Accessory ligand strategies for hexacyanometallate networks deriving perovskite polycrystalline electromagnetic absorbents

在线全文

学校读者我要写书评

暂无评论

Journal of Materials Science & Technology 2021年第23期82卷 69-79页

作者： Zhenguo Gao Zehao Zhao Di Lan kaichang kou Jiaoqiang Zhang Hongjing Wu School of Chemistry and Chemical Engineering Northwestern Polytechnical UniversityXi’an710072China MOE Key Laboratory of Material Physics and Chemistry Under Extraordinary School of Physical Science and TechnologyNorthwestern Polytechnical UniversityXi’an710072China

The controllable adjustment of electromagnetic(EM)properties for high-efficiency EM absorbents are indispensable,nonetheless,rare in crystals engineering ***,for the first time,regulated amount of sodium citrate was employed as accessory ligand of cobalt cation in aqueous solution to kinetically assist the controllable fabrication of Prussian blue analogs(PBAs)and corresponding lanthanide perovskite hybrid Co Fe alloy ***,the multi-phase features were analyzed based on Rietveld refinement of XRD patterns,illustrating the existence of distortions,defects and heterogeneous interfaces in resultant *** to the dielectric and magnetic adjustment,polycrystalline absorbents achieved excellent impedance matching and EM attenuation,as the minimum reflection loss of Co Fe/La FeO_(3)and Co Fe/La FeO_(3)/La_(2)O_(3)reached-44.13 and-33.95 d B,ranking broadest effective bands up to 4.88 and 3.36 *** validity of the strategy provided a novel sight into the controllable fabrication of high-performance magnetic semiconductor polycrystalline devices.

关键词： Sodium citrate Prussian blue analogs Polycrystalline Electromagnetic absorption Interfacial polarization

Preparation and Properties of Nano-SiO_2/TDE-85/BMI/BAD Cy Composites

在线全文

学校读者我要写书评

暂无评论

Journal of Wuhan University of Technology(Materials Science) 2013年第2期28卷 261-264页

作者：吴广磊 kou kaichang CHAO Min ZHUO Longhai ZHANG Jiaoqiang School of Science Northwestern Polytechnical University

A new type of the nanometer particles and epoxy/bismaleimide-triazine nanocomposites were prepared using a nanometer silica （nano-SiO2）, a 4,5-epoxycyclohexane 1,2-dicarboxylic acid dilycidyl （TDE-85） epoxy resin, a 4,4＇-bismaleimidodiphenymethane （BMI） and a bisphenol a dicyanate （BADCy）. The properties of nano-SiOJTDE-85/BMI/BADCy composites, such as mechanical and thermal properties, were systemically investigated in detail by mechanical measurement, scanning electron microscope （SEM）, dynamic mechanical analysis （DMA） and thermogravimetric analysis （TGA）. The experimental results showed that the addition of the appropriate amount of nano-SiO： could improve the impact strength and the flexural strength of the nano- SiO2/TDE-85/BMI/BADCy composites. Simultaneously, the thermal stability of the blends was found to be higher than that of the TDE-85/BMI/BADCy copolymers.

关键词： nano-Si02 cyanate ester resin epoxy resin bismaleimide resin mechanical properties thermal properties

Preparation and Microwave Absorbing Characteristics of Multi-Walled Carbon Nanotube/Chiral-Polyaniline Composites

在线全文

学校读者我要写书评

暂无评论

Open Journal of Polymer Chemistry 2014年第3期4卷 62-72页

作者： Jiaoqiang Zhang Changming Shi Tiezheng Ji Guanglei Wu kaichang kou Key Laboratory of Space Applied Physics and Chemistry of Ministry of Education Department of Applied Chemistry School of Science Northwestern Polytechnical University Xi’an China

The multi-walled carbon nanotubes (MWCNTs)/chiral-polyaniline composite was synthesized by in-situ chemical polymerization. Morphology, structure as well as thermal stability of the hybrid composites were characterized by using various techniques. Moreover, the complex permeability, permittivity, and microwave absorbing characteristics of the MWCNTs/chiral-polyaniline composites have been studied. Compared with those of the polyaniline (PANI) and MWCNTs, the real part () and imaginary part () of the complex permittivity as well as dielectric dissipation factor of the MWCNTs/chiral-PANI composites were much greater, while the real part () and imaginary part () of the complex permeability and the magnetic dissipation factor were smaller. The results indicate that the microwave absorption of MWCNTs/chiral-PANI composites was mainly attributed to the dielectric loss rather than magnetic loss.

关键词： Conducting Polymers Composites Dielectric Properties Properties and Characterization Thermogravimetric Analysis (TGA)

维普期刊数据库评论

在线全文

维普期刊数据库

学校读者我要写书评

暂无评论

共聚法引入甲基对聚苯胺结构及电导率的影响

材料导报 2013年第10期27卷 1-4页

作者：颜海燕寇开昌西北工业大学理学院西安710072

通过间甲基苯胺与苯胺在右旋樟脑磺酸水性介质中进行化学氧化共聚得到它们各自的均聚物及共聚物,在聚苯胺链段上引入甲基来改变产物的结构与电导率。用FT-IR、UV-Vis、XRD、SEM方法表征聚合物的分子链结构与微观形貌,用四探针法测定聚... 详细信息

通过间甲基苯胺与苯胺在右旋樟脑磺酸水性介质中进行化学氧化共聚得到它们各自的均聚物及共聚物,在聚苯胺链段上引入甲基来改变产物的结构与电导率。用FT-IR、UV-Vis、XRD、SEM方法表征聚合物的分子链结构与微观形貌,用四探针法测定聚合物电导率。结果表明,所得聚合物为直径100nm左右的短纤维,聚苯胺分子链上甲基的引入削弱了苯环之间的π-π共轭,使FT-IR、UV-Vis光谱特征峰发生蓝移。在单体总浓度一定的条件下,可通过调节单体比例将聚合物的电导率控制在0.02～6.50S/m的范围内。XRD谱图分析表明,甲基还具有诱导聚苯胺分子链取向的作用,使聚苯胺链聚集态规整性提高。

关键词：聚苯胺间甲基苯胺共聚电导率

在线全文

学校读者我要写书评

暂无评论

微螺旋炭纤维结构性能的研究

材料导报 2007年第5期21卷 118-120,128页

作者：毕辉寇开昌张教强西北工业大学理学院应用化学系西安710072

微螺旋炭纤维因其特殊的三维手性结构,具有多种优异性能。综述了微螺旋炭纤维的微观形貌、力学性能、电性能、热性能、吸波性能和储气性能,并展望了螺旋炭纤维的应用前景,同时也总结了螺旋炭纤维研究中存在的问题。

关键词：螺旋炭纤维化学气相沉积性能

接结纱经向间距对EP/CFSF复合材料性能的影响

在线全文

学校读者我要写书评

暂无评论

工程塑料应用 2017年第4期45卷 39-43页

作者：张鹏飞寇开昌西北工业大学理学院西安710129 陕西出入境检验检疫局西安710068

基于不同接结纱经向间距的设计,研究了不同接结纱经向间距对环氧树脂(EP)/碳纤维间隔织物(CFSF)复合材料的力学性能、电学性能的影响规律,结合扫描电子显微镜,分析经向间距对复合材料性能的影响机制。结果表明,随着接结纱经向间距的增加... 详细信息

基于不同接结纱经向间距的设计,研究了不同接结纱经向间距对环氧树脂(EP)/碳纤维间隔织物(CFSF)复合材料的力学性能、电学性能的影响规律,结合扫描电子显微镜,分析经向间距对复合材料性能的影响机制。结果表明,随着接结纱经向间距的增加,EP/CFSF复合材料的冲击强度和弯曲强度减小,韧性减弱,电阻率增大。当接结纱经向间距为4 mm时,复合材料具有较佳的综合性能,其冲击强度为13.5 k J/m^2,弯曲强度为121.30 MPa,导电性能最好,电阻率为0.077Ω·m。

关键词：碳纤维环氧树脂接结纱经向间距力学性能电学性能

MoSi_2-WSi_2复合体系的自蔓延燃烧合成

在线全文

学校读者我要写书评

暂无评论

稀有金属材料与工程 2000年第3期29卷 190-192页

作者：寇开昌杨延清艾云龙陈彦康沫狂西北工业大学材料科学与工程学院西安710072

利用自蔓延燃烧合成法制备了 Mo Si2 - WSi2 复合粉体 ,并对合成产物进行了 X射线衍射分析。研究表明 ,通过自蔓延燃烧合成反应既可实现 Mo Si2 与 WSi2 的复合 ,又可通过调整反应物 Mo,W,Si的比例 ,在 Mo Si2 中引入 WSi2的同时还能引... 详细信息

利用自蔓延燃烧合成法制备了 Mo Si2 - WSi2 复合粉体 ,并对合成产物进行了 X射线衍射分析。研究表明 ,通过自蔓延燃烧合成反应既可实现 Mo Si2 与 WSi2 的复合 ,又可通过调整反应物 Mo,W,Si的比例 ,在 Mo Si2 中引入 WSi2的同时还能引入足够量的 Mo5 Si3- W5 Si3相。W量的增加使体系的绝热温度降低 ,对自蔓延燃烧合成反应产生影响。研究还表明 Mo Si2 - WSi2 和 Mo5 Si3- W5 Si3均以固溶体的形式存在。

关键词：自蔓延燃烧合成 MoSi2-WSi2 绝热温度

氟橡胶-金属黏接用环氧树脂胶黏剂的黏接性能与黏接机理

在线全文

学校读者我要写书评

暂无评论

合成橡胶工业 2008年第1期31卷 58-61页

作者：颜录科寇开昌哈恩华西北工业大学理学院应用化学系陕西西安710072 北京航空材料研究院北京100095

用具有高热变形温度的砜类聚合物制备的增黏剂配制了氟橡胶与金属黏接用环氧树脂胶黏剂,研究了胶黏剂的黏接性能及其影响因素。结果表明,增黏剂的适宜用量为30～50质量份,用于胺类硫化氟橡胶与金属黏接时的平均拉伸剪切强度为8～10 MPa... 详细信息

用具有高热变形温度的砜类聚合物制备的增黏剂配制了氟橡胶与金属黏接用环氧树脂胶黏剂,研究了胶黏剂的黏接性能及其影响因素。结果表明,增黏剂的适宜用量为30～50质量份,用于胺类硫化氟橡胶与金属黏接时的平均拉伸剪切强度为8～10 MPa。差示扫描量热法的研究表明,增黏剂不仅促进了胶黏剂与金属的黏接,还参与了氟橡胶的黏合与硫化反应,固化剂双氰胺及其分解产物单氰胺均属于伯胺,易于向树脂内扩散,也易于向橡胶层扩散,不但可与环氧基进行加成反应,而且与氟橡胶在黏接界面处生成配位键,从而改善了与氟橡胶的黏接性能。

关键词：氟橡胶金属环氧树脂胶黏剂增黏剂黏接机理

硅烷偶联剂对聚苯胺/Fe_3O_4复合材料结构与性能的影响

在线全文

学校读者我要写书评

暂无评论

塑料科技 2008年第7期36卷 70-73页

作者：颜海燕寇开昌西安工业大学材料与化工学院陕西西安 710032 西北工业大学理学院化工系陕西西安 710072

利用原位复合法制备了聚苯胺(PANI/)/Fe3O4复合材料,运用紫外光谱、扫描电镜、四探针电阻率仪等测试方法研究了硅烷偶联剂KH-550对PANI/Fe3O4复合材料结构及性能的影响。结果表明:经KH-550处理后的PANI/Fe3O4复合材料的微粒不易团聚,其... 详细信息

利用原位复合法制备了聚苯胺(PANI/)/Fe3O4复合材料,运用紫外光谱、扫描电镜、四探针电阻率仪等测试方法研究了硅烷偶联剂KH-550对PANI/Fe3O4复合材料结构及性能的影响。结果表明:经KH-550处理后的PANI/Fe3O4复合材料的微粒不易团聚,其电导率比未经处理的PANI/Fe3O4复合材料高约1个数量级,且随热处理温度的升高,复合材料的电导率降低,由半导体变为绝缘体;KH-550影响PANI与Fe3O4之间的电荷作用,使复合材料的紫外光谱特征吸收峰产生了一定的位移。

关键词：聚苯胺硅烷偶联剂复合材料电导率