Structures and physical properties of rigid polyurethane foams with water as the sole blowing agent

Science china Chemistry 2006年第4期49卷 363-370页

作者： li xiaobin1.2. cao hongbin1.& zhang yi1.1. institute of process engineering, Chinese Academy of Sciences,{1.,{2. 2. Graduate School of the Chinese Academy of Sciences, beijing 1.0039,{2. institute of {1. {2. Chinese Academy of Sciences Beijing China Graduate School of the Chinese Academy of Sciences Beijing China

Rigid polyurethane foams blown by varying water level were prepared in this study. The structures and physical properties of rigid polyurethane foams blown by water were measured with FT-IR, universal testing machine (Instron3365), scanning electron microscope (SEM) and differential scanning calorimeter (DSC). The results show that polyurea and polybiuret were the typical charac- teristics, and the cream time and gel time were shorter for the fully water blown rigid foams than that for the fully cyclopentane blown foams. The density of foam samples decreased from 45.0 kg/m3 to 2..4 kg/m3 with the increase of water level from 3 pph to 7 pph. Compressive strength exhibited the similar behavior with density. The average cell size of foam samples ranged from 2.1.μm to 356 μm with the increase of water level from 3 pph to 7 pph, respectively. At the same time, poorer dimen- sional stabi{1.ty was encountered with the increase of average cell size due to fast diffusion rate of CO2.out of the foam. The results of thermal analysis show that the glass transition temperature (Tg) shifted to a higher temperature with the increase of isocyanate level when more water was used as chemical blowing agent.

关键词： polyether polyol, polyurethane rigid foam, compressive strength, dimensional stability, cell size, glass transition temperature.

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：