Oxide dispersion strengthened stainless steel 316L with superior strength and ductility by selective laser melting

Journal of Materials Science & Technology 2020年第7期42卷 97-105页

作者： Yuan Zhong leifeng liu Ji Zou Xiaodong Li Daqing Cui Zhijian Shen Department of Materials and Environmental Chemistry Arrhenius LaboratoryStockholm UniversitySE-10691 StockholmSweden School of Metallurgy and Materials University of BirminghamB152TT UK Department of Chemistry-Radiochemistry P.O.Box 55FI-00014 University of HelsinkiFinland

Dense oxide dispersion strengthened(ODS) 316 L steels with different amount of Y2O3 additions were succe s s fully fabricated by selective laser melting(SLM) even though part of the added Y2O3 got lost during the *** microstructure was characterized in details and the mechanical properties were tested at room temperature,250℃ and 400℃,*** effect of the scanning speed on agglomeration of nanoparticles during SLM process was *** properties,e.g.,yield strength of 574 MPa and elongation of 91%,were achieved at room temperature in SLM ODS 316 L with additional 1% of Y2 *** elevated temperature s,the strength kept high but the elongations dropped dra *** was observed that nano-voids nucleated throughout the whole gauge section at the sites where nanoinclusions *** growth and coalescence of these voids were suppre s sed by the formation of an element segregation network before necking,which relieved local stress concentration and thus delayed *** unusual necking behavior was studied and compared to the previous *** appeared that the strong convection presented in the melt pool can evenly redistribute the short-time milled coarse Y2O3 precursor powder during SLM *** findings can not only solve the problems encountered during the fabrication of ODS components but also replenish the strengthening mechanism of SLM 316 L thus pave a way for further improving of mechanical properties.

关键词： ODS steel Selective laser melting(SLM) Elevated-temperature properties Necking Strain hardening

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

Self-supported yttria-stabilized zirconia mesocrystals with tunable mesopores prepared by a chemi-thermal process

引用

Journal of Materiomics 2019年第3期5卷 350-356页

作者： leifeng liu Mirva Eriksson Ji Zou Yuan Zhong Qi liu Zhi liu Yu-Lung Chiu Zhijian Shen Department of Materials and Environmental Chemistry Arrhenius LaboratoryStockholm University10691StockholmSweden School of Metallurgy and Materials University of BirminghamB152TTUK Department of Materials Science and Engineering South University of Science and Technology of China518055China Size Materials Co. JiujiangChina

Mesoporous mesocrystals are highly desired in catalysis,energy storage,medical and many other applications,but most of synthesis strategies involve the usage of costly chemicals and complicated synthesis routes,which impede the commercialization of such *** the sintering of dense ceramics,coarsening is an undesirable phenomenon which causes the growth of the grains as well as the pores hence hinders the densification,however,coarsening is desired in the sintering of porous ceramics to expand the pore sizes while retaining the total pore *** we report a chemi-thermal process,during which nanocrystallite aggregates were synthesized by hydrothermal process and then converted to the product by *** this strategy,we synthesized mesoporous self-supported mesocrystals of yttria-stabilized zirconia with tunable pore size and the process was then scaled-up to industrial *** thermal conductivity measurement shows that the mesoporous powder is a good thermal *** monolith pellets can be obtained by SPS sintering under high pressure and the mesoporosity is retained in the monolith *** work features facile and scalable process as well as low cost raw chemicals making it highly desirable in industrial applications.

关键词： Mesocrystal Mesoporous Yttria-stabilized zirconia Industry production

来源：

维普期刊数据库评论

在线全文

维普期刊数据库

学校读者我要写书评

暂无评论

Current-collapse suppression and leakage-current decrease in AlGaN/GaN HEMT by sputter-TaN gate-dielectric layer

引用

Journal of Semiconductors 2024年第7期45卷 70-75页

作者： Bosen liu Guohao Yu Huimin Jia Jingyuan Zhu Jiaan Zhou Yu Li Bingliang Zhang Zhongkai Du Bohan Guo Lu Wang Qizhi Huang leifeng Jiang Zhongming Zeng Zhipeng Wei Baoshun Zhang State Key Laboratory of High-Power Semiconductor Laser School of PhysicsChangchun University of Science and TechnologyChangchun 130022China Nanofabrication facility Suzhou Institute of Nano-Tech and Nano-BionicsChinese Academy of SciencesSuzhou 215123China Suzhou Powerhouse Electronics Technology Co. Ltd.Suzhou 215123China

In this paper, we explore the electrical characteristics of high-electron-mobility transistors(HEMTs) using a TaN/AlGaN/GaN metal insulating semiconductor(MIS) structure. The high-resistance tantalum nitride(TaN) film prepared by magnetron sputtering as the gate dielectric layer of the device achieved an effective reduction of electronic states at the TaN/AlGaN interface, and reducing the gate leakage current of the MIS HEMT, its performance was enhanced. The HEMT exhibited a low gate leakage current of 2.15 × 10^(-7) mA/mm and a breakdown voltage of 1180 V. Furthermore, the MIS HEMT displayed exceptional operational stability during dynamic tests, with dynamic resistance remaining only 1.39 times even under 400 V stress.

关键词： AlGaN/GaN MIS HEMTs gate dielectric layer depletion-mode gate reliability I_(on)/I_(off)ratio

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

Preparation of nano-sized Bi2Te3 thermoelectric material powders by cryogenic grinding

引用

Progress in Natural Science:Materials International 2012年第3期22卷 201-206页

作者： Xiaozong Chen a, leifeng liu b, Yuan Dong a, Lianjun Wang a, Lidong Chen c, Wan Jiang a, a State Key Laboratory for Modification of Chemical Fibers and Polymer Materials, Donghua University, 2999 people of North Road, Shanghai 201620, PR China b Department of Materials and Environmental Chemistry, Stockholm University, SE-106 91 Stockholm, Sweden c Shanghai Institute of Ceramics, Chinese Academy of Sciences, 1295 Dingxi Road, Shanghai 200050, PR China State Key Laboratory for Modification of Chemical Fibers and Polymer Materials Donghua University 2999 people of North Road Shanghai 201620 PR China Department of Materials and Environmental Chemistry Stockholm University SE-106 91 Stockholm Sweden Shanghai Institute of Ceramics Chinese Academy of Sciences 1295 Dingxi Road Shanghai 200050 PR China

A novel method for rapid preparation of Bi2Te3 nano-sized powders with an average particle size of about 70 nm was developed. A starting powder mixture consisting of Bi2Te3 coarse particles of ～5 mm was ground using cryogenic grinding in the liquid nitrogen. For comparison, the conventional high-energy ball milling was used to prepare the Bi2Te3 nano-sized powders. Sintering properties of as-prepared powders was investigated by spark plasma sintering (SPS). The effects of the preparation procedure on the crystallinity, morphology and structure were examined by X-ray diffraction (XRD) and transmission electron microscopy (TEM). It was found that Bi2Te3 was not transformed into a non-equilibrium amorphous phase or decomposed during the cryogenic grinding process, and as-prepared nano-powders possessed excellent sinterability. This technique might also be applicable to other thermoelectric materials.

关键词： Thermoelectric (TE) material Cryogenic grinding Bi2Te3 Nanoparticles Two-step breaking model

来源：

同方期刊数据库评论

在线全文

同方期刊数据库

学校读者我要写书评

暂无评论

霉菌侵蚀前后的皮革的成分变化

引用

中国皮革 2008年第1期37卷 45-47页

作者：胡尚勤刘天贵刘磊峰重庆师范大学生命科学学院重庆400047

为了弄清楚霉菌对皮革侵蚀前后,皮革成分变化及其霉菌产生危害的机理,利用蒽酮比色法、石油醚萃取法、凯氏定氮法与水杨酸比色法、甲醛滴定法,分别对侵蚀前后的皮革样品中糖、脂肪、蛋白质和游离氨基酸含量进行了分析。结果表明:侵蚀前... 详细信息

为了弄清楚霉菌对皮革侵蚀前后,皮革成分变化及其霉菌产生危害的机理,利用蒽酮比色法、石油醚萃取法、凯氏定氮法与水杨酸比色法、甲醛滴定法,分别对侵蚀前后的皮革样品中糖、脂肪、蛋白质和游离氨基酸含量进行了分析。结果表明:侵蚀前皮革样品中的糖、脂肪、蛋白质和游离氨基酸含量分别为0.0603%、4.9%、3.89%、21.0%;侵蚀后的含量分别为0.0155%、2.2%、2.19%、13.5%。霉菌对皮革中的游离氨基酸和脂类的分解利用最明显,其次是对蛋白质和糖的分解。该研究为揭示霉菌侵蚀皮革的机理,提供了可靠的科学依据。

关键词：霉菌皮革侵蚀成分分析

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

鼻内镜辅助低温等离子手术治疗喉神经鞘瘤1例

引用

临床耳鼻咽喉头颈外科杂志 2022年第1期36卷 61-62页

作者：刘磊峰江枫邱海涛王代红惠明朗陈纯柳广东医科大学附属医院耳鼻咽喉头颈外科广东湛江524001

1 病例报告患者,女,68岁,以进行性加重的吞咽梗阻感为主诉,伴有较明显的咽部异物感,吞咽时加重,进流食时出现饮水呛咳,无明显声嘶,无呼吸困难、咽干、咽痒、咽痛,偶有刺激性咳嗽,无咳痰及痰中带血,无反酸嗳气,无消瘦乏力。喉镜检查(图1)... 详细信息

1 病例报告患者,女,68岁,以进行性加重的吞咽梗阻感为主诉,伴有较明显的咽部异物感,吞咽时加重,进流食时出现饮水呛咳,无明显声嘶,无呼吸困难、咽干、咽痒、咽痛,偶有刺激性咳嗽,无咳痰及痰中带血,无反酸嗳气,无消瘦乏力。喉镜检查(图1):左侧杓会厌襞接近披裂处可见一近球形肿物,表面黏膜光滑,2.1 cm×1.5 cm×2.0 cm大小,边界清楚,似带蒂,肿物体积较大挤压至左侧梨状窝内,将左侧杓会厌襞向内推移位.

关键词：喉神经鞘瘤低温等离子手术鼻内镜

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

载中药聚乳酸多孔纳米纤维医用敷料

引用

材料导报 2024年第10期38卷 241-247页

作者：李亮刘淑萍裴斐斐杨雷锋刘让同中原工学院纺织学院郑州451191 先进纺织装备技术省部共建协同创新中心郑州451191 河南省功能纺织材料重点实验室郑州451191 郑州大学第一附属医院郑州450000

为构筑人体可吸收、抗菌消炎且轻薄柔软的可用于伤口愈合的医用敷料,以聚乳酸为原料,掺杂板蓝根(RI)、柴胡(BC)和茶多酚(GTP)等中药成分,采用氯仿与丙酮二溶剂体系,借助静电纺技术制备聚乳酸(PLA)多孔纳米纤维载中药敷料。通过扫描电镜... 详细信息

为构筑人体可吸收、抗菌消炎且轻薄柔软的可用于伤口愈合的医用敷料,以聚乳酸为原料,掺杂板蓝根(RI)、柴胡(BC)和茶多酚(GTP)等中药成分,采用氯仿与丙酮二溶剂体系,借助静电纺技术制备聚乳酸(PLA)多孔纳米纤维载中药敷料。通过扫描电镜、红外光谱仪、X射线衍射仪(XRD)和接触角测试仪等手段分析了载中药敷料的微观结构、润湿性能、保水吸液性、抗菌性以及体外降解性能等。结果表明:采用氯仿和丙酮二溶剂体系制备的载中药敷料其纤维具有多孔特征,纤维直径为747~1 550 nm。敷料中所载板蓝根、柴胡、茶多酚与聚乳酸间并未发生负面改性的化学反应。载板蓝根、柴胡、茶多酚的敷料在载药量为3%时对金黄色葡萄球菌抑菌率分别为79.2%、82.5%、75.7%,对大肠杆菌抑菌率分别为79.1%、80.2%、73.9%。同时,较纯聚乳酸敷料,载中药敷料具有较好的透气性和体外降解性,其保水吸液性均提高20%以上,适合用作伤口敷料。

关键词：多孔聚乳酸纳米纤维板蓝根茶多酚柴胡敷料抗菌性能

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

复杂性食管异物的诊疗现状

引用

国际耳鼻咽喉头颈外科杂志 2018年第5期42卷 297-301页

作者：李飞刘磊峰姚俊广东医科大学附属医院耳鼻咽喉头颈外科湛江524001

食管异物是耳鼻咽喉头颈外科常见的临床急症之一，而复杂性食管异物是食管异物伴有严重并发症且好发于儿童和老年患者的一类可危及患者生命的疾病，其治疗十分复杂，严重影响患者的健康和生活质量，不仅增加相应的医疗成本，更增加了临... 详细信息

食管异物是耳鼻咽喉头颈外科常见的临床急症之一，而复杂性食管异物是食管异物伴有严重并发症且好发于儿童和老年患者的一类可危及患者生命的疾病，其治疗十分复杂，严重影响患者的健康和生活质量，不仅增加相应的医疗成本，更增加了临床医疗事件的风险。本文主要从食管异物的发病特点及不同类型复杂性食管异物的诊治现状做一综述，以引起临床上对该疾病高度重视和有效的治疗以及预防。

关键词：异物食管穿孔

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

尖锐食管异物致颈部游走性异物的诊治体会

引用

临床耳鼻咽喉头颈外科杂志 2019年第11期33卷 1068-1071页

作者：刘磊峰邱海涛江枫陈立航李飞姚俊广东医科大学附属医院耳鼻咽喉头颈外科广东湛江524001 广东医科大学附属医院放射科

目的:探讨尖锐食管异物穿透食管壁,形成颈部游走性异物的临床表现、影像学表现及治疗方法。方法:9例患者均为异物史明确,消化道造影或胃镜检查未发现食管内异物,经颈部CT检查后发现异物已游走于食管外颈部软组织内,8例患者成功取出异物,... 详细信息

目的:探讨尖锐食管异物穿透食管壁,形成颈部游走性异物的临床表现、影像学表现及治疗方法。方法:9例患者均为异物史明确,消化道造影或胃镜检查未发现食管内异物,经颈部CT检查后发现异物已游走于食管外颈部软组织内,8例患者成功取出异物,1例术中未发现明确异物。结果:9例患者中,8例患者成功取出异物未出现咽瘘等并发症。1例患者术中未发现明确异物,术后出现气管食管瘘,带胃管出院。结论:对于有明确异物史的患者,消化道造影或胃镜检查有可能表现为阴性,应及时行颈部或胸部增强CT检查,排除食管外异物。CT检查尤其是增强扫描对于食管外游走性异物的诊断及定位至关重要,同时可以准确的判断异物与重要组织及血管间的关系,对于异物成功取出及降低并发症产生具有指导性意义。

关键词：食管穿孔颈部异物诊断治疗

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

复杂性食管异物的临床诊疗分析

引用

山东大学耳鼻喉眼学报 2019年第6期33卷 85-89页

作者：李飞姚俊刘磊峰广东医科大学研究生院广东湛江524001 广东医科大学附属医院耳鼻咽喉头颈外科广东湛江524001

目的探讨复杂性食管异物伴发严重并发症的种类及特点,总结其临床诊断及治疗方法。方法对广东医科大学附属医院2015年1月至2018年1月住院治疗的244例食管异物中22例伴有严重并发症的患者资料进行回顾性分析,包括发患者群、就诊时间、异... 详细信息

目的探讨复杂性食管异物伴发严重并发症的种类及特点,总结其临床诊断及治疗方法。方法对广东医科大学附属医院2015年1月至2018年1月住院治疗的244例食管异物中22例伴有严重并发症的患者资料进行回顾性分析,包括发患者群、就诊时间、异物类型及嵌顿位置、并发症类型及诊断治疗方式等。结果22例中除4例儿童外,其余患者均在发病后通过进食馒头、蔬菜、努力吞咽等方式,试图将异物强行推入胃中未果,从而出现严重并发症;从发病到就诊最长达32 d,平均5.9 d;误吞异物类型中17例(77.3%)为动物性骨头,以鱼骨和鸡骨为主;10例嵌顿于食管入口水平,5例嵌顿于T1-T2水平,3例嵌顿于T8-T9水平;严重并发症包括食管穿孔或合并食管局部炎症6例(27.3%),颈部及纵隔气肿、脓肿5例(22.7%),食管纵隔瘘4例(18.2%),游走于食管外异物3例(13.6%),咽后壁脓肿1例(4.5%),气胸1例(4.5%),气管食管瘘1例(4.5%),食管主动脉瘘1例(4.5%);14例于食管镜下取出异物,3例经颈侧切开探查取出异物,3例同时行颈部及纵隔脓肿切开引流术,1例行食管镜+胸腔镜探查,并行肺大泡切除术,1例行支气管镜异物取出术+气管食管瘘修补术;22例患者中治愈21例(95.5%),平均住院时间为6.2 d,死亡1例(4.5%)。结论复杂性食管异物多见于老年患者,多因发生异物嵌顿后患者错误的暴力吞咽方式、不及时就医等不恰当处理方法,导致了患者病情的延误。异物的类型、嵌顿位置及就医时间与并发症的产生及严重程度呈正相关,上消化道造影及CT检查是诊断食管异物及其并发症的最有效方法,能够清楚地显示出异物与周围重要组织器官的关系,多学科协助治疗是挽救严重并发症引起危重病情的重要方式。

关键词：食管异物食管穿孔纵隔脓肿气管食管瘘

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

在线全文

在线全文

在线全文

在线全文

在线全文

在线全文

在线全文

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

在线全文

在线全文

在线全文

在线全文

在线全文

在线全文

在线全文

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：