Al_2O_3-Coated Nano-SiC Particles Reinforced Al_2O_3 Matrix Compo.ites

Journal of Materials Science & Technology 2002年第6期18卷 541-543页

作者： juxian zhang, jinjun feng and longqiao gaobeijing vacuum electronics research institute, po. box 749 ext. box 33, beijing 100016, china beijing vacuum Electron. Res. Inst. PO Box 749 Beijing 100016 China

Properties of Al2O3-coated nano-SiC have been compared with those of as-received SiC. The isoelectric po.nt (IEP) of SiC changed from pH3.4 to pH7.3 after coating with the alumina precursor, which is close to that of alumina. Because both surfaces of coated SiC and AI2O3 po.sess higher po.itive charge at pH=4.5-5.0, they are uniformly dispersed in the two-phase aqueous suspensions, Then a mixed po.der containing nano-SiC dispersed homogeneously into the Al2O3 matrix was achieved from flocculating the two-phase suspension. Finally, Al2O3/SiC nanocompo.ites were obtained by coating nano-SiC with Al2O3, in which the majority of SiC particles were located within the AI2O3 grains. The observation by transmission electron microscopy (TEM) and the analysis by the X-ray photoelectron spectroscopy (XPS) showed that cracks propagated towards the intragranular SiC rather than along grain boundaries.

关键词： Coated nano-SiC Colloidal processing Nanocompo.ites Intragranular structure Transgranular fracture

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：