高岭土(Kaolinite)和蒙脱土(Montromollite)等粘土,被广泛用作添加剂来改善聚合物的耐热性能.文章用各种先进技术对高岭土与蒙脱土的形态、组成和结构进行表征比较.电子透射电镜及电子探针(TEM/EDX)结果显示高岭土较蒙脱土有较大的粒径... 详细信息

高岭土(Kaolinite)和蒙脱土(Montromollite)等粘土,被广泛用作添加剂来改善聚合物的耐热性能.文章用各种先进技术对高岭土与蒙脱土的形态、组成和结构进行表征比较.电子透射电镜及电子探针(TEM/EDX)结果显示高岭土较蒙脱土有较大的粒径和较小的硅铝比,TEM还显示出这些粘土是由片层粒子堆积而成.热重分析(TGA)的结果表明蒙脱土由于失去吸附水从60℃升温至90℃失重明显(约7%),而高岭土在此温度下几乎不失水.高岭土脱除结构羟基官能团脱水失重的温度大约在510℃,低于蒙脱土的670℃.室温下光声傅里叶变换(PAS-FTIR)红外光谱显示蒙脱土在羟基吸收区有较强的吸附水的吸收,1 650 cm-1处孤立的弱吸收谱带可给予左证.变温红外和TGA的结果显示,片层硅酸盐表面的结构羟基从100～500℃非常稳定,它可以和异氰酸酯基团(NCO)封端的预聚物反应形成热固性PU/PLS复合聚合物.

关键词：粘土表征 PU/PLS复合物

用于制备聚氨酯纳米复合物的高岭石粒子的表征(英文)

在线全文

学校读者我要写书评

暂无评论

引用

无机化学学报 2003年第11期19卷 1261-1265页

作者：李再峰王义银 luba S.kotlyar Keng H.Chung 青岛科技大学化学与分子工程学院青岛266042 西安交通大学管理学院西安710049 ICPET National Research Council1200 Montreal RoadOttawaOntario Syncrude Canada Ltd. Edmonton Research Centre9421-17th AvenueEdmontonAlberta

Clay such as kaolinite, is commonly used as an additive to modify the thermal properties of polymer. In this paper, the morphology, composition, shape and structure of kaolinite was characterized by various advanced techniques. The TEM/ EDX data showed that the kaolinite had a larger particle size and a Si/Al ratio of 1.8. The individual particle of kaolinite was a single crystalline. TEM also showed that these particles were always stacked together due to the presence of electrostatic cohesive energy and hydrogen bond between plaletes. The PAS FTIR spectra showed that no absorbance of hydroxyl group for hydration water in hydrogen bond region or at 1650cm- 1 was observed at room temperature. It meant a little ability to adsorb water for kaolinite particle. Kaolinite clay also showed no change for its PAS FTIR spectra with increasing temperature. The TGA results revealed that kaolinite almost doesn′ t lose weight at 60℃ due to loss of dehydration of absorbed water, however, it will decomposed around 510℃ and lose its hydroxyl functional group in the form of water (dehydroxylation). The result is consistent with that of PAS FTIR analysis. This suggests that the structural hydroxyl group on the surface of individual kaolinite clay particle is very stable below 500℃ , and the kaolinite composed polymer could be got by the reaction of its stable structural hydroxyl group with isocynate group of polyurethane prepolymer.

关键词：制备聚氨酯纳米复合聚合物高岭石粒子表征

Athabasca油砂沥青中重组分的分子模拟

在线全文

学校读者我要写书评

暂无评论

引用

化工学报 2003年第1期54卷 9-17页

作者：高金森徐春明 luba S.kotlyar Keng H.CHUNG 石油大学重质油加工国家重点实验室北京102249 加拿大国家研究院加拿大合成油有限公司埃德蒙顿研究中心

利用分子模拟技术对加拿大Athabasca油砂沥青超临界萃取分馏残渣组分的化学分子结构进行了研究 ,首先选用长度不同的桥链构建了其三维平均结构 ,然后采用分子力学 (MM)和分子动力学 (MD)方法得到能量最低也即最稳定的构象 .研究发现 ,... 详细信息

利用分子模拟技术对加拿大Athabasca油砂沥青超临界萃取分馏残渣组分的化学分子结构进行了研究 ,首先选用长度不同的桥链构建了其三维平均结构 ,然后采用分子力学 (MM)和分子动力学 (MD)方法得到能量最低也即最稳定的构象 .研究发现 ,即使分子的二维结构相同 ,其三维结构差别也很大 ,由此可见仅用二维模型来表征重质油大分子的结构和物理化学性质远远不够 .另外 ,分子模拟还可以预测沥青质残渣中最有可能存在的桥链长度 .Athabasca沥青残渣组分中长度为C5到C7的桥链存在的可能性最大 ,而C1和C2桥链则由于其总能量相对较高。

关键词： Athabasca油砂沥青分子模拟重组分分子结构分子力学分子动力学超临界萃取分馏残渣