Surface Characteristics of Mussel-inspired Polydopamine Coating on Titanium Substrates

Journal of Wuhan University of Technology(Materials Science) 2014年第1期29卷 197-200页

作者：姜玲 JIN Guangchun KANG Jiyeon YU Lingmin YOON Wookang lim myungjin PAR K Ilsong LEE Minho JIN Dongchun Yantai Affiliated Hospital of Binzhou Medical University Oral Medical College Beihua University Department of Oral and Maxillofacial Surgery Hallym University Dongtan Sacred Heart Hospital Department of Dental Biomaterials and Institute of Oral Bioscience School of Dentistry BK21 Project Chonbuk National University Department of Veterinary Yanbian University

Mussel adhesive proteins are non-toxic, biodegradable and have low immunogenic qualities that make them highly attractive for medical purposes compared with man-made materials. 3,4-DOPA, which is a dopamine precursor, is a critical element for achieving mussel-like adhesive properties. In present study, polydopamine was coated onto the titanium surfaces by dipping in a 2 mg/mL dopamine solution in 10 mM Tris- HCl buffer at pH 8.5. EDX element analysis and Raman spectroscopic analysis of the surface were conducted to verify the formation of polydopamine. The surface characteristics of polydopamine-coated titanium plates were observed by SEM and AFM. Hydrophilicity and corrosion-resistance were also evaluated by static contact angle measurements and potentiodynamic polarization corrosion tests. The absorption intensity for pH-induced polymerization rapidly increased for the initial four hours and thereafter smoothly increased. EDX element analyses revealed that the content of carbon and oxygen increased and the content of titanium decreased after the coating process. In the Raman spectra, polydopamine resulted in two new peaks at approximately 1 370 and 1 570 cm^-1 resulting from the stretching and deformation of catechol. Microstructural features revealed that nanometer-sized bright granules were randomly distributed after coating, and these nanoparticles grew with increased coating time. The Ra values of polydopamine-coated titanium plates were showed to increase with coating time. Compared to the pure titanium curve, the inflection point of polydopamine-coated titanium was located at a higher corrosion potential and lower corrosion current density. Findings from our research suggested that polydopamine coatings offer a versatile approach for titanium surface modification.

关键词： surface modification titanium polydopamine surface characteristics

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：