Effect of TiC addition on the microstructure and wear resistance of induction brazed nickel-based coating in air

在线全文

学校读者我要写书评

暂无评论

China Welding 2022年第4期31卷 1-6页

作者： Long Weimin Sun Huawei liu dashuang Qin Jian Zhang Lei Lu Hongbo China Academy of Machinery Ningbo Academy of Intelligent Machine Tool Co. Ltd.Ningbo 315700China State Key Laboratory of Advanced Brazing Filler Metals and Technology Zhengzhou Research Institute of Mechanical Engineering Co.Ltd.Zhengzhou 450001China School of Material Science and Engineering Hefei University of TechnologyHefei 230009China Zhengzhou Dingsheng Advanced Engineering Technology Co. LtdZhengzhou 450001China

The nickel-based coating with different TiC addition was fabricated onto 45 steel substrate by using induction brazed technology in *** effect of TiC addition on the microstructure and wear resistance of induction brazing coating was *** results show that the microstructure of brazing coating is strengthened and refined by adding *** the increase of the amount of TiC added,the amount of TiC in the Ni-based matrix is increased,and the matrix structure is obviously *** is because the high melting point TiC particles can be used as heterogeneous nucleation cores,thus refining the Ni based matrix ***,the wear resistance of brazing coating is improved due to the addition of TiC.

关键词： induction brazing nickel-based coating TiC

在线全文

学校读者我要写书评

暂无评论

感应钎涂粉末熔融及传热机制

焊接学报 2021年第11期42卷 29-34,I0002,I0003页

作者：龙伟民刘大双张冠星吴爱萍清华大学北京100084 郑州机械研究所有限公司郑州450001 合肥工业大学合肥230009

感应钎涂技术是材料表面修型提性的重要技术手段,分别选用碳钢和陶瓷作为基板进行感应钎涂试验,系统研究了粉状和膏状钎涂层温度变化规律,分析了钎涂过程热量传递方式和路径.结果表明,感应钎涂时涂层材料不能被直接感应加热,钎涂层升温... 详细信息

感应钎涂技术是材料表面修型提性的重要技术手段,分别选用碳钢和陶瓷作为基板进行感应钎涂试验,系统研究了粉状和膏状钎涂层温度变化规律,分析了钎涂过程热量传递方式和路径.结果表明,感应钎涂时涂层材料不能被直接感应加热,钎涂层升温的热源几乎全部来自于钢基体的热传导,液固界面剧烈传热并梯次推进,促进了金属钎料的熔融铺展;当基材由导电且能够被感应加热的碳钢替换为陶瓷时,涂层材料升温只能依靠自身生热.粉状钎涂料呈游离态,粉末颗粒之间及粉末颗粒与金刚石之间充满气体,基体的热量难以传导至上部,粉末难以充分熔融,而添加粘结剂的膏状钎涂料在感应过程中能快速熔化,粘结剂兼有导热、助熔和保护等多重作用.

关键词：感应钎涂涡流生热传导传热粘结助熔

在线全文

学校读者我要写书评

暂无评论

旋耕刀感应钎涂层热处理工艺研究

材料导报 2022年第7期36卷 98-102页

作者：龙伟民秦建路全彬刘大双吴爱萍清华大学机械工程系郑州机械研究所有限公司合肥工业大学材料科学与工程学院

金刚石感应钎涂过程对钢基体组织和性能有较大影响，钎涂后热处理是提高基体性能的重要手段，但对涂层也有较大影响。采用高温金相显微镜、SEM、XRD、硬度试验等分析测试手段，研究了钎涂后热处理工艺对感应钎涂镍基合金组织演变及硬度... 详细信息

金刚石感应钎涂过程对钢基体组织和性能有较大影响，钎涂后热处理是提高基体性能的重要手段，但对涂层也有较大影响。采用高温金相显微镜、SEM、XRD、硬度试验等分析测试手段，研究了钎涂后热处理工艺对感应钎涂镍基合金组织演变及硬度的影响规律。结果表明，钎涂后的NiCrSiB钎涂层组织主要由Ni固溶体、CrB、Ni;Si、Ni;B和Ni-Ni;Si共晶组成；淬火处理后，Ni;Si-Ni固溶体共晶数量减少，尺寸减小，CrB出现一定程度的长大，且整体Ni;Si含量降低；回火处理后，NiCrSiB钎涂层组织晶界附近共晶数量又增多，CrB进一步长大，促进少量的Ni;Si组织生成。在钎涂状态下涂层硬度较高，经淬火后显微硬度整体下降，再经回火处理后显微硬度有所回升。以农机装备用旋耕刀为具体对象，研发了钎涂联合热处理提升旋耕刀整体性能的新技术。

关键词：金刚石感应钎涂高温金相硬度分布

省市共享技术平台的应用——湘潭市广播电视监测监管平台建设

在线全文

同方期刊数据库

学校读者我要写书评

暂无评论

电视技术 2024年第6期48卷 40-43页

作者：刘大双湘潭市广播电视台湖南湘潭411104

随着广播电视技术的迅速发展,广播电视和网络视听节目内容日益丰富,数据量日益增加,必须通过现代化的手段才能实现有效监管监测。为此,详细介绍湘潭市广播电视监管中心在湖南省广播电视局监管资源平台省市共享技术的基础上建设市级监测... 详细信息

随着广播电视技术的迅速发展,广播电视和网络视听节目内容日益丰富,数据量日益增加,必须通过现代化的手段才能实现有效监管监测。为此,详细介绍湘潭市广播电视监管中心在湖南省广播电视局监管资源平台省市共享技术的基础上建设市级监测监管平台的情况。

关键词：广播电视网络视听监测监管省市共享

金刚石粒度及添加量对大气环境感应钎涂层耐磨性的影响

在线全文

学校读者我要写书评

暂无评论

机械工程学报 2023年第12期59卷 225-235页

作者：龙伟民刘大双吴爱萍钟素娟王德成清华大学机械工程学院北京100084 郑州机械研究所有限公司郑州450001 中机智能装备创新研究院(宁波)有限公司宁波315700 合肥工业大学材料科学与工程学院合肥230009 机械科学研究总院集团有限公司北京100044

金刚石是自然界中最坚硬的物质,因其具有良好的耐磨性能,广泛应用于切削、磨削等行业。利用钎涂技术制备金刚石工具,具有独特优势。钎涂层中的金刚石粒度及添加量是影响涂层耐磨性的关键因素,为此,试验研究金刚石添加量及粒度对大气环... 详细信息

金刚石是自然界中最坚硬的物质,因其具有良好的耐磨性能,广泛应用于切削、磨削等行业。利用钎涂技术制备金刚石工具,具有独特优势。钎涂层中的金刚石粒度及添加量是影响涂层耐磨性的关键因素,为此,试验研究金刚石添加量及粒度对大气环境感应钎涂层界面组织及耐磨性的影响规律,探讨金刚石钎涂层的耐磨机制。结果表明,Cr元素在金刚石微粒/Ni基钎料合金界面处形成了宽度约2μm的富集带。当金刚石添加量达到15%时,可原位生成一定比例的碳化物,且碳化物类型为Cr7C3。同质量分数添加金刚石微粒(210~280μm)的钎涂层耐磨性要优于添加颗粒(700~840μm)的钎涂层。对于添加不同含量金刚石微粒的钎涂层而言,金刚石添加量为20%时涂层耐磨性最优,当金刚石添加量超过20%,耐磨性不增反降。钎涂层中金刚石在磨损过程中,呈现完整、钝化、裂纹、破碎、脱落等形式。

关键词：金刚石钎涂感应加热耐磨性

同方期刊数据库

Microstructure and properties of induction brazing nickel base/WC composite coating

在线全文

学校读者我要写书评

暂无评论

China Welding 2023年第1期32卷 27-34页

作者：秦建杨骄刘攀刘大双卢洪波廖清泉常云峰 Zhengzhou Dingsheng High-tech Energy Engineering Technology Co. LTD.Zhengzhou 450001China School of Materials Science and Engineering Hefei University of TechnologyHefei 230009China State Key Laboratory of Brazing Materials and Technology Zhengzhou Machinery Research Institute Co.LTD.HenanZhengzhou 450001China

BNi-2/WC composite wear-resisting coating was prepared on carbon steel by the method of induction *** microstructure and phase composition of the composite coating were analyzed,and the bonding strength and wear-resisting performance of the coating were *** the process of induction brazing,the tungsten carbide partially dissolves and reacts with the filler metal alloy to form NiW compound phase,which realizes the metallurgical combination of tungsten carbide and filler metal *** matrix of the filler metal alloy consists of Ni solid solution and Ni_(3)B/Ni_(3)Si eutectic phase,and the metallurgical diffusion reaction occurs between the filler metal alloy and the steel *** mechanical analysis results show that the self-strength of the composite coating reaches 140 MPa and the bonding strength of the filler metal alloy to the steel matrix reaches 360 *** dry sand rubber wheel wear testing machine showed that the coating weight loss was only 0.2824 g,which was only 1/5 of the weight loss of 65 Mn matrix under the same conditions.

关键词： composite coating induction brazing tungsten carbide BNi-2 wear resistance

浅谈卡洛特水电站EPC总承包项目进度计划管理

在线全文

学校读者我要写书评

暂无评论

人民长江 2018年第A02期49卷 217-219页

作者：白琦瑞王嵬刘大双长江三峡技术经济发展有限公司北京100038

国际工程EPC总承包项目管理主要包括计划、组织、指挥、协调和控制等。计划是首要职能,计划和控制是管理的核心。在一定程度上可以说,没有计划,就没有控制,也就没有项目管理。项目管理的结果将体现是否能在成本约束下仍能按期保质安全... 详细信息

国际工程EPC总承包项目管理主要包括计划、组织、指挥、协调和控制等。计划是首要职能,计划和控制是管理的核心。在一定程度上可以说,没有计划,就没有控制,也就没有项目管理。项目管理的结果将体现是否能在成本约束下仍能按期保质安全实施完成。针对巴基斯坦卡洛特水电站项目,借鉴三峡工程的施工计划管理经验,探讨了EPC管理中容易出现的问题,处理措施,制定了该项目的 EPC计划,为保证卡洛特水电站的顺利施工打下了坚实基础。

关键词：卡洛特水电站 EPC合同国际工程进度计划管理巴基斯坦

铝微粉对大气环境感应钎涂金刚石涂层性能影响

在线全文

学校读者我要写书评

暂无评论

焊接学报 2021年第12期42卷 67-71,I0004,I0005页

作者：龙伟民刘大双王博吴爱萍王德成清华大学北京100084 中机智能装备创新研究院(宁波)有限公司宁波315700 合肥工业大学合肥230009 中国机械科学研究总院集团有限公司北京100044

金刚石钎涂是材料表面修形提性的重要技术手段,由于金刚石的超硬特性使得钎涂涂层中金刚石与钎料的性能难以匹配.在镍基钎料中加入铝微粉,研究Al对涂层组织及耐磨性的影响.结果表明,Al的添加降低了金刚石钎涂层孔隙率,同时钎涂过程中在... 详细信息

金刚石钎涂是材料表面修形提性的重要技术手段,由于金刚石的超硬特性使得钎涂涂层中金刚石与钎料的性能难以匹配.在镍基钎料中加入铝微粉,研究Al对涂层组织及耐磨性的影响.结果表明,Al的添加降低了金刚石钎涂层孔隙率,同时钎涂过程中在基体内原位生成Al_(2)O_(3)相,提高了金刚石钎涂层的耐磨性.阐明了Al脱氧消减气孔及其脱氧产物Al_(2)O_(3)作为原位生成硬质相增强涂层硬度及耐磨性的机制.进一步揭示了原位生成Al_(2)O_(3)可细化、强化钎料组织,优化涂层形态、增加涂层厚度的机理.明确了感应钎涂中活性微粉的脱氧作用和原位生成氧化物陶瓷的耐磨作用.

关键词：铝微粉大气环境感应钎涂原位生成

WC-Co纳米粉末对E4303焊条性能的影响

在线全文

学校读者我要写书评

暂无评论

热加工工艺 2010年第11期39卷 57-59页

作者：董丰波陈文华刘大双南京航空航天大学材料科学与技术学院江苏南京210016

将WC-Co纳米粉末加入到E4303焊条药皮中,制备新型耐磨堆焊焊条。对该焊条进行了工艺性试验,并对堆焊层的组织,化学成分及硬度等进行了检验和分析。结果表明:该焊条工艺性良好,堆焊熔敷金属组织中有大量均匀的W碳化物生成,同时Co作为堆... 详细信息

将WC-Co纳米粉末加入到E4303焊条药皮中,制备新型耐磨堆焊焊条。对该焊条进行了工艺性试验,并对堆焊层的组织,化学成分及硬度等进行了检验和分析。结果表明:该焊条工艺性良好,堆焊熔敷金属组织中有大量均匀的W碳化物生成,同时Co作为堆焊层的粘结相,可以很好的粘结硬质相和过渡相,使得堆焊的金属层具有较高的抗裂纹萌生和扩展阻力,从而增加了E4303焊条耐磨性,提高其硬度(达30HRC以上),极大的改善E4303焊条的性能。

关键词：纳米粉末 E4303焊条耐磨堆焊材料