Microstructure and mechanical properties of ZrO_2(Y_2O_3)-Al_2O_3 nanocomposites prepared by spark plasma sintering

Particuology 2012年第3期10卷 345-351页

作者： Shufeng Li hiroshi izui Michiharu Okano Weihua Zhang Taku Watanabe College of Science and Technology Nihon University7-24-1NarashinodaiFunabashiChiba 274-8501Japan College of Science and Technology Nihon University1-8-14KandasurugadaiChiyoda.Tokyo 101-8308Japan College of Materials Science and Technology Xi'an University of Technology5 SouthJinhua RoadXi'anShaanxi 710048China

Zirconia （yttria）-alumina ceramic nanocomposites were fabricated from different powders by spark plasma sintering （SPS）. One powder was a commercially available nanocomposite powder TZP-3Y2OA, consisting of 3 mol% yttria-stabilized zirconia （3-YSZ） reinforced with 20wt% alumina, and the other, used as a comparison, was a conventional mechanically mixed powder 3YSZ-2OA, a blend made of 3 mol% yttria-stabilized zirconia powder ZrO2 （3Y） and 20 wt% ,x-alumina powder. The effect of the sintering temperature on the densification, the sintering behavior, the mechanical properties and the microstructure of the composites was investigated. The results showed that the density increased with increasing sintering temperature, and thus, the mechanical properties were strengthened because of the increased densification. The nanocomposite powder TZP-3Y20A was easily sintered, and good mechanical properties were achieved as compared with the powder from the conventional mechanically mixed method, the maximum flexural strength and fracture toughness of which were 967 MPa and 5.27 MPa m 1/2, respectively.

关键词： Zirconia-aluminaNanocompositeSpark plasma sintering (SPS)Mechanical propertiesMicrohardnessFracture toughnessDensification

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：