Physical and mechanical characteristics of composite briquette from coal and pretreated wood fines

International Journal of Coal Science & Technology 2021年第5期8卷 1088-1098页

作者： Adekunle Adeleke jamiu odusote Peter Ikubanni Olumuyiwa Lasode Madhurai Malathi Dayanand Pasawan Department of Mechanical Engineering Landmark UniversityOmu-AranNigeria Department of Materials and Metallurgical Engineering University of IlorinIlorinNigeria Department of Mechanical Engineering University of IlorinIlorinNigeria Metal Extraction and Recycling Division National Metallurgical LaboratoryJamshedpurIndia

Melina wood torrefied at 260℃ for 60 min was agglomerated with lean grade coal fines into composite briquettes using pitch as *** biomass(3%-20%)and coal fines(80%-97%)were blended together to produce the composite briquettes under a hydraulic press(28 MPa).The briquettes were cured at 300℃.Density,water resistance,drop to fracture,impact resistance,and cold crushing strength were evaluated for the composite *** proximate,ultimate,and calorific value analyses were carried out according to different ASTM *** studies were carried out using scanning electron microscope and electron probe microanalyzer equipped with energy dispersive *** Transform Infrared Spectrophotometer(FTIR)was used to obtain the functional groups in the raw materials and *** density of the composite briquettes ranged from 0.92 to 1.31 g/cm^(3) after *** with95%).The highest cold crushing strength of 4 MPa was obtained for briquettes produced from 97%coal fines and 3%torrefied *** highest drop to fracture(54 times/2 m)and impact resistance index(1350)were obtained for the sample produced from 97%coal and 3%torrefied *** fixed and elemental carbons of the briquettes showed a mild improvement compared to the raw *** peaks from FTIR spectra for the briquettes shows the presence of aromatic C=C bonds and phenolic OH *** composite briquettes with up to 20%torrefied biomass can all be useful as fuel for various applications.

关键词： Composite briquettes Lean grade coal Torrefied biomass Physico-mechanical properties Combustion properties

来源：

维普期刊数据库评论

在线全文

维普期刊数据库

学校读者我要写书评

暂无评论

Evaluation of Corrosion Behaviour of Grey Cast Iron and Low Alloy Steel in Cocoa Liquor and Well Water

引用

Journal of Minerals and Materials Characterization and Engineering 2013年第2期1卷 44-48页

作者： John Oluyemi Olawale jamiu Kolawole odusote Abuldkarim Baba Rabiu Emmanuel Onazi Ochapa Department of Materials Science and Engineering Obafemi Awolowo University Ile-Ife Nigeria Department of Mechanical Engineering University of Ilorin Ilorin Nigeria

Corrosion behaviour of cast iron and low alloy steel in cocoa liquor and well water was investigated. The average weight losses of the specimens were measured using digital weighing balance. The results showed that the weight losses of both cast iron and low alloy steel in both media increases with time. Corrosion rate of cast iron in cocoa liquor increases rapidly with time for up to 336 hours (1000 μm/yr), but in well water the rapid rate of corrosion only lasted up to 187 hours (1160 μm/yr) thereafter it continuously dropping until 264 hours (667 μm/yr) after which it remains constant. Low alloy steel corroded faster in cocoa liquor up to 264 hours (200 μm/yr), whereas the initial rapid corrosion rate only lasted up to 168 hours (180 μm/yr) in well water environment. The results revealed that low alloy steel exhibited better corrosion resistance in both media, with cocoa liquor been more aggressive. Thus, low alloy steel will be a better material for piping and pumping system in cocoa processing industries.

关键词： Corrosion Grey Cast Iron Low Alloy Steel Cocoa Liquor Well Water

来源：

维普期刊数据库评论

在线全文

维普期刊数据库

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：