China

This study focuses on the thermo-mechanical properties of Carbon Fibre/Polyimide Composite(CFPC)attaching collars under transient *** CFPC attaching collars were fabricated by a high-temperature resin transfer moulding process,and their thermo-mechanical properties under the conditions of simultaneous transient heating and bending load were *** results show that the attaching collar tends to fail at 118% of the limit *** failure mode includes the fracture of the connecting screws,local extrusion damage of the hole edges,and slight ablation damage at the outer *** there is no observable residual deformation in the composite attaching ***,considering that the material properties vary with temperature,a progressive damage model based on the sequential thermo-mechanical coupling method was established to study the failure mechanism of the attaching ***,the damage factor of the CFPC was calculated to assess the safety status of the attaching *** results show that the primary damage modes of the composite attaching collar are intralaminar failure,which mainly occurs at the heat insulation layer and the hole edges,and these slightly affect the structural bearing capacity.A good correlation between the experiment and FEA is *** test methods and analysis models proposed contribute to the safety assessment of composite structures under transient heating.

关键词： Polyimide composites Progressive damage model Resin transfer moulding Thermo-mechanical properties Transient heating

Laser ablation mechanism and performance of glass fiber-reinforced phenolic composites:An experimental study and dual-scale modelling

在线全文

学校读者我要写书评

暂无评论

Chinese Journal of Aeronautics 2024年第8期37卷 470-485页

作者： Ran BI Pengfei SHEN Longyu ZHU Zhengzheng MA chuyang luo Yongfeng LI Lijian PAN Shanghai Key Laboratory of Lightweight Composite Donghua UniversityShanghai 201620China Shanghai High Performance Fibers and Composites Center(Province-Ministry Joint) Center for Civil Aviation CompositesDonghua UniversityShanghai 201620China AVIC Composite Corporation Ltd Beijing 101300China

Both experimental and simulation approaches were employed to investigate the laser ablation mechanism and performances of Glass Fiber Reinforced Phenolic Composites(GFRP).During the ablation process,the difference in thermal conductivities of the glass fibers and the resin matrix as well as their discrepant physical and chemical reactions form a conical ablation *** formation of a residual carbon layer effectively mitigates the ablation rate in the thickness direction.A higher power density results in a faster ablation rate,while a longer irradiation time leads to a larger ablation pit *** account for the variation in thermal conductivity between the fiber and resin,a macro-mesoscale model was developed to differentiate the matrix from the fiber *** element analysis revealed that laser irradiation leads to phenolic decomposition,glass fiber melting vaporization,and residual carbon skeleton *** dual-scale model exhibits precise prediction capabilities concerning the laser ablation process of GFRP,and its accuracy is confirmed through the comparison of simulation and experimental results for the GFRP laser ablation *** model provides a feasible method for performance evaluation and lifetime prediction of GFRP subjected to continuous wave laser irradiation.

关键词： Polymer-matrix composites Continuous-wave laser Microstructural analysis Ablation mechanism Finite element method

基于熔融沉积成型的连续纤维增强复合材料3D打印研究进展

在线全文

学校读者我要写书评

暂无评论

航空兵器 2023年第2期30卷 42-52页

作者：於琳涛聂祥樊罗楚养重庆交通大学航空学院重庆400074 重庆交通大学绿色航空技术研究院重庆401120 空军工程大学航空学院西安710038 东华大学民用航空复合材料协同创新中心上海201620

熔融沉积成型(Fused Deposition Modeling,FDM)工艺具有无模自由成型、可设计性强、快速成型等特点,进一步扩大了连续纤维增强复合材料的应用范围,是当前受到广泛关注和研究的3D打印成型工艺。本文针对连续纤维增强复合材料的FDM工艺成... 详细信息

熔融沉积成型(Fused Deposition Modeling,FDM)工艺具有无模自由成型、可设计性强、快速成型等特点,进一步扩大了连续纤维增强复合材料的应用范围,是当前受到广泛关注和研究的3D打印成型工艺。本文针对连续纤维增强复合材料的FDM工艺成形原理、工艺方法及设备、打印原材料等方面进行综述;分析了工艺参数、浸渍状态以及路径规划算法对连续纤维增强复合材料3D打印样件的力学性能及表面质量的影响。针对当前FDM工艺以及技术发展所遇到的问题进行总结并对今后发展的重点方向提出建议。

关键词：复合材料 3D打印连续纤维熔融沉积成型飞行器

陶瓷抗激光涂层对钛合金焊缝及凹槽区域的防护效果研究

在线全文

学校读者我要写书评

暂无评论

西北工业大学学报 2021年第6期39卷 1281-1288页

作者：朱洁旻赵懿杨振程功罗楚养东华大学民用航空复合材料协同创新中心上海201620 哈尔滨工业大学航天学院黑龙江哈尔滨150001 中国空空导弹研究院河南洛阳471009

为探究焊缝区域以及凹槽结构对钛合金基材激光毁伤效果以及陶瓷涂层抗激光效果的影响,采用对比实验法研究了钛合金表面存在和不存在陶瓷抗激光涂层2种情况下,连续激光对钛合金焊缝区域以及凹槽区域的毁伤效果,结果表明,陶瓷涂层能够有... 详细信息

为探究焊缝区域以及凹槽结构对钛合金基材激光毁伤效果以及陶瓷涂层抗激光效果的影响,采用对比实验法研究了钛合金表面存在和不存在陶瓷抗激光涂层2种情况下,连续激光对钛合金焊缝区域以及凹槽区域的毁伤效果,结果表明,陶瓷涂层能够有效减轻钛合金基底的激光毁伤效果。焊缝区域陶瓷涂层抗激光性能减弱,但仍能进行有效抗激光防护。凹槽结构的棱部、角部的激光毁伤效果随激光功率密度的增加而加重,在相同激光功率密度条件下,凹槽结构内部毁伤效果明显较外部毁伤效果小,角部结构毁伤效果较棱部结构小。高反射型陶瓷涂层在反射部分激光能量后,会吸收大量由激光辐照产生的热能,发生烧结作用导致内部结构变化,从而对钛合金基底起到保护作用。

关键词：激光毁伤陶瓷涂层焊缝区域凹槽结构钛合金

智能隐身材料在空空导弹结构设计中的应用展望

在线全文

学校读者我要写书评

暂无评论

航空兵器 2023年第2期30卷 21-30页

作者：郭正玉毕冉马征峥罗楚养中国空空导弹研究院河南洛阳471009 空基信息感知与融合全国重点实验室河南洛阳471009 东华大学民用航空复合材料协同创新中心上海201620

空空导弹是战斗机夺取制空作战优势的重要武器,总体设计技术的发展和作战使用需求的推动,使空空导弹飞行距离越来越远,将面临突防问题。隐身是增强突防能力的关键,隐身材料是空空导弹实现隐身的重要载体和关键技术,也是其结构设计的重... 详细信息

空空导弹是战斗机夺取制空作战优势的重要武器,总体设计技术的发展和作战使用需求的推动,使空空导弹飞行距离越来越远,将面临突防问题。隐身是增强突防能力的关键,隐身材料是空空导弹实现隐身的重要载体和关键技术,也是其结构设计的重要组成部分。本文分析了目前在可见光、红外和雷达等技术领域的隐身材料和智能隐身技术的研究现状,提出了下一阶段智能隐身技术的发展重点。

关键词：空空导弹隐身材料结构设计智能隐身技术

基于RTM技术的碳纤维/聚酰亚胺复合材料舵面一体化制备与验证

在线全文

学校读者我要写书评

暂无评论

复合材料学报 2020年第9期37卷 2152-2162页

作者：江晟达罗楚养张朋文子豪蔡培培东华大学民用航空复合材料协同创新中心上海201620 中国空空导弹研究院洛阳471009 航空工业复合材料技术中心先进复合材料重点实验室北京101300

设计了一种碳纤维/聚酰亚胺复合材料舵面结构,采用PAM-RTM软件模拟了舵面在注胶过程中的树脂流动,根据模拟结果设计了成型模具,并通过树脂传递模塑(RTM)工艺制备了耐高温碳纤维/聚酰亚胺复合材料舵面,对其进行了力学试验,并将三维有限... 详细信息

设计了一种碳纤维/聚酰亚胺复合材料舵面结构,采用PAM-RTM软件模拟了舵面在注胶过程中的树脂流动,根据模拟结果设计了成型模具,并通过树脂传递模塑(RTM)工艺制备了耐高温碳纤维/聚酰亚胺复合材料舵面,对其进行了力学试验,并将三维有限元分析结果与试验结果对比。试验结果表明,碳纤维/聚酰亚胺复合材料舵面在150%的使用载荷下保持了结构的完整性,骨架的最大应变为2408×10^–6,复合材料蒙皮的最大应变为2371×10^–6。有限元分析结果表明,金属骨架的最大应力出现在舵轴根部圆弧过渡区,而碳纤维/聚酰亚胺复合材料蒙皮的最大应力出现在与垫片外圆弧接触处;碳纤维/聚酰亚胺复合材料舵面的初始破坏为蒙皮单向带横向拉伸失效。

关键词：复合材料舵面聚酰亚胺树脂传递模塑破坏机制

碳纳米纤维增强聚酰亚胺复合气凝胶的合成与性能

在线全文

学校读者我要写书评

暂无评论

材料工程 2022年第1期50卷 125-131页

作者：章玲王雪李家强罗楚养张威张礼颖东华大学民用航空复合材料协同创新中心上海201620 东华大学纺织学院上海201620 东华大学材料科学与工程学院上海201620

以4,4′-二氨基二苯醚(ODA)、均苯四甲酸二酐(PMDA)为单体,酸化碳纳米纤维(a-CNF)为增强材料,采用溶胶-凝胶方式成型,运用冷冻干燥技术制备PI复合气凝胶。对复合气凝胶的形貌、隔热、吸波以及压缩性能等进行表征分析。研究结果表明:随着... 详细信息

以4,4′-二氨基二苯醚(ODA)、均苯四甲酸二酐(PMDA)为单体,酸化碳纳米纤维(a-CNF)为增强材料,采用溶胶-凝胶方式成型,运用冷冻干燥技术制备PI复合气凝胶。对复合气凝胶的形貌、隔热、吸波以及压缩性能等进行表征分析。研究结果表明:随着a-CNF含量的增加,PI复合气凝胶的收缩率从45.52%降至35.32%,密度也随之从0.084 g/cm^(3)降至0.069 g/cm^(3),气凝胶孔洞分布呈增大增宽趋势。a-CNF的引入有效抑制了PI复合气凝胶的收缩率,热导率降低;整个体系的导电损耗增加,同时由于气凝胶的多孔结构提供了较好的阻抗匹配,使得PI复合气凝胶的反射损耗(RL)在8.3 GHz达到-9.7 dB。加入质量分数为15%的CNF/PI复合气凝胶压缩强度和压缩模量分别是纯PI气凝胶的近1.5倍和2倍。

关键词：聚酰亚胺气凝胶碳纳米纤维隔热吸波压缩

RTM成型非对称复合材料T型接头的拉伸失效机制

同方期刊数据库

同方期刊数据库博看期刊评论

在线全文

学校读者我要写书评

暂无评论

复合材料学报 2023年第1期40卷 613-624页

作者：王帅陈梦熊李伟东罗楚养潘利剑东华大学民用航空复合材料协同创新中心上海201620 中航复合材料有限责任公司北京航空材料研究院先进复合材料重点实验室北京100095

采用树脂传递模塑(RTM)工艺制备了结构对称和非对称两种复合材料T型接头试样,并对其进行了静态拉伸力学试验,对比分析了两种结构的拉伸破坏模式、结构刚度及破坏载荷。同时基于T接头内聚力模型(CZM),研究了两种不同结构T型接头的拉伸破... 详细信息

采用树脂传递模塑(RTM)工艺制备了结构对称和非对称两种复合材料T型接头试样,并对其进行了静态拉伸力学试验,对比分析了两种结构的拉伸破坏模式、结构刚度及破坏载荷。同时基于T接头内聚力模型(CZM),研究了两种不同结构T型接头的拉伸破坏过程及失效机制,并对比分析了不同偏转角下T接头的层间应力。结果表明:不同结构T型接头的拉伸破坏模式不同,偏转角的存在使结构非对称T型接头夹角大侧圆弧受力明显高于小侧圆弧,导致接头首先在大侧夹角圆弧与三角区界面定向萌生初始裂纹,随后裂纹主要沿大侧腹板翻边与蒙皮的界面扩展,进而导致接头最终破坏,最终失效载荷较对称T型接头提高了15.3%,且结构刚度更大。有限元结果表明T型接头三角区的初始失效主要由层间正应力及剪应力引起,有限元分析的失效模式与试验一致,结构对称及非对称T型接头最终失效载荷与试验值均吻合较好;且随着偏转角的增加,腹板圆弧处层间应力逐渐减小,初始失效载荷将随之增大;初始破坏位置将转移至大侧夹角圆弧末端。

关键词：复合材料 T型接头失效机制有限元分析树脂传递模塑