Microwave gel combustion synthesis and sinterability of Nd:GGG nanopowders

Journal of Rare Earths 2014年第6期32卷 521-525页

作者： kiranmala laishram Rekha Mann Neelam Malhan Laser Materials Division Laser Science and Technology Centre DRDO

Neodymium doped gadolinium gallium oxide （Nd：GGG） nanopowders synthesized by microwave gel combustion using alanine as a fuel was reported. Metal nitrates solution with alanine fuel was combusted in microwave to give precursor. The micro-wave precursor powder was calcined at different temperatures from 800 to 1100 ℃. Phase pure Nd：GGG formation took place at 800 to 1100 ℃ as observed by X-ray diffraction （XRD） and Fourier transform infra-red （FTIR） spectroscopy. However particle size in-creased with calcinations temperature from 25 nm at 800 ℃ to 200 nm at 1100 ℃.Nd：GGG nanopowder obtained at different calci-nation temperatures were compacted and sintered at 1550 ℃ for 3 h in air. Most densified ceramic was obtained from Nd：GGG nanopowder calcined at 1100 ℃. Microstructure as observed from scanning electron microscopy （SEM） showed that the most densi-fied ceramic, obtained from nanopowder calcined at a higher calcination temperature, had a more uniform grain-size distribution, fewer pores and greater densification. XRD of sintered sample showed retention of phase purity.

关键词： Nd:GGG microwave gel combustion calcinations densification rare earths

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

Single step low temperature synthesis of gadolinium gallium garnet nanopowders

引用

Journal of Rare Earths 2012年第6期30卷 545-547页

作者： Rekha Mann kiranmala laishram Neelam Malhan Laser Materials Division Laser Science and Technology CentreDRDOMetcalfe House Delhi-110054India

Solution combustion synthesis of single-phase gadolinium gallium oxide （Gd3GasO12, GGG） nanopowders, by a fuel mixture approach using urea and glycine at a low temperature of 500 ℃, was being reported for the first time. Based on the fact that urea and glycine are good fuels for gallium oxide and gadolinium oxide synthesis, the fuel mixture composition was obtained, which could lead to direct phase pure cubic Gd3Ga5O12 formation without any subsequent calcination step. Combustion was carried out in furnace pre-heated at 500 ℃. Thermogravimetric analysis （TGA） of combustion product showed negligible mass loss indicating direct formation of GGG powder. Fourier transform infrared （FTIR） spectrum of combusted product showed peak characteristic of GGG in case of mixed fuel. X-ray diffraction （XRD） confirmed formation of phase pure GGG at 500 ℃ in preheated furnace. Very fine, well dispersed nanometric particles of size range of 50-100 nm were obtained, being uniform and close to spherical morphology as observed by transmission electron microscope （TEM）.

关键词： direct synthesis solution combustion GGG mixed fuel calcinations free rare earths

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：