Journal of Advanced Ceramics 2019年第1期8卷 39-46页

作者： Shile CHEN Mengting CHENG Ying LANG Chuanjin TIAN hongkang wei Chang-An Wang School of Materials Science and Engineering Jingdezhen Ceramic Institute State Key Laboratory of New Ceramics and Fine Processing School of Materials Science and Engineering Tsinghua University

The α-Fe_2 O_3@SiO_2 reddish pigments with core-shell structure were successfully prepared by hydrothermal and Stober methods. The structure, morphology, and chromaticity of the synthesized pigments were characterized by XRD, SEM, TEM, FTIR, XPS, and colorimetry. The results indicated that the as-prepared pigments have the characteristics of narrow particle size distribution, high dispersion,and good sphericity. The α-Fe_2 O_3@SiO_2 reddish pigments were uniform and well dispersed in solution. In addition, the pigments with different shell thickness were also prepared, and the effect of shell thickness on the color performance of the pigments was discussed.

关键词： Fe2O3@SiO2 pigments core-shell structure monodispersed spherical

在线全文

学校读者我要写书评

暂无评论

氮化硼晶须氮化工艺及其生长机理(英文)

硅酸盐学报 2014年第7期42卷 831-835页

作者：赵林魏红康谢志鹏汪长安景德镇陶瓷学院材料科学与工程学院景德镇333403 清华大学新型陶瓷与精细工艺国家重点实验室北京100084

通过氮化由三聚氰胺和硼酸为原料制备的氮化硼晶须前驱体制备出氮化硼晶须,并采用扫描电子显微镜、X射线衍射仪、红外光谱仪和热分析仪对氮化硼晶须氮化工艺进行研究,同时对氮化硼晶须的生长机理进行探讨。结果表明:当升温速率5℃/min... 详细信息

通过氮化由三聚氰胺和硼酸为原料制备的氮化硼晶须前驱体制备出氮化硼晶须,并采用扫描电子显微镜、X射线衍射仪、红外光谱仪和热分析仪对氮化硼晶须氮化工艺进行研究,同时对氮化硼晶须的生长机理进行探讨。结果表明:当升温速率5℃/min、氮气流量0.2L/min、氮化温度1 700℃、保温时间30min时可制备出长径比高、性能优良的氮化硼晶须。氮化硼晶须的生长机理可归纳为前驱体脱水、聚合反应、无机化反应和晶相转变等过程。

关键词：氮化硼晶须氮化生长机理

溶胶-凝胶法制备NASICON型Li_(1.15)Y_(0.15)Zr_(1.85)(PO_4)_3固态电解质

在线全文

学校读者我要写书评

暂无评论

硅酸盐学报 2015年第3期43卷 276-279页

作者：刘美景魏红康李玉涛汪长安景德镇陶瓷学院材料科学与工程学院江西景德镇333000 清华大学材料学院新型陶瓷与精细工艺国家重点实验室北京100084

以碳酸锂、硝酸锆、磷酸氢二铵和硝酸钇为原料,柠檬酸为络合剂,采用溶胶–凝胶法制备了NASICON型Li1.15Y0.15Zr1.85(PO4)3固态电解质材料,通过无压烧结和放电等离子烧结(SPS)得到固态电解质片。结果表明:采用无压烧结在1 150℃制备的电... 详细信息

以碳酸锂、硝酸锆、磷酸氢二铵和硝酸钇为原料,柠檬酸为络合剂,采用溶胶–凝胶法制备了NASICON型Li1.15Y0.15Zr1.85(PO4)3固态电解质材料,通过无压烧结和放电等离子烧结(SPS)得到固态电解质片。结果表明:采用无压烧结在1 150℃制备的电解质密度可以达到理论密度的95.2%,在室温下晶粒电导率和总电导率分别为2.19×10–4 S/cm和0.86×10–4 S/cm;采用SPS在1 150℃烧结得到的电解质片密度可达到理论密度的96.8%,在室温下样品总电导为0.97×10–4S/cm,激活能为0.44 e V。四方相Zr O2的存在是样品激活能升高的主要原因。

关键词：溶胶-凝胶法固态电解质离子电导率

流延成型法制备透明氧化铝陶瓷烧结性能的研究

在线全文

学校读者我要写书评

暂无评论

陶瓷学报 2015年第2期36卷 132-137页

作者：赵林刘亮魏红康谢志鹏汪长安景德镇陶瓷学院材料科学与工程学院江西景德镇333403 清华大学新型陶瓷与精细工艺国家重点实验室北京100084

采用流延成型法制备透明氧化铝陶瓷坯片,然后在氢气保护的高温电炉中烧结制备出性能优良的透明氧化铝陶瓷。系统研究了排胶升温速率、固相含量、烧结助剂等工艺参数对透明氧化铝陶瓷烧结性能的影响。分别采用高温综合热分析仪、扫描电... 详细信息

采用流延成型法制备透明氧化铝陶瓷坯片,然后在氢气保护的高温电炉中烧结制备出性能优良的透明氧化铝陶瓷。系统研究了排胶升温速率、固相含量、烧结助剂等工艺参数对透明氧化铝陶瓷烧结性能的影响。分别采用高温综合热分析仪、扫描电子显微镜和紫外-可见分光光度计测试差示扫描量-热重曲线、SEM图和总透光率。实验结果表明:排胶升温速率1℃/min;固相含量55vol.%;烧结助剂Mg(NO3)2、Y(NO3)3、La(NO3)3配比为5M+3Y+3L时可制备出总透光率为73.5%的透明氧化铝陶瓷。

关键词：透明氧化铝烧结助剂固相含量总透光率

Bi_(0.5)Na_(0.5)TiO_(3)和Bi_(0.5)K_(0.5)TiO_(3)含量对三元固溶体系无铅PTC热敏陶瓷性能的影响

同方期刊数据库博看期刊评论

在线全文

学校读者我要写书评

暂无评论

材料导报 2023年第10期37卷 110-115页

作者：赵瑞钰欧阳琪马名生陆毅青魏红康刘志甫景德镇陶瓷大学材料科学与工程学院江西景德镇333403 中国科学院上海硅酸盐研究所上海200050

PTC热敏陶瓷的无铅化是绿色智能加热及电路智能保护元件研制的重要前提。为了获得可在空气气氛下烧结且兼具高居里温度和高升阻比的无铅化PTC热敏陶瓷,本工作采用固相法制备了(1-x)BaTiO_(3)-0.5 x Bi_(0.5)Na_(0.5)TiO_(3)-0.5 x Bi_(0... 详细信息

PTC热敏陶瓷的无铅化是绿色智能加热及电路智能保护元件研制的重要前提。为了获得可在空气气氛下烧结且兼具高居里温度和高升阻比的无铅化PTC热敏陶瓷,本工作采用固相法制备了(1-x)BaTiO_(3)-0.5 x Bi_(0.5)Na_(0.5)TiO_(3)-0.5 x Bi_(0.5)K_(0.5)TiO_(3)和0.98BaTiO_(3)-0.02 y Bi0.5 Na_(0.5)TiO_(3)-0.02(1-y)Bi_(0.5)K_(0.5)TiO_(3)三元固溶体系无铅PTC热敏陶瓷材料,研究了不同含量的Na和K元素对无铅PTC热敏陶瓷材料的烧结特性和电学性能的影响。结果表明,BNT和BKT均与BaTiO_(3)形成固溶体,随着BNT含量的增加,PTC陶瓷平均晶粒尺寸减小,当BNT和BKT含量相同时,PTC陶瓷可以在较宽的烧结温度范围内实现半导化,且在空气气氛下烧结温度为1200℃的陶瓷样品具有最佳的PTC效应,其室温电阻率为128Ω·cm,升阻比为5个数量级,居里温度为142℃。

关键词： PTC陶瓷无铅化钛酸钡三元固溶体系交流阻抗谱

在线全文

学校读者我要写书评

暂无评论

碳化硼SPS烧结致密化行为研究

陶瓷学报 2014年第5期35卷 470-473页

作者：魏红康汪长安谢志鹏邓翔宇景德镇陶瓷学院江西景德镇333403 清华大学北京100084

采用放电等离子烧结工艺,在1600℃下对碳化硼粉末进行烧结。研究了保温时间、烧结压力对碳化硼烧结致密化行为和力学性能的影响,并借助X射线衍射和扫描电镜分析了烧结制品物相组成和微观结构的变化规律。研究结果表明:保温时间和烧结压... 详细信息

采用放电等离子烧结工艺,在1600℃下对碳化硼粉末进行烧结。研究了保温时间、烧结压力对碳化硼烧结致密化行为和力学性能的影响,并借助X射线衍射和扫描电镜分析了烧结制品物相组成和微观结构的变化规律。研究结果表明:保温时间和烧结压力的增加有利于碳化硼的烧结致密化和力学性能的提高。当烧结温度为1500℃-1600℃时,B4C的烧结致密化速率最快。1600℃保温13 min后,试样不再收缩。

关键词：碳化硼放电等离子烧结烧结致密化行为力学性能微观结构

界面缩聚法合成双(烯基环戊二烯基)钛(锆)聚胺的研究

同方期刊数据库博看期刊评论

在线全文

学校读者我要写书评

暂无评论

高分子材料科学与工程 1989年第3期5卷 93-96页

作者：沈宏康魏荣宝林琳梁娅薛其峰天津理工学院化工系元素有机高分子研究室

双(烯基环戊二烯基)钛(锆)二氯化物与二胺类反应制备了一系列新的高分子化合物,并进行了IR、分子量及TGA的测试。文中还对实验参数与分子量关系进行了讨论。

关键词：钛有机聚合物界面缩聚法

在线全文

学校读者我要写书评

暂无评论

以酚醛树脂为碳源合成超细碳化硼粉体的研究

陶瓷学报 2022年第3期43卷 462-468页

作者：李昊展魏红康邱慧娟毛苗妙汪长安谢志鹏景德镇陶瓷大学材料科学与工程学院江西景德镇333403 清华大学新型陶瓷与精细工艺国家重点实验室北京100084

以酚醛树脂和氧化硼为原料,在氩气气氛中合成了超细碳化硼粉体。研究了C与B_(2)O_(3)摩尔比和煅烧温度对合成粉体的物相组成和微观结构的影响。研究结果表明:初始粉料中氧化硼含量的增加有利于提高合成粉体中碳化硼相的纯度。此外,氧化... 详细信息

以酚醛树脂和氧化硼为原料,在氩气气氛中合成了超细碳化硼粉体。研究了C与B_(2)O_(3)摩尔比和煅烧温度对合成粉体的物相组成和微观结构的影响。研究结果表明:初始粉料中氧化硼含量的增加有利于提高合成粉体中碳化硼相的纯度。此外,氧化硼含量和煅烧温度越高,合成的碳化硼粉粒径越大。当C与B_(2)O_(3)摩尔比为1.0:1.0且煅烧温度为1700℃时,合成的碳化硼粒径约为180 nm。对合成粉体进行除碳和除氧化硼处理后,能够得到中位粒径为62 nm且粒径单分散的碳化硼粉体。除碳和除氧化硼处理后的碳化硼粉体在真空气氛中,于1850℃、60 MPa和保温30 min的条件下热压烧结,所得到的碳化硼陶瓷的致密度、弯曲强度和断裂韧性分别为93.27%、304 MPa和4.41 MPa·m^(1/2)。

关键词：碳化硼酚醛树脂亚微米粒径单分散

同方期刊数据库

碳热还原法制备高性能^(10.8)B_4C和^(10)B_4C粉末

在线全文

学校读者我要写书评

暂无评论

陶瓷学报 2014年第4期35卷 372-375页

作者：赵林魏红康张玉军谢志鹏汪长安景德镇陶瓷学院材料科学与工程学院江西景德镇333403 山东大学材料液态结构及其遗传性教育部重点实验室济南250061 清华大学新型陶瓷与精细工艺国家重点实验室北京100084

采用碳热还原法制备出普通碳化硼(10.8B4C)粉末和硼10碳化硼(10B4C)粉末。系统研究了碳源、硼碳比、烧成温度、球磨时间等工艺参数对10.8B4C粉末性能的影响,并分别采用X射线衍射仪和激光粒度仪对其物相组成和粒度分析,实验结果表明:以... 详细信息

采用碳热还原法制备出普通碳化硼(10.8B4C)粉末和硼10碳化硼(10B4C)粉末。系统研究了碳源、硼碳比、烧成温度、球磨时间等工艺参数对10.8B4C粉末性能的影响,并分别采用X射线衍射仪和激光粒度仪对其物相组成和粒度分析,实验结果表明:以碳黑为碳源、硼碳比为6:7、烧成温度1750℃、球磨5 h后可制备出高纯度、中位粒径为2.56 μm的10.8B4C粉末。采用相同的工艺参数可制备出性能优良的10B4C粉末。

关键词：碳热还原碳化硼中位粒径球磨

维普期刊数据库博看期刊

BNp/Si_3N_4和BNw/Si_3N_4多孔复合透波材料性能的比较

在线全文

学校读者我要写书评

暂无评论

中国陶瓷 2016年第10期52卷 54-56,62页

作者：赵林魏红康于美玲谢志鹏汪长安景德镇陶瓷大学材料科学与工程学院景德镇333403 清华大学新型陶瓷与精细工艺国家重点实验室北京100084

采用凝胶注模成型和无压烧结工艺分别制备了BNp/Si_3N_4和BNw/Si_3N_4多孔复合透波材料。采用扫描电子显微镜、X射线衍射仪和矢量网络分析仪等仪器检测了两种材料的微观形貌、物相组成和介电常数等性能,并对其性能进行对比分析。结果表... 详细信息

采用凝胶注模成型和无压烧结工艺分别制备了BNp/Si_3N_4和BNw/Si_3N_4多孔复合透波材料。采用扫描电子显微镜、X射线衍射仪和矢量网络分析仪等仪器检测了两种材料的微观形貌、物相组成和介电常数等性能,并对其性能进行对比分析。结果表明:与BNp/Si_3N_4多孔复合透波材料相比,BNw/Si_3N_4多孔复合透波材料具有更佳的力学性能和介电性能。

关键词： BNp/Si3N4 BNw/Si3N4 多孔透波