Understanding microstructure and mechanical properties of(AlTa(0.76))xCoCrFeNi(2.1) eutectic high entropy alloys via thermo-physical parameters

引用

Journal of Materials Science & Technology 2020年第22期54卷 131-137页

作者： Min Jung Kim gyeol chan kang Sung Hwan Hong Hae Jin Park Sang Chul Muna Gian Song Ki Buem Kim Department of Nanotechnology and Advanced Materials Engineering Sejong University209 Neungdong-roCwangjin-guSeoul143-747South Korea Division of Advanced Materials Engineering Kongju National UniversityCheonanChungnam330-717South Korea

(AlTa(0.76))xCoCrFeNi(2.1)(x values in molar ratio,x=0.1,0.3,0.5,0.7,1.0,and 1.5) alloys were designed to investigate the microstructure and mechanical properties of the eutectic high entropy alloys(EHEAs)consisting of FCC,B2,and Laves *** on the compositional variatio,clear microstructural variation was observed,as follows:(1) Group 1:FCC dendrite+Laves interdendrite(x=0.1),(2) Group 2:FCC dendrite+fine-eutectic structure consisting of FCC and Laves phases(x=0.3,0.5 and 0.7),(3) Group 3:B2 dendrite+bimodal eutectic structure [FCC/B2+Laves](x=1.0),(4) Group 4:Laves dendrite+eutectic structure consisting of B2 and Laves phases(x=1.5).As the fraction of Laves or B2 phases increases,yield stress increases from 293 to 2336 MPa,while the plastic strain decreases from 50 % to 2%.Thermo-physical parameters,such as mixing entropy(△S(mix)),mixing enthalpy(△H(mix)),valence electron concentration(VEC),and atomic size difference(δr),were calculated to understand the microstructural *** criteria(δr-VEC and δr-△H(mix)) were utilized to elucidate the formation of the eutectic structures in the present EHEAs,revealing the usefulness of the thermo-physical parameters in the development of EHEAs.

关键词： High-entropy alloy Eutectic high-entropy alloy Microstructure Mechanical properties Thermo-physical parameter

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

Evolution of microstructure and mechanical characteristics of(CrFeNiCu)_(100-x)Ti_(x)high-entropy alloys

引用

稀有金属:英文版 2023年第9期42卷 3088-3098页

作者： Yusupov Dilshodbek Sung Hwang Hong Muhammad Aoun Abbas gyeol chan kang Hae Jin Park Elyorjon Jumaev Wei-Min Wang Ki Buem Kim Department of Nanotechnology and Advanced Materials Engineering Sejong UniversitySeoul05006Republic of Korea Almalyk Mountain Mining Complex(MMC) Almalyk City110100Republic of Uzbekistan School of Materials Science and Engineering Shandong UniversityJinan250100China Department of Chemical Engineering New Uzbekistan UniversityTashkent100007Republic of Uzbekistan

Cr Fe Ni Cu)_(100-x)Ti_(x)(x=0,3,5,7 and 10;at%)high-entropy alloys have been designed by the consideration of the thermophysical relationship between Ti and other principal elements to investigate the influence of Ti on the microstructural evolution and mechanical properties of(CrFeNiCu)_(100-x)Ti_(x)high-entropy *** addition of Ti content in HEAs leads to a change in phase formation from dual-phase(FCC1 and FCC2,FCC:face-centered cubic)to the mixture of FCC1,FCC2 phases,and an additional body-centered cubic(BCC)*** yield strength and Vickers hardness of the alloys are enhanced from 291 to 1511 MPa and HV 134 to HV 531,respectively,which depends strongly on the volume fraction of BCC *** the one hand,the plasticity of the alloys reduces from 45.00%to 24.09%,but it could be considered reasonable *** results revealed that the addition of a minor alloying element in high-entropy alloys with consideration of thermophysical parameters led to the formation of a multiple solid solution structure with excellent mechanical properties.

关键词： High-entropy alloy(HEA) Microstructure Mechanical properties Theoretical parameters

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：