Orange dye polyaniline composite based impedance humidity sensors

Chinese Physics B 2013年第1期22卷 161-166页

作者： Muhammad Tariq Saeed Chani Kh. S. Karimov F. A. khalid S. Z. Abbas M. B. Bhatty GIK Institute of Engineering Sciences and Technology Topi 23640 Khyber Pakhtunkhwa Pakistan Center of Excellence for Advanced Materials research (CEAMr) King Abdulaziz University Jeddah 21589 P.O. Box 80203 Saudi Arabia Physical Technical Institute Aini St. 299/1 Dushanbe 734063 Tajikistan

This study presents the fabrication and investigation （PANI） composite films. A blend of 3 wt.% OD with 1 of humidity sensors based on orange dye （OD） and polyaniline wt.% PANI was prepared in 1 ml water. The composite films were deposited on glass substrates between pre-deposited silver electrodes. The gap between the electrodes was 45 um. The sensing mechanism was based on the impedance and capacitance variations due to the absorption/desorption of water vapor. It was observed that with the increase in relative humidity （rH） from 30% to 90%, the impedance decreases by 5.2 × 10^4 and 8.8 × 10^3 times for the frequencies of 120 Hz and 1 kHz, respectively. The impedance-humidity relationship showed a more uniform change compared to the capacitance-humidity relationship in the rH range of 30% to 90%. The consequence of annealing, measuring frequency, response and recovery time, and absorption-desorption behavior of the humidity sensor were also discussed in detail. The annealing resulted in an increase in sensitivity of up to 2.5 times, while the measured response time and recovery time were 34 s and 450 s, respectively. The impedance-humidity relationship was simulated.

关键词： organic-organic composite humidity sensor polyaniline orange dye

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

Effects of friction stir processing and nano-hydroxyapatite on the microstructure,hardness,degradation rate and in-vitro bioactivity of WE43 alloy for biomedical applications

引用

Journal of Magnesium and Alloys 2024年第1期12卷 209-224页

作者： Bo Wu Farazila Yusof Fuguo Li Huan Miao A.r.Bushroa Mohd ridha Bin Muhamad Irfan Anjum Badruddin Mahmoud Z.Ibrahim Department of Mechanical Engineering Faculty of EngineeringUniversiti MalayaKuala Lumpur 50603Malaysia Centre of Advanced Manufacturing and Material Processing(AMMP Centre) Universiti MalayaKuala Lumpur 50603Malaysia Center of Foundation studies in Science Universiti MalayaKuala Lumpur 50603Malaysia State Key Laboratory of Solidification Processing School of Materials Science and EngineeringNorthwestern Polytechnical UniversityXi’an 710072China Mechanical Engineering Department College of EngineeringKing Khalid UniversityAbha 61421Saudi Arabia Design and Production Engineering Faculty of EngineeringAin Shams UniversityCairo 11517Egypt

Nowadays,magnesium alloys are emerging in biomedical implants for their similar properties to natural ***,the rapid degradation of magnesium alloys in biological media hinders successful *** of microstructure,as well as reinforcement particles can significantly improve the degradation *** this work,multi-pass friction stir processing(FSP)was proposed to synthesize WE43/nano-hydroxyapatite(n HA)surface composite,the microstructure,reinforced particle distribution,micro-hardness,corrosion behavior and in-vitro bioactivity were *** subsequent FSP passes of WE43 alloy and WE43/n HA composite refined the grain size which was reduced by 94.29%and 95.92%(2.63 and 1.88μm,respectively)compared to base metal after three *** resulted in increasing the microhardness by 120%(90.86 HV0.1)and 135%(105.59 HV0.1)for the WE43 and WE43-n HA,*** is found that increasing FSP passes improved the uniform distribution of n HA particles within the composite matrix which led to improved corrosion resistance and less degradation *** corrosion rate of the FSPed WE43/n HA composite after three passes was reduced by 38.2%(4.13 mm/year)and the degradation rate was reduced by 69.7%(2.87 mm/y).This is attributed to secondary phase(Mg24Y5and Mg41Nd5)particle fragmentation and redistribution,as well as a homogeneous distribution of n ***,the growing Ca-P and Mg(OH)2layer formed on the surface represented a protective layer that reduced the degradation *** wettability test revealed a relatively hydrophilic surface with water contact angle of 49.1±2.2°compared to 71.2±2.1°for base ***,biomineralization test showed that apatite layer grew after immersion 7d in simulated body fluid with atomic ratio of Ca/P 1.60 approaching the stoichiometric ratio(1.67)indicating superior bioactivity of FSPed WE43/n HA composite after three *** results raise that the grain refinement by FSP and introduction of n HA partic

关键词： Friction stir processing Magnesium-based composite Nano-hydroxyapatite Corrosion behavior In-vitro bioactivity

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：